Yerli ham bor cevherlerinden kalsiyum hekzaborür üretimi ve refrakterlerde antioksidan olarak kullanılması

CaB6 production from boron containing domestic raw materials and its usage as an antioxidant in magnezite refractories

PDF İndir

  1. Tez No: 223429
  2. Yazar: ORKUN ORHAN
  3. Danışmanlar: PROF.DR. ERCAN AÇMA
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Kalsiyum hekzaborür, kolemanit, MgO-C refrakter, antioksidan, Calcium hexaboride, colemanit, MgO-C refractories, antioxidant
  7. Yıl: 2006
  8. Dil: Türkçe
  9. Üniversite: İstanbul Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Üretim Metalurjisi ve Teknolojileri Mühendisliği Bilim Dalı
  13. Sayfa Sayısı: 96

Özet

Bu çalısmada, kolemanit mineralinin borik asit ve kokla birlikte ark fırınındaredükleyerek kalsiyum hekzaborür üretimi ve demir-çelik üretiminde ana refraktermalzeme olan magnezya karbon (MgO-C) tuglalara katılarak bu refrakterlerinoksidasyon dirençlerinin yükseltilmesi amaçlanmıstır. Deneylerde, Kırka yöresindensaglanan kolemanit cevherinin, kok ve borik asit ile birlikte yapılan hazırlanan sarjharmanı, açık ark ile ısıtılmakta olan ark fırını potasına beslenmis ve ergitilmistir.Yapılan ark fırın deneylerinde 40 ile 120 volt ve 80 ile 140 amper arasında çalısılmıstır.Sarj bitiminde üst elektrodun yukarı dogru çekilmesiyle ark kesilerek, agza kadar sarjile dolu olan fırın sogumaya terk edilmistir. Fırın tamamen soguduktan sonra fırıniçinde sinterlenmis farklı fazlardan numuneler alınmıstır. Deneyler sonunda elde edilenmetal fazları karakterize etmek amacıyla X-ısınları difraksiyonu (XRD) analizine tabitutularak incelenmistir. Oksidasyon deneylerinde ise antioksidan etkilerinikarsılastırmak için magnezya, pullu grafit ve antioksidan ilavesi olarak alüminyum,silisyum, bor karbür ve ark fırını deneylerinde elde edilen ürünler belirli oranlardakarıstırtmıs, baglayıcı olarak fenolik reçine kullanılmıstır. 1300 °C ve 1500 °Csıcaklıklarda belirli sürelerde sinterlenen numunelerin oksidasyon davranısının tespitiiçin agırlık kaybından yola çıkılmıs ve agırlık kayıpları hesaplanırken, numunelerinoksidasyona ugramasıyla meydana gelen karbon kaybı yüzdesi esas alınmıstır.

Özet (Çeviri)

In this study existing CaB6 synthesis technologies were summarized, colemanite wasanalysed by both chemical and physical characterization techniques, an electric arcfurnace synthesis practice was realized, and obtained product, CaB6, was characterized,respectively. Finally, behaviour of synthesized CaB6 as a deoxidant additive in MgO-Crefractories was experimented comparatively. In the experiments; domestic colemanitemineral which was obtained from Kırka, coke and boric acid were used as a rawmaterials to obtained product CaB6 was in the electric arc furnace synthesis practice.The voltage could be increased from 40 to 120 volts and the amperage was operated 80to 140 amper. After the had been consumed and the furnace has been allowed to cool,compact material and unreacted or partially reacted starting materials were obtained.At the end of the experiments, the metal phases which obtained form the crucible of thearc furnace were analysed using X-ray diffraction techniques (XRD). Secondly,oxidation experiments were investigated for different antioxidant additives. Aluminium,silicon, boron carbide and CaB6 were added to the mixture of sinter magnesia andgraphite and mixtures were shaken off for 60 minutes by mixer. 15% of graphite wasadded to the bulk material, MgO, together with 2% of antioxidant and solid phenolicresin was used as a binder. Refractory mixtures were pelletized as cylindrical pellets byhydraulic press. Then, the samples were tempered for 18 hour at 200 °C to stabilizetheir structure. Finally, the samples were oxidized in sinter furnace at 1300 °C and1500°C for 30, 60, 90 and 120 minutes, respectively. The weight changes of the pelletswere calculated after the oxidation.

Benzer Tezler

  1. Tez No

    677464

    Sorgum (Sorghum bicolor L.) çeşitlerinin bor noksanlığı ve fazlalığına duyarlılıkları

    Susceptibilities of sorghum (Sorghum bicolor L.) varieties to boron deficiency and toxicity

    RABİA GÜLŞEN KARAHAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    ZiraatÇanakkale Onsekiz Mart Üniversitesi

    Toprak Bilimi ve Bitki Besleme Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ YAKUP ÇIKILI

  2. Tez No

    897365

    Bor tülü sır araştırmaları ve uygulamalar

    Boron tulle glaze research and applications

    EYLÜL KURTCEBE

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Güzel SanatlarDokuz Eylül Üniversitesi

    Seramik ve Cam Tasarımı Ana Sanat Dalı

    DOÇ. PINAR ÇALIŞKAN GÜNEŞ

  3. Tez No

    652800

    Sol-jel yöntemi ile polimerik öncülerden nükleer kalite bor karbür tozların düşük sıcaklıkta üretimi ve radyasyon kalkanı olarak polimer nanokompozitlerde kullanımı

    Production of nuclear grade boron carbide powders from polymeric precursors by sol-gel method and their utilization as radiation shield in polymer nanocomposites

    SUNA AVCIOĞLU

    Doktora

    Türkçe

    Türkçe

    2020

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. FİGEN KAYA

  4. Tez No

    160568

    Türkiye'de bor mineralleri ve dış ticareti

    Foreign trade of boron minerals in Turkey

    PINAR EKİNCİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2005

    EkonomiKaradeniz Teknik Üniversitesi

    İktisat Ana Bilim Dalı

    PROF.DR. KENAN ÇELİK

  5. Tez No

    719155

    Çağdaş tekstil ve moda tasarımında yenilikçi yaklaşımlar bor minerali

    Innovative approaches in contemporary textile and fashion design boron mineral

    İSA DAL

    Sanatta Yeterlik

    Türkçe

    Türkçe

    2021

    Giyim EndüstrisiHaliç Üniversitesi

    Tekstil ve Moda Tasarımı Ana Sanat Dalı

    PROF. DR. NECİP ATAR

Geri Dön