Reşadiye bentonitinin amin ile modifikasyonu ve epoksi bazlı nanokompozit malzeme üretimi
Amine modification of Reşadiye bentonite and preparation of epoxy based nanocomposite
- Tez No: 179162
- Danışmanlar: YRD. DOÇ. DR. İBRAHİM ALP
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Kimya, Maden Mühendisliği ve Madencilik, Polymer Science and Technology, Chemistry, Mining Engineering and Mining
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2008
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Maden Mühendisliği Bölümü
- Bilim Dalı: Maden Mühendisliği Ana Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada; geniş bir ticari uygulama alanına sahip olan epoksi reçinelerin mukavemet özelliklerini iyileştirebilmek için organik olarak modifiye edilmiş Reşadiye (Tokat) Na-benonitinin katkı maddesi olarak kullanılabilirliği ve epoksiye sağladığı iyileştirme etkisi incelenmiştir.Çalışma üç aşamada gerçekleştirilmiştir. Birinci aşamada doğal ortamından alınan Na-bentonit hidrosiklon ile zenginleştirilerek feldspat, kuvars, kalsit ve biyotit gibi safsızlıklar uzaklaştırılmış ve Na'ca zengin bir ürün elde edilmiştir.İkinci aşamada zenginleştirilmiş Na-bentonit literatürde de çok yaygın olarak kullanılan HTAB(R(CH3)3NBr (R: C16H33)) ile farklı konsantrasyonlarda muamele edilerek bentonit yüzeyi modifiye edilmiş ve tabakalar arası mesafeleri arttırılmıştır. Aynı zamanda HTAB miktarına bağlı olarak yüzey polaritesinde ve tabakalar arası mesafedeki değişim belirlenmiştir.Üçüncü aşamada ise modifiye edilmiş Na-bentonit öğütülmüş ve epoksi reçinesi içerisinde dağıtılarak kil/epoksi matriksi oluşturulmuştur. Bu karışım ASTM D638-03 standartında belirtilmiş olan ölçülere uygun olan bir kalıba dökülüp mikrodalga kürleme yöntemi ile kürlenmiştir. Elde edilen kompozit çubuklar çekme dayanımı testleri ile analiz edilmişlerdir.Çalışma neticesinde HTAB ile modifiye edilmiş Na-bentonitinin polaritesinin epoksi reçine içerisinde dağılabilmesine uygun derecede olduğu ve tabakalar arası mesafesinin modifiye edilmeden önce 12,7 Å iken modifikasyon sonrasında 22,19 Å seviyesine yükseldiği gözlenmiştir. Ayrıca modifiye edilmemiş ve modifiye edilmiş ürünler ile yapılan nanokompozit ürünlerin mukavemet testleri neticesinde modifiye edilmiş ürünler ile hazırlanan nanokompozitlerin çekme dayanımı değerlerinde düşüş olduğu ancak modifiye edilmemiş ürünler ile hazırlanan nanokompozitlerin çekme dayanımı değerlerinde %16'ya varan iyileştirme elde edilmiştir.
Özet (Çeviri)
In this study organically modified Na-bentonite from Karakaya-Reşadiye-Tokat was introduced into epoxy resin as filler to determine its utility and contrubution effect over the strenght properties of epoxy resin.This study consists of three parts. In the first part, the raw Na - bentonite was upgraded with hdrocyclone process to obtain a Na rich bentonite and to remove the impurities such as feldspar, quartz, calsite and biotite.In the second part, the Na rich bentonite was treated with HTAB (R(CH3)3NBr (R: C16H33)), which is commonly used in the literature, at different concentrations to modify the bentonite surface and the extend the interlayer spaces. At the same time depending on the ammount of the HTAB added, the changes induced to the surface polarity and interlayer space was determined.In the third part, the modified Na-bentonite was dispersed in ground epoxy resin to obtain the clay/epoxy matrix. This matrix was poured in to a teflon mold made according to the ASTM D638-03 standart. The teflon mold was then cured in a microwave oven to obtaine composite bars which were analysed through tensile tests.At the end of the study, HTAB modified Na-bentonite gained enough polarity for dispersion in epoxy resin and the interlayer spaces expanded to from the original value of 12,7 Å to 22,19 Å. The tensile strenght of the nanocomposites not showed any improvement when organophilic clays were used as filler. On the other hand the organophobic clays were showed %16 improvement on tensile strenght values when compared with those of the neat epoxy.
Benzer Tezler
- Tokat-Reşadiye bölgesi bentonitinin duvar karosu bünyelerinde kullanılabilirliğinin araştırılması
Investigations of the applicability of Tokat-Reşadiye region bentonites in wall tile bodies
BÜŞRA ÇETİN
Yüksek Lisans
Türkçe
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. NECİP ÜNLÜ
- Reşadiye/Tokat bentonitinden elde edilen sodyum montmorillonit ile hazırlanan organokillerin adsorplama özelliklerinin incelenmesi
Investigation of the adsorbtive properties of organoclays prepared by the sodium montmorillonite obtained from the Reşadiye/Tokat bentonite
MÜŞERREF ÖNAL
- Kuzey ve Batı Anadolu bentonitlerinin kalıp kumu özelliklerine etkisinin incelenmesi
The Investigation of the effect of north and west anatolian bentonites on casting mold sand properties
NECİP ÜNLÜ
- Reşadiye bentonitinin organik ve inorganik katyonlarla modifikasyonu ve modifiye ürünlerde 75Se radyoizotopunun adsorpsiyonunun incelenmesi
Modification of reşadiye bentonite by using organic and inorganic cations and investigation of 75Se radioisotope adsorption on the modified products
ESRA ORUÇOĞLU
Doktora
Türkçe
2011
Enerjiİstanbul Teknik ÜniversitesiEnerji Bilimi ve Teknolojileri Ana Bilim Dalı
YRD. DOÇ. DR. SEVİLAY HACIYAKUPOĞLU
- Reşadiye bentonitinden organofilik bentonit sentezi
Synthesis of organophilic bentonite from Reşadiye bentonite
ALİCAN VATANSEVER
Yüksek Lisans
Türkçe
2009
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. AHMET SİRKECİOĞLU