İkiz merdane döküm yöntemiyle üretilen AA5XXX ve AA6XXX serisi alüminyum alaşımlarında segregasyonların karakterizasyonu
Segregation characterization in AA5XXX and AA6XXX series aluminum alloys produced by twin roll casting method
- Tez No: 179273
- Danışmanlar: DOÇ. DR. METİN USTA
- Tez Türü: Yüksek Lisans
- Konular: Bilim ve Teknoloji, Metalurji Mühendisliği, Mühendislik Bilimleri, Science and Technology, Metallurgical Engineering, Engineering Sciences
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2008
- Dil: Türkçe
- Üniversite: Gebze Yüksek Teknoloji Enstitüsü
- Enstitü: Mühendislik ve Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 141
Özet
Bu çalışmada ikiz merdane döküm yöntemiyle üretilen ve segregasyon oluşturmaya eğilimli AA5XXX ve AA6XXX serisi alüminyum alaşımlarında oluşan segregasyonlar karakterize edilmiştir. Bu alüminyum alaşımları, yapılarındaki alaşım elementleri nedeniyle katılaşma aralığı oldukça geniş olan alaşımlardır ve bu yüzden ikiz merdane döküm yöntemiyle üretilmeleri oldukça zordur. Segregasyonlar hem mekanik özellikleri hem de yüzey kalitesini olumsuz etkilemesi nedeniyle istenmeyen yapılardır. AA5754 ve AA6082 alaşımlarında görülen yüzey ve merkez hattı segregasyonları optik mikroskop ve taramalı elektron mikroskobu (SEM) ile incelenmiştir. Bu sayede farklı alaşımlardaki farklı segregasyonlarda görülen parçacık şekillerinin nasıl oldukları görülmüş ve segregasyonların ulaştıkları derinlikler bulunmuştur. Yapıda bulunan segregasyonların kimyasal içerikleri ve fazları enerji dağılım spektroskopisi (EDS), elektron prob mikro analizörü (EPMA) ve X-ışınları difraktometresi (XRD) ile tespit edilmiştir. Yüzeyde bulunan segregasyon çeşidine göre elektrik iletkenlikleri arasında farklıklar gözlemlenmiştir. Yüzey segregasyonlarının hangi alaşım elementleri açısından daha zengin oldukları radyo frekanslı ısı boşaltma cihazı (RF GDOES) ile tespit edilmiştir. Ayrıca kral suyu ile yapılan çözündürme işlemlerinden sonra yüzeye yakın parçacıkların SEM ve EDS analizleri yapılmıştır. İkiz merdane döküm yöntemiyle üretilen alaşımların yüzey ve merkez hattındaki katılaşma hızlarının ne seviyede olduğunu bulabilmek için doğrudan çil (DC) dökümde görülen katılaşma hızına benzer katılaşma hızına sahip bir yöntem ile döküm yapılarak katılaşma hızları kıyaslanmıştır.
Özet (Çeviri)
In this study the segregations which form in AA5XXX and AA6XXX series aluminum alloys produced by twin roll casting method and having a tendency to constiute segregations were characterized. These aluminum alloys have wide freezing range because of their alloying elements. Therefore, it is difficult for them to be produced by twin roll casting method. Segregations are not preferred constitutions because they have negative effects on both the mechanical properties and the surface quality. The surface and centerline segregations observed in AA5754 and AA6082 alloys were characterized with optical microscope and scanning electron microscope (SEM). In this way the shape of intermetallic particles seen in different segregations and the alloys were observed and the distance of segregations from surface to the inside were measured. The chemical compounds and phases of the segregations were investigated with energy dispersive spectroscopy (EDS), electron probe micro analyzer (EPMA) and X-ray diffractometer (XRD). It was found that there is a difference in the electrical conductivity depending on the segregation on the surface. Radio frequency glow discharge optical emission spectroscopy (RF GDOES) was used to find what alloying elements are richer in surface segregations. In addition, after dissolving the samples with the king solution, the intermetallic particles close to the surface were characterized with SEM and EDS. In order to find the solidification rate in the surface and center line of the alloys produced by twin roll casting, the casting which produces the solidification rate similar to one produced by direct chill (DC) casting was performed. Then, the solidification rates from two methods were compared.
Benzer Tezler
- İkiz merdane döküm yöntemi ile alüminyum AA5754 alaşımı levha üretimi, döküm ve termomekanik proses parametrelerinin etkilerinin araştırılması
Production of AA5754 aluminum alloy by twin roll casting, investigating effects of casting and thermomechinal process parameters
YELİZ DEMİRAY CUCURACHI
Doktora
Türkçe
2016
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ONURALP YÜCEL
- İkiz merdane döküm yöntemiyle üretilen AA8006 alaşımlı levhaların termomekanik davranışının incelenmesi
Investigation of thermomechanical behaviour of strip-cast AA8006 alloy sheets
GÖKHAN KARA
Yüksek Lisans
Türkçe
2002
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
- İkiz merdane döküm yöntemiyle üretilen 3005 ve 3105 alaşımlarındaki merdane bükülmesi farklılığı
Difference in roll bending of 3005 and 3105 alloys produced by twin roll casting method
ÖZLEM BAHADIR
Yüksek Lisans
Türkçe
2009
Metalurji MühendisliğiGebze Yüksek Teknoloji EnstitüsüMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DOÇ. DR. METİN USTA
- İkiz merdane sürekli döküm yöntemiyle üretilen AA 1050 alüminyum alaşımına anodik oksidasyon (Eloksal) işleminin uygulanabilme kabiliyetinin incelenmesi
Investigation of applied capability anodic oxidation (eloxal) process on AA 1050 aluminum alloy produced by twin roll casting method
FATİH DEMİRAL
Yüksek Lisans
Türkçe
2015
Metalurji MühendisliğiGebze Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. METİN USTA
- İkiz merdane döküm yöntemiyle dökülen 3xxx alaşımların alternatif termo-mekanik proses sonrası mikroyapı ve korozyon davranışının incelenmesi
Investigation of the microstructural and corrosion behavior of 3xxx alloys cast by twin roll casting method after alternative thermo-mechanical process
ALİ ULAŞ MALCIOĞLU
Doktora
Türkçe
2022
Metalurji MühendisliğiSakarya ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MEDİHA İPEK