Nanoparçacık içeren uv ile kürleştirilmiş kaplamaların mekanik özelliklerinin incelenmesi

Investigation of the mechanical properties of nano particles containing uv cured coatings

  1. Tez No: 245090
  2. Yazar: ÖZLEM KALABALIKOĞLU
  3. Danışmanlar: PROF. DR. NERGİS ARSU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Polimer Bilim ve Teknolojisi, Chemistry, Polymer Science and Technology
  6. Anahtar Kelimeler: Nanoparçacık, TiO2, SiO2, DSC, DMA, Nanoparticles, TiO2, SiO2, DSC, DMA
  7. Yıl: 2008
  8. Dil: Türkçe
  9. Üniversite: Yıldız Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 139

Özet

Tiyokzanton türevi olan Tiyokzanton-antrasen (TX-A), 2-Merkapto-tiyokzanton (TX-SH),2-Tiyokzanton-tiyoasetikasit (TXSCH2COOH) ve 2-(Karboksimetoksi)tiyokzanton(TXOCH2COOH) fotobaslatıcıları beraberinde yardımcı bir fotobaslatıcı ilave edilmeksizin,epoksidiakrilat (P-3016) ve Tripropilenglikoldiakrilat (TPGDA) akrilat sistemi içerisine,nanoparçacık ilave edilmeden ve edildikten sonra hazırlanan formülasyonların polimerizasyonreaksiyonları Foto-Diferansiyel Kalorimetre (Foto-DSC) kullanılarak gerçeklestirildi. Foto-DSC'den elde edilen ısı akısları kullanılarak, polimerizasyon hızları ve monomerin polimeredönüsüm yüzdeleri hesaplandı. Nanoparçaçık katkılı ve katkısız formülasyonlar ZamanaBağlı Fourier Dönüsüm Infrared Spektroskopisi (RT-FTIR) kullanılarak sertlestirildi vemonomerin polimere dönüsüm yüzdeleri hesaplandı. Hazırlanan formülasyonlar 60?m kalınlığında, önceden kalıp ayırıcı (Polivaks) uygulanmıs teflon plaka üzerine kaplanıpUV ile kürlestirme tekniği kullanılarak, Mini UV-Kür cihazından 5 m/dk hızla geçirilereksertlestirildi. Filmler teflon plaka üzerinden çıkarılarak 5.3 mm eninde film kesme aparatıylakesilerek örnekler hazırlandı. Hazırlanan film örneklerinin, 0.5 N sabit gerilim altında, odasıcaklığından 100-130 0C' ye kadar 5 0C/dk hızla ısıtılarak kayıp modülü, depolama modülüve Tan d grafikleri elde edildi. Grafiklerin maksimum noktalarından Tg değerleri saptandı.Ayrıca elde edilen filmlerin çözücü dirençleri Metiletilketon ile silinerek saptandı.

Özet (Çeviri)

In this study, without using any other coinitators, the thioxanthone derivative photoinitiatorsTX-A, TX-SH, TXSCH2COOH ve TXOCH2COOH are used in P-3016 ve TPGDA acrylatesystem for determination of polymerization rate, conversion % and heat flow of nanoparticlesadded and non-added formulations by using Photo-Differential Scanning Calorimetry (Photo-DSC). By using heat flow of Photo-DSC, rate of polymerization (H) and conversionpercentage of monomer were calculated. The formulations with and without nanoparticleswere cured by using Real Time-Fourier Transform Infrared Spectroscopy (RT- FTIR) and the% conversion from monomer to polymer were calculated. Formulations were coated on 60?m polytetrafloroetilen (teflon) that were treated with Polivaks before. After coating, theseformulations were cured by UV curing system and the equipment that was used was MiniUV- Curing machine at speed of 5 m/min. The UV-Cured films were seperated from teflonplate and then cut into pieces by using 5.3 mm width film cutting aparate. The storagemodulus, lost modulus and Tan d graphs of the prepared film samples were investigated bytreating at range of 100-130 0C temperature, 5 0C/min heating speed and under the tension 0.5N. By determination of maximum points of the graphs Tg values were calculated.Furthermore, the solvent resistance of the films were determiend by cleaning withMethlyethlyketon.

Benzer Tezler

  1. UV ile kürleştirilmiş nanokaplamalar ve uygulamaları

    UV cured nanocoatings and their applications

    ÖNER İZGİN

    Doktora

    Türkçe

    Türkçe

    2023

    KimyaYıldız Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. NERGİS ARSU

  2. Synthesize and photocatalytic applications of titanium dioxide and magnetic nanoparticles containing high sulfur content polymeric composites

    Titanyum dioksit ve manyetik nanoparçacık içeren yüksek kükürt içerikli polimerik kompozitlerin sentezi ve fotokatalitik uygulamaları

    MERT TOPCUOĞLU

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    KimyaAtılım Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT KAYA

    PROF. DR. ATİLLA CİHANER

  3. Preparation and characterization of ultra thin films containing silver-copper nanoalloys using layer-by-layer depositon technique for antibacterial applications

    Antibakteriyel uygulamalar için gümüş-bakır nanoalaşımlar içeren ve katman-katman-kaplama yöntemi ile hazırlanan ultra ince filmlerin hazırlanması ve karakterizasyonu

    MERVE TANER CAMCI

    Yüksek Lisans

    İngilizce

    İngilizce

    2012

    Kimyaİhsan Doğramacı Bilkent Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ŞEFİK SÜZER

  4. Nanoparçacık içeren polimerlerin optiksel ve yapısal karakterizasyonlarının incelenmesi

    Investigation of optical and structural characterizations of polymers containing nanoparticle

    MURAT TÜREMİŞ

    Doktora

    Türkçe

    Türkçe

    2016

    Fizik ve Fizik MühendisliğiCelal Bayar Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ. DR. AHMET ÇETİN

    DOÇ. DR. RANA KİBAR

  5. II-VI yarıiletken nanoparçacık içeren organik langmuir-blodgett ince filmlerin özelliklerinin incelenmesi

    II-VI yariiletken nanoparçacik içeren organik langmuir-blodgett ince filmlerin özelliklerinin incelenmesi

    TAYFUN UZUNOĞLU

    Doktora

    Türkçe

    Türkçe

    2008

    Bilim ve TeknolojiAnkara Üniversitesi

    Fizik Mühendisliği Ana Bilim Dalı

    PROF. DR. RIFAT ÇAPAN

    YRD. DOÇ. DR. HÜSEYİN SARI