2017A, 6061 ve 7039 alüminyum alaşımlarının mikroark oksidasyon yüzey kaplama yöntemi ile sert seramik kaplanması
Hard ceramic coating of 2017A, 6061 and 7039 aluminyum alloys by microark oksidation surface modification method
- Tez No: 233129
- Danışmanlar: DOÇ. DR. METİN USTA, YRD. DOÇ. MURAT MAKARACI
- Tez Türü: Doktora
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Alüminyum Alaşımları, Yüzey Modifikasyonu, Seramik Kaplama, Mikroark Oksidasyon, Aşınma, Triboloji, Korozyon, Sertlik, Yapışma, Yüzey Pürüzlüğü, Aluminum Alloys, Surface Modification, Ceramic Coating, Microarc Oxidation, Wear, Hardness, Tribology, Corrosion, Adhesion, Surface Roughness
- Yıl: 2009
- Dil: Türkçe
- Üniversite: Kocaeli Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada Al 2017, Al 6061 ve 7039-T6 alüminyum alaşımı üzerine alkali silikat çözelti içerisinde farklı kaplama parametrelerinde mikroark oksidasyon (MAO) yöntemi ile aşınma ve korozyona dirençli kalın ve sert seramik (alüminyum oksit) kaplamalar yapılmıştır. Kaplama parametrelerinden; kaplama zamanı, akım yoğunluğu ve elektrolit çözelti kompozisyonunun kaplamanın büyüme kinetiğine, faz kompozisyonuna, mikro yapısına, sertliğine, yüzey pürüzlülüğüne, altlık malzemeye yapışmasına, aşınma, korozyon ve alaşımların çentik darbe ve çekme testi özelliklerine olan etkisi incelenmiştir. MAO kaplama kinetiğinin büyük oranda uygulanan akım yoğunluğuna bağlı olduğu ve kaplama kalınlığının kaplama süresiyle lineer bir şekilde arttığı tespit edilmiştir. Ayrıca kaplama yüzey pürüzlülüğünün kaplama kalınlığının fonksiyonu olduğu ve artan kaplama kalınlığı ile arttığı belirlenmiştir. XRD analiz sonuçları kaplamaların ekseriyetle ?-Al2O3, ?-Al2O3 ve mulit fazlarından oluştuğunu göstermiştir. Daha sert ve yoğun olan ?-Al2O3 fazının nispi oranı akım yoğunluğu ve kaplama kalınlığıyla artmıştır. MAO kaplaması en büyük sertlik ara yüzeye yakın ve en düşük sertlik kaplama yüzeyinde olacak şekilde kaplama kalınlığı boyunca mikro sertlik değeri göstermiştir. Kaplama süresi, akım yoğunluğu ve elektrolit konsantrasyonun artırılması ile kaplama yüzey pürüzlülüğü artmıştır. Uygun kaplama parametreleri seçildiğinde MAO işleminin alaşımların mekaniksel özelliklerini fazla düşürmediği ve alaşımların elastisite modulünü kısmen artırdığı belirlenmiştir. Kaplama sonrası 2017A, 6061 ve 7039 alüminyum alaşımının oldukça düşük olan aşınma ve korozyon direncinin önemli bir miktarda arttığı görülmüştür.
Özet (Çeviri)
In this study, thick and hard alumina coatings resistant to wear and corrosion were fabricated on 2017A, 6061 and 7039 Al alloy substrates for different coating parameters by using of microarc oxidation (MAO) technique in an alkali-silicate electrolytic solution. The influence of the coating parameters such as the oxidation time, the current density and electrolyte concentration on the kinetic, phase composition, microstructure, hardness, surface roughness, adhesion to substrates, wear, corrosion of the coating and impact and tensile properties of al alloys were investigated. The results show that the kinetic of coating mainly depends on applied current density and, the coating thickness is increased linearly with increasing oxidation time. The surface roughness of coating is a function of coating thickness and increases with increasing coating thickness. The XRD results revealed that the coatings are composed of ?-Al2O3, ?-Al2O3 and mullite phase. The relative ratio of harder and denser ?-Al2O3 phase was increased with increasing current density and coating thickness. MAO coatings typically exhibit micro hardness gradient across the coating thickness with maximum hardness close to the interface and the lowest hardness at the surface of the coating. The surface roughness of the coatings was increased with increasing the coating time, current density and electrolyte concentration. MAO treatment will not greatly decrease the mechanical properties of the Al-based materials; especially it will enhance elastic modulus to some extend when appropriate coating parameters are selected. The wear and corrosion resistance of the Al alloy substrates are significantly increased after the modification of the microarc oxidation.
Benzer Tezler
- Farklı nitrifikasyon inhibitörlü azotlu gübrelerin silajlık mısırın (Zea mays İndentata) verim ve kalite özelliklerine etkisi
The effect of nitrogenous fertilizers with different nitrification inhibitors on yield and quality characteristics of silage maize (Zea mays İndentata)
EMİNE UÇAR
- Organ kaybı deneyimleyen cerrahi hastalarının öfke ve öz-bakım gücü düzeylerinin değerlendirilmesi
Evaluating the anger and self-care ability levels of surgical patients experiencing organ loss
HATİCE MERVE ALPTEKİN
Yüksek Lisans
Türkçe
2018
HemşirelikTrakya ÜniversitesiHemşirelik Ana Bilim Dalı
PROF. DR. ÜMMÜ YILDIZ FINDIK
- İnflamatuar bağırsak hastalığında entamoeba histolytica ve cytomegalovirus enfeksiyonu görülme sıklığı
Prevalence of entamoeba histolytic and cytomegalovirus infection in inflammatory bowel di̇sease
SERAY ÇIRKIN KORGAN
Tıpta Uzmanlık
Türkçe
2020
GastroenterolojiDokuz Eylül Üniversitesiİç Hastalıkları Ana Bilim Dalı
PROF. DR. HALE AKPINAR
- Kronik ürtikerde omalizumab gerçek yaşam verileri: Tedaviye yanıt oranları, tedaviye yanıtı belirleyen belirteçler ve tedavinin hastalık aktivite skorları ile yaşam kalitesi üzerine etkilerini inceleyen retrospektif çalışma
Real life experiences wi̇th omalizumab for the treatment of chronic urticaria: A retrospective study to evaluate treatment responses , factors associated with treatment response, omalizumab's effect on disease activity and quality of life scores
KÜBRA KIZILTAÇ
Tıpta Uzmanlık
Türkçe
2017
DermatolojiSağlık Bilimleri ÜniversitesiDeri ve Zührevi Hastalıklar Ana Bilim Dalı
DOÇ. DR. EMEK KOCATÜRK GÖNCÜ
- Yabancı cisim aspirasyonlarında tedavi seçeneklerinin değerlendirilmesi
Evaluation of treatment options in foreign body aspirations
RABİA DEMİR
Tıpta Uzmanlık
Türkçe
2018
Çocuk CerrahisiSağlık Bilimleri ÜniversitesiÇocuk Cerrahisi Ana Bilim Dalı
PROF. EMRAH ŞENEL