Bi-(Pb)-Sr-Ca-Cu-O yüksek sıcaklık süperiletkenlerinde Ag2O ilavesinin AC kayıplarına etkisi
Effect of Ag2O addition on the AC losses of Bi-(Pb)-Sr-Ca-Cu-O superconductors
- Tez No: 170979
- Danışmanlar: PROF. DR. SELAHATTİN ÇELEBİ
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Ag2Ü İlavesi, Bi-(Pb)-Sr-Ca-Cu-0 Süperiletkeni, AC Kayıpları, Kritik Akım Yoğunluğu, Ag20 Addition, Bi-(Pb)-Sr-Ca-Cu-0 Superconductor, AC Losses, Critical Current Density VI
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 59
Özet
ÖZET Bu tezde, Ag2O ilavesinin BSCCO sisteminin AC kayıpları üzerine etkileri, AC alınganlık ölçümleri ve teorik analizleri ile araştırıldı. AC alınganlık ve kayıplarının manyetik alana ve frekansa bağlılığı incelendi. Numunelerin deneysel sonuçlarının incelenmesinden, Ag2Û ilavesinin frekansa ve alana bağlı AC alınganlık eğrilerinin deseninde değişiklik yaptığı görüldü. Deneysel sonuçlar kritik hal modeli çerçevesinde nitel olarak tartışıldı. Ag2Û ilave miktarının (% 0, 15, 30) artmasıyla, kritik akım yoğunluğunun azaldığı bulundu. Tanelerin hacimsel kesirleri, Ag2Û miktarı ve alan büyüklüklerinin bir fonksiyonu olarak tahmin edildi. Kritik hal modeli hesaplamalarında kritik akım yoğunluğunun Jcm(T) = ^f aJ TY 1- ) ile verilen bağıntısı kullanıldı. Burada oc0, T=0 da çivileme şiddeti parametresini göstermekte, n ve p sırası ile tanelerarası kritik akım yoğunluğunun alan ve sıcaklık bağlılığım temsil etmektedir. Her numune için teorik ve deneysel en iyi uyum eğrilerinden tanelerarası kritik akım yoğunluğunun alan (Bn ) ve sıcaklık bağlılığı (p) belirlendi. Ag2Û ilave miktarının artmasıyla, alan üssü n, tanelerin hacim kesri fg, ve sıcaklık üssü p'nin, arttığı belirlendi. %"(T) verilerinde uyum parametreleri kullanılarak yapılan hesaplamalar, alan genliğine göre değişen deneysel eşsıcaklık histerezis kayıplarına oldukça iyi uyum eğrileri vermektedir.
Özet (Çeviri)
SUMMARY Effect of Ag2O Addition on the AC Losses of Bi-(Pb)-Sr-Ca~Cu-0 Superconductors In this thesis, the effects of Ag20 addition on AC losses of Bi-(Pb)-Sr-Ca-Cu-0 system have been investigated by means of AC susceptibility measurements and theoretical analysis. Dependence on magnetic field and frequency of AC susceptibility and losses have been studied. From the examinations of the experimental results for the samples, Ag20 addition was seen to change the pattern of frequency dependent AC susceptibility and field dependent AC susceptibility curves. Experimental results are qualitatively discusssed in the framework of the critical state model. Intergranular critical current density was found to decrease with increased amount of Ag20 addition (0, 15, 30 wt %). The volume fractions of the grains were estimated as a function of both Ag20 amount and field amplitudes. The expression for the critical current density given by Jcm(T) = -4 aJ TY 1- T V cm J is used in critical state calculations. Where a 0 denotes the pinning strength parameter at T=0, n and p represent the field and temperature dependence of the intergranular critical current density, respectively. The field and temperature dependence (Bn and p) of the intergranular critical current density for each sample were determined from the comparison of the experimental and calculated curves. The field exponent n, volume fractions of the grains fg, temperature exponent p, were found to increase with increasing amount of Ag20 addition. Experimental isothermal hysteresis losses as a function of field amplitude are reproduced quite well by calculation using the same fitting parameters as that for %"(T) data.
Benzer Tezler
- Bi(Pb)-Sr-Ca-Cu-O yüksek sıcaklık süperiletkenliklerinin yapısal bazı özelliklerinin incelenmesi
Investigation of some structural properties of high-temperature Bi(Pb)-Sr-Ca-Cu-O superconducting compounds
MUSTAFA ERÜNSAL
Yüksek Lisans
Türkçe
2003
Fizik ve Fizik MühendisliğiKırıkkale ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. SAFFET NEZİR
- The effect of Au diffusion-doped on structural, superconducting and mechanical properties of Bi1.8Pb0.35Sr1.9Ca2.1Cu3Oy
Bi1.8Pb0.35Sr1.9Ca2.1Cu3Oy süperiletkeninde Au difüzyonunun yapısal, üstüniletkenlik ve mekanik özellikleri üzerine etkisi
ÖZGÜR ÖZTÜRK
Doktora
İngilizce
2007
Fizik ve Fizik MühendisliğiAbant İzzet Baysal ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
DOÇ. DR. CABİR TERZİOĞLU
- Amonyum nitrat yöntemiyle hazırlanmış yüksek sıcaklık Bi (Pb)-Sr-Ca-Cu-O süperiletken bileşiklerin bazı elektriksel yapısal ve magnetik özellikleri
Başlık çevirisi yok
SAFFET NEZİR
Yüksek Lisans
Türkçe
1996
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. MUSTAFA ALTUNBAŞ
- Yüksek sıcaklık süperiletken malzemelerin üretimi ve fiziksel özelliklerinin tayini
Preparation and physical characterization of high temperature superconductors
AHMET KILIÇ
Yüksek Lisans
Türkçe
2000
Fizik ve Fizik MühendisliğiAnkara ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. ALİ GENCER
- Eritme-Döküm yöntemiyle üretilmiş Bi1-6 Pb0.4 Sr 2 Ca3 Cu4 012 (2234) süperiletkenin yapısal ve fiziksel özelliklerinin incelenmesi
Başlık çevirisi yok
TAYFUR KÜÇÜKÖMEROĞLU
Yüksek Lisans
Türkçe
1994
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. EKREM YANMAZ