Bi(Pb)-Sr-Ca-Cu-O yüksek sıcaklık süperiletkenliklerinin yapısal bazı özelliklerinin incelenmesi

Investigation of some structural properties of high-temperature Bi(Pb)-Sr-Ca-Cu-O superconducting compounds

  1. Tez No: 136270
  2. Yazar: MUSTAFA ERÜNSAL
  3. Danışmanlar: DOÇ. DR. SAFFET NEZİR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
  6. Anahtar Kelimeler: Superconductor, Bi(Pb)-Sr-Ca-Cu-0 system, liquid ammonium nitrate method, high Tc phase, sintering effect, abnormal volume expansion, powder x-ray diffraction pattern, electrical resistance, critical current density, thermal expansion, magnetic susceptibility, electron microscopy. rv
  7. Yıl: 2003
  8. Dil: Türkçe
  9. Üniversite: Kırıkkale Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Fizik Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 53

Özet

ÖZET Bi(Pb)-Sr-Ca-Cu-0 YÜKSEK SICAKLIK SÜPERİLETKENLERİN YAPISAL BAZI ÖZELLİKLERİNİN İNCELENMESİ ERÜNSAL, Mustafa Kırıkkale Üniversitesi Fen Bilimleri Enstitüsü Fizik Anabilim Dalı, Yüksek Lisans Tezi Danışman: Doç. Dr. Saffet NEZİR Ocak 2003, 41 sayfa Bu çalışmada, 110 K'lik kritik sıcaklığa sahip Bi(Pb)-Sr-Ca-Cu-0 süperiletken bileşikler, amonyum nitrat kullanılarak üretildi. Anormal hacim artışının gözlendiği bu numunelerde, tavlama süresinin ve uzun süre bekletmenin etkisi incelendi. Numunelerin, elektriksel özdirençleri ölçüldü. X- ışını kırınım piklerinin şiddetlerinden, yüksek sıcaklık fazının oranı belirlendi. Numunelerin yapraksı taneleri, SEM mikrograflarından gözlendi. Sinterleme süresinin 50 saatten 150 saate kadar artmasıyla, numunelerde ortalama tane büyüklüğünün 5 ym'dan 10 fjm'a kadar çıktığı ve taneler arası temasın da bir miktar arttığı gözlendi. Diğer yandan, 2223 yüksek sıcaklık fazının oranı 100 saatlik sinterleme işlemi sonucunda % 90'lara kadar artmaktadır.50, 100, 125 ve 150 saat sinterlenen süperiletken numunelerin çok uzun süre normal hava ortamında bekletildiğinde özdirençleri %10 civarında arttı. Numuneler, 106-107 K'de süperiletken halden normal hale dönüşürken, uzun süre bekletmenin sonucunda 102-103 K'de normal hale dönüştüler. Anahtar Kelimeler; Süperiletken, Bi(Pb)-Sr-Ca-Cu-0 Sistemi, sıvı amonyum nitrat yöntemi, yüksek Tc Fazı, sinterlemenin etkisi, x- ışını toz kırınım deseni, elektriksel özdirenç, elektron mikroskobu.

Özet (Çeviri)

ABSTRACT INVESTIGATION OF SOME STRUCTURAL PROPERTIES OF HIGH- TEMPERATURE Bi(Pb)-Sr-Ca-Cu-0 SUPERCONDUCTING COMPOUNDS ERÜNSAL, Mustafa Kırıkkale University Graduate School Of Natural and Applied Sciences Department Department of Physics, M.Sc. Thesis Supervisor: Assoc. Prof. Dr. Saffet NEZİR January 2003, 41 pages In this thesis, Bi(Pb)-Sr-Ca-Cu-Q superconducting compounds with transition temperature near 1 10 K were fabricated by using ammonium nitrate. Abnormal volume expansion was observed in these samples. The effects of sintering period and keeping the samples for a long period of time were examined. Electrical resistivity of the samples and from the analysis of XRD patterns, the ratio of high-Tc phase were determined. Flake-like grain of these granular superconductors was observed from SEM micrographs. As the sintering period increased from 50 h to 150 h, it was observed that the average grain size in the samples was increased from 5 |Jm to 10 (Jm. This process also slightly increased the interconnectivity of the grains. On the other hand, the ratio of the 2223 high-Tc phase was about 90 % after the sintering for 100 h. The resistivity of superconductor samples sintered for 50, 100, 125 and 150 increased 10 % when they were kept under normal conditions for a long period of mtime. The samples turned into normal from superconductivity at 106-107 K, while they became normal at 102-103 K as the result of keeping them for long period of time.

Benzer Tezler

  1. Tez No

    170979

    Bi-(Pb)-Sr-Ca-Cu-O yüksek sıcaklık süperiletkenlerinde Ag2O ilavesinin AC kayıplarına etkisi

    Effect of Ag2O addition on the AC losses of Bi-(Pb)-Sr-Ca-Cu-O superconductors

    İBRAHİM DÜZGÜN

    Yüksek Lisans

    Türkçe

    Türkçe

    2005

    Fizik ve Fizik MühendisliğiKaradeniz Teknik Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. SELAHATTİN ÇELEBİ

  2. Tez No

    57810

    Amonyum nitrat yöntemiyle hazırlanmış yüksek sıcaklık Bi (Pb)-Sr-Ca-Cu-O süperiletken bileşiklerin bazı elektriksel yapısal ve magnetik özellikleri

    Başlık çevirisi yok

    SAFFET NEZİR

    Yüksek Lisans

    Türkçe

    Türkçe

    1996

    Fizik ve Fizik MühendisliğiKaradeniz Teknik Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. MUSTAFA ALTUNBAŞ

  3. Tez No

    95792

    Yüksek sıcaklık süperiletken malzemelerin üretimi ve fiziksel özelliklerinin tayini

    Preparation and physical characterization of high temperature superconductors

    AHMET KILIÇ

    Yüksek Lisans

    Türkçe

    Türkçe

    2000

    Fizik ve Fizik MühendisliğiAnkara Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ. DR. ALİ GENCER

  4. Tez No

    33752

    Eritme-Döküm yöntemiyle üretilmiş Bi1-6 Pb0.4 Sr 2 Ca3 Cu4 012 (2234) süperiletkenin yapısal ve fiziksel özelliklerinin incelenmesi

    Başlık çevirisi yok

    TAYFUR KÜÇÜKÖMEROĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    1994

    Fizik ve Fizik MühendisliğiKaradeniz Teknik Üniversitesi

    Fizik Ana Bilim Dalı

    YRD. DOÇ. DR. EKREM YANMAZ

  5. Tez No

    216588

    The effect of Au diffusion-doped on structural, superconducting and mechanical properties of Bi1.8Pb0.35Sr1.9Ca2.1Cu3Oy

    Bi1.8Pb0.35Sr1.9Ca2.1Cu3Oy süperiletkeninde Au difüzyonunun yapısal, üstüniletkenlik ve mekanik özellikleri üzerine etkisi

    ÖZGÜR ÖZTÜRK

    Doktora

    İngilizce

    İngilizce

    2007

    Fizik ve Fizik MühendisliğiAbant İzzet Baysal Üniversitesi

    Fizik Mühendisliği Ana Bilim Dalı

    DOÇ. DR. CABİR TERZİOĞLU

Geri Dön