Çinko borat katkılı poliüretan filmlerin hazırlanması ve karakterizasyonu

Preparing and characterization of polyurethane-zinc borate films

  1. Tez No: 172148
  2. Yazar: BAŞAR YILDIZ
  3. Danışmanlar: PROF.DR. SENİHA GÜNER
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2006
  8. Dil: Türkçe
  9. Üniversite: İstanbul Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 61

Özet

ÇİNKO BORAT KATKILI POLİÜRETAN FİLMLERİN HAZIRLANMASI VE KARAKTERİZASYONU ÖZET Polimer endüstrisinde son yıllarda en hızlı gelişen gruplardan biri de hiç kuşkusuz poliüretanlardır. Basit olarak poliüretan reaksiyonu izosiyonat fonksiyonel grubunun hidroksi fonsiyonel grubuyla reaksiyonu sonucunda oluşur. İlk olarak Otto Bayer ve çalışma arkadaşları tarafından 1937 yılında sentezlenmiştir. Ticari olarak poliüretanda hidroksi kaynağı olarak yaygın olarak polyester ve polieter poliol kullanılırken alifatik ve aromatik olarak farklı türde izosiyonat kullanılır. Kullanım alanlarına bakılacak olunursa, uçak-gemi yapı malzemlerinden, koltuk süngerleri, paketleme köpükleri, elyaf, izolasyon malzemesi, oyuncak, tekerlek, suni deri, ayakkabı tabam, yapıştırıcı, medikal uygulamalar v.b. olmak üzere çok geniş bir spektrumda kullanım alanı bulmuştur. Çinko Borat, son yıllarda alev geciktirici olarak kullanılan bir bor bileşiğidir. Zehirli özelliğe sahip olmadığı için diğer reçinelere ilave edilmesi sırasında özel yöntemlere gerek yoktur. Bu özellik çinko boratı diğer alev geciktiricilerin önüne geçirmektedir. Kullanılan yüzeyde daha ileri yanmayı engelleyen yüzey tabakası oluşturarak polimerin yanarak kömürleşmesini yavaşlatma özelliği nedeniyle; alev geciktirici, duman bastırıcı, korozyon geciktirici olarak polimerde ve kaplamada olmak üzere belli başlı kablolar, boyalar, kumaşlar, elektrik/elektronik parçalar, halı kaplamalar, taşıt araçları iç aksamı ve kağıt endüstrisinde v.b. kullanım alam bulmuştur. Çalışmada poliüretan olarak, suni deri sektöründe kullanılan, alifatik ve aromatik polyester bazlı poliüretanlar kullanılmıştır. Alınan poliüretanlar, farklı oranlarda çinkoborat ile karıştırılarak aynı kalınlıklarda filmler hazırlanmıştır. Hazırlanan filmler farklı karakterizasyon yöntemleri ile karakterize edilmiştir. Karakterizasyon sonrasında, poliüretan içinde çinko boratın dağıldığı, çinko boratın poliüretan filme vıııyanma geciktirici özellik kattığı, antioksidant etki ederek bozunmasını yavaşlattığı, filmleri matlaştırdığı, poliüretanın mekanik özelliklerini değiştirmediği gözlenmiştir. ıx

Özet (Çeviri)

PREPARING AND CHARACTERIZATION OF POLYURETHANE - ZINC BORATE FILMS SUMMARY In polymer industries the importance of polyurethanes has incsreased in recent years. Fundementaly, polyurethane reaction occurs isocyanate functional groups with hidroxyl functional groups. First polyurethane was synthesized by Otto bayer and his colleagues in 1937. Polyester and polyether polyol as a hydroxyl end groups and aliphatic and aromatic isocyanates are commonly used in commercial polyurethane production. Polyurethane is used in airplane/ship constructions, foam in furniture, packaging foam, fiber, insulation materials, toys, wheels, artificial leather, shoe sole, adhesives and medical applications in wide area. Zinc borate is a bore compound which has been used as flame retardant in recent years. As it shows non-toxic properties it does not require special compounding methods when it is added to other resins. Therefore zinc borate is more prefered as a flame retardant. It works with mechanism of producing layer on surface and this layer decreases flame and char. For this reason it is used as a flame retardant, smoke supprasant and corrosion retardant in cables, dyes, fabrics, electric/electronic devices, carpet coatings, inner part of vehicles and paper industries. In my research, polyester based aliphatic and aromatic polyurethanes which are used in artificial leather sector were taken. Films which had same thickness were prepared by adding different proportions of zinc borate to aromatic and aliphatic polyurethanes. Than these films were characterized by different methods. It was seen that zinc borate was separated in polyurethane. Other observations were as follows; zinc borate provided flame retarding and antioxidant properties to polyurethane, decreased gloss value in polyurethane, did not affect mechanical porperties of polyurethane.

Benzer Tezler

  1. Çinko borat katkılı polimer kompozit zırh malzemelerin üretilmesi ve özelliklerinin incelenmesi

    Production of zinc borate reinforcement polymer composite shielding materials and determination of their properties

    TOYGAR ÇARDAK

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    EnerjiBursa Teknik Üniversitesi

    Enerji Sistemleri Mühendisliği Ana Bilim Dalı

    PROF. DR. SONGÜL AKBULUT ÖZEN

  2. Special resin additives for polyurethane

    Poliüretan için özel reçine katkı maddeleri

    GÖRKEM ÜLKÜ

    Doktora

    İngilizce

    İngilizce

    2023

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    DOÇ. DR. NESRİN KÖKEN

  3. The effects of using zinc borate and glass fiber additives on the properties of rigid polyurethane foams

    Başlık çevirisi yok

    ENGİN ACAR

    Yüksek Lisans

    İngilizce

    İngilizce

    2019

    Polimer Bilim ve TeknolojisiOndokuz Mayıs Üniversitesi

    Nanobilim ve Nanoteknoloji Ana Bilim Dalı

    DOÇ. DR. ENGİN BURGAZ

  4. Effects of some additives on the properties of rigid polyurethane foams: flame retardancy, thermal conductivity and compressive strength

    Bazı katkıların sert poliüretan köpüklerin özellikleri üzerine etkileri: alev geciktiricilik, ısıl iletkenlik ve basma dayanımı

    EMRE AKDOĞAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    KimyaAnadolu Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ. DR. MURAT ERDEM

    PROF. DR. MUSTAFA ERDEM ÜREYEN

  5. Rigid polyurethane foams with improved reaction to fire and low emission properties

    Geliştirilmiş yangın dayanım performanslı ve düşük emisyonlu rijit poliüretan köpükler

    BERRİN DEĞİRMENCİ

    Doktora

    İngilizce

    İngilizce

    2023

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ NESRİN KÖKEN

    PROF. DR. ELİSABETTA SALATELLI