İkiz merdane döküm yöntemiyle üretilen AA8006 alaşımlı levhaların termomekanik davranışının incelenmesi

Investigation of thermomechanical behaviour of strip-cast AA8006 alloy sheets

  1. Tez No: 126684
  2. Yazar: GÖKHAN KARA
  3. Danışmanlar: PROF. DR. HÜSEYİN ÇİMENOĞLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2002
  8. Dil: Türkçe
  9. Üniversite: İstanbul Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 76

Özet

İKİZ MERDANE DÖKÜM YÖNTEMİ İLE ÜRETİLEN AA8006 ALAŞIMLI LEVHALARIN TERMOMEKANİK DAVRANIŞININ İNCELENMESİ ÖZET İlk yatırım maliyeti oldukça düşük, soğuk haddelemeye kadar olan adımlara gerek duymayan, döküm ve soğuk haddelemeyle nihai ürün kalınlığına inerek daha düşük üretim maliyeti sunan ikiz merdane döküm tekniği alüminyum alaşımlı levha üretiminde gelişmekte olan bir öneme sahiptir. Yassı mamul alüminyum alaşımlarının mekanik özellikleri, kimyasal kompozisyonlarının yanında malzemenin mikroyapısı ile de doğrudan ilişkilidir. İkiz merdane döküm yönteminin katılaşma doğasından dolayı malzeme yapısında mevcut olan metallerarası bileşikler ve tane yapısının malzeme özellikleri üzerinde çok büyük etkisi vardır. Metallerarası bileşiklerin malzeme özellikleri üzerindeki etkileri, boyutları ve dağılımları ile ilişkilidir. Sonuç olarak istenilen performansta mamul üretmek, kontrollü bir mikroyapı ile sağlanabilmektedir. Alaşım yapısında bulunan metallerarası bileşikler ve alaşımın tane yapısı, malzemeye uygulanan termomekanik işlemlerle değiştirilerek istenen seviyelere getirilebilir ve böylece yüksek kalitede ürünler elde edilebilir. Folyo ürünleri üretiminde kullanılan AA8006 alaşımı yapısında bulunan demir ve manganın malzeme mikroyapısı üzerinde etkisi nedeni ile levhanın termomekanik davranışını etkilemektedir. Uygulanan bir yüksek sıcaklık işlemi ile levhalarda tane kabalaşması meydana gelerek malzemenin mekanik özelliklerini düşürmektedir. Bu durum özellikle iyi şekillendirilebilirlik istenen alüminyum folyo ürünlerinin kalitesini kötü etkilemektedir. Bu çalışmada, iki tip (hızlı ve süper dökücü) ikiz merdane döküm makinasında üretilen AA8006 alüminyum alaşımlı levhaların termomekanik davranışı incelenmiştir. Döküm kalınlığında ve %20 - %97 arasında değişen deformasyonlar sonrası uygulanan 450°C/4h - 580°C/4h tavlar ile mikroyapısal değişimler ve mekanik özellikler incelenmiştir. Süper-dökücü ve hızlı-dökücülerde üretilen levhalar döküm parametrelerinin farklı olması nedeniyle mikroyapısal farklılıklar göstermiştir. Her iki tip dökücüde üretilen levhada da tane kabalaşması durumu yaşanmıştır. Tane kabalaşması döküm yapısı ile ilişkilendirilmiş ve temel oluşum mekanizmaları incelenmiştir. 0,6mm ve daha düşük kalınlıklara haddelendikten sonra tavlanan levhalarda süneklikte ani düşüşler bulunmuş ve bu durum tane yapısı açısından kıyaslanmıştır. vii

Özet (Çeviri)

INVESTIGATION OF THERMOMECHANICAL BEHAVIOUR OF STRIP-CAST AA8006 ALLOY SHEETS SUMMARY The relatively low capital cost of twin-roll casters, in combination with their lower energy and manning cost, have made twin roll casting an increasingly popular method of producing a wide range of aluminum flat rolled products. Mechanical properties of flat rolled aluminum products are directly correlated to microstructure of materials. Due to the solidification rates encountered in twin-roll casting process, primary phases and grain structure have significant impact on properties of twin-roll cast materials. The influences of intermetallic constituents on properties are related to their size and volume fraction. Consequently for producing high performance products it is of interest to control microstructure by thermomechanical processes. AA 8006 is one of the popular commercial alloy that contains iron and manganese is often produced by twin roll casting process for foil product. In AA8006 alloy, both iron and manganese influences the microstructure have significant impact on thermomechanical behaviour. Annealing at elevated temperatures abnormal grain growth occurs and has detrimental effect on mechanical properties and formability of products. In this study, termomechanical behaviour of AA 8006 aluminum alloy sheets that were cast by two different types of twin roll casting machine (super-caster and speed-caster) are discussed. Microstructural evolution and mechanical behaviour of annealed ( in the range of 450°C/4h to 580°C/4h ) sheets in cast thickness (6mm) and after colled reduction between %20 and %97 are examined. Super-cast and speed-cast strips exhibit different microstructures due to their casting parameters. Abnormal grain growth occered in both types of strips. Grain coarsening was correlated to as-cast structure and basic mechanism of abnormal grain growth are discussed. Ductility decreases when sheets colled deformed to the thicknesses of 0,6mm and below, and this was investigated by means of abnormal grain growth phenomena. vııı

Benzer Tezler

  1. Tez No

    179273

    İkiz merdane döküm yöntemiyle üretilen AA5XXX ve AA6XXX serisi alüminyum alaşımlarında segregasyonların karakterizasyonu

    Segregation characterization in AA5XXX and AA6XXX series aluminum alloys produced by twin roll casting method

    ZEYNEP SİREL

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Bilim ve TeknolojiGebze Yüksek Teknoloji Enstitüsü

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DOÇ. DR. METİN USTA

  2. Tez No

    245307

    İkiz merdane döküm yöntemiyle üretilen 3005 ve 3105 alaşımlarındaki merdane bükülmesi farklılığı

    Difference in roll bending of 3005 and 3105 alloys produced by twin roll casting method

    ÖZLEM BAHADIR

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    Metalurji MühendisliğiGebze Yüksek Teknoloji Enstitüsü

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DOÇ. DR. METİN USTA

  3. Tez No

    405389

    İkiz merdane sürekli döküm yöntemiyle üretilen AA 1050 alüminyum alaşımına anodik oksidasyon (Eloksal) işleminin uygulanabilme kabiliyetinin incelenmesi

    Investigation of applied capability anodic oxidation (eloxal) process on AA 1050 aluminum alloy produced by twin roll casting method

    FATİH DEMİRAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Metalurji MühendisliğiGebze Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. METİN USTA

  4. Tez No

    725342

    İkiz merdane döküm yöntemiyle dökülen 3xxx alaşımların alternatif termo-mekanik proses sonrası mikroyapı ve korozyon davranışının incelenmesi

    Investigation of the microstructural and corrosion behavior of 3xxx alloys cast by twin roll casting method after alternative thermo-mechanical process

    ALİ ULAŞ MALCIOĞLU

    Doktora

    Türkçe

    Türkçe

    2022

    Metalurji MühendisliğiSakarya Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MEDİHA İPEK

  5. Tez No

    179049

    The effects of alloying elements on the microstructure and the annealing behavior of the twin-roll cast AA1050 strip

    Alaşım elementlerinin ikiz merdane sürekli döküm yöntemiyle üretilmiş AA1050 levhanın mikroyapısına ve ısılişlem davranışına etkisi

    FATİH KARAKOYUN

    Yüksek Lisans

    İngilizce

    İngilizce

    2007

    Makine MühendisliğiBoğaziçi Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. SABRİ ALTINTAŞ

Geri Dön