Dimetilformamit/su karışımlarının sodyum aljinat, sodyum aljinat/poli(vinil alkol), sodyum aljinat/zeolit ve sodyum aljinat/poli(vinil alkol)/zeolit membranlar kullanılarak ayrılması
Separation of dimethylformamide/water mixtures using sodium alginate, sodium alginate/poli(vinil alkol), sodium alginate/zeolite and sodium alginate/poly(vinyl alcohol)/zeolite membranes
- Tez No: 245561
- Danışmanlar: PROF. DR. OYA ŞANLI
- Tez Türü: Doktora
- Konular: Kimya, Polimer Bilim ve Teknolojisi, Chemistry, Polymer Science and Technology
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2009
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Bölümü
- Bilim Dalı: Kimya Ana Bilim Dalı
- Sayfa Sayısı: 176
Özet
Bu çalışmada, pervaporasyon (PV), evapomasyon (EV) ve sıcaklık farklı evapomasyon (TDEV) yöntemleri kullanılarak dimetilformamit (DMF)-su karışımlarının ayrılabilirlikleri araştırıldı. Ayırmada sodyum aljinat (NaAlg) esaslı membranlar kullanıldı. NaAlg; poli(vinil alkol) ve zeolit kullanılarak modifiye edildi. Hazırlanan membranlar Fourier transform infrared spektrometrisi (FTIR), diferansiyel taramalı kalorimetri (DSC), termal gravimetrik analiz (TGA) ve taramalı elektron mikroskopi (SEM) kullanılarak karakterize edildi.Deneysel çalışmalar; membran kalınlığının, çalışma sıcaklığının, membran bölgesi sıcaklığının ve besleme çözeltisi derişiminin geçiş hızı (akı) ve ayırma faktörü (seçicilik) üzerindeki etkisine yoğunlaştırıldı.Deneysel çalışmalar üç bölüm halinde gerçekleştirildi. Birinci bölümde pervaporasyon yöntemi kullanılarak NaAlg membranlar ile DMF-su karışımlarının ayrılması çalışıldı. %20 DMF (m/m) çözeltisi için optimum çalışma sıcaklığı 40 oC ve membran kalınlığı 60 ? m olarak tespit edildi.İkinci bölümde NaAlg/PVA alaşım membranlar hazırlandı. PV yöntemi kullanılarak, 40 oC çalışma sıcaklığı ve %20 DMF besleme çözeltisi derişiminde en uygun NaAlg/PVA oranı 80/20 (v/v) olarak belirlendi.Üçüncü bölümde NaAlg/zeolit ve NaAlg/PVA/zeolit kompozit membranlar hazırlandı ve hazırlanan membranlar DMF-su karışımlarının üç farklı yöntem (PV, EV ve TDEV) ile ayrılmasında kullanıldı. NaAlg/zeolit ve NaAlg/PVA/zeolit kompozit membranlar kullanılmasıyla geçiş hızının arttığı, ayırma faktörünün azaldığı belirlendi.Kullanılan dört farklı membran için geçiş hızı ve ayırma faktörünün kullanılan yönteme bağlı olarak değişiklik gösterdiği sonucuna varıldı. En yüksek ayırma faktörü değerine TDEV yönteminde ulaşıldı. Bununla birlikte PV ile elde edilen akı değerlerinin EV ve TDEV yöntemlerinde elde edilen değerlerden daha yüksek olduğu bulundu.
Özet (Çeviri)
In this study, separation of dimethylformamide (DMF)-water mixtures was investigated using pervaporation (PV), evapomeation (EV) and temperature difference evapomeation (TDEV) methods. Sodium alginate (NaAlg) based membranes were used in the separation. NaAlg was modified using poly (vinyl alcohol) and zeolite. Membranes prepared were characterized using Fourier transform infrared spectrometry (FTIR), differantial scanning calorimetry (DSC), thermal gravimetric analysis (TGA) and scanning electron microscopy (SEM).Experimental studies were majored on the effect of membrane thickness, operating temperature, membrane surrounding temperature and the feed composition on the permeation rate (flux) and the separation factor (selectivity).Experimental studies were carried out in three parts. In the first part; DMF-water mixtures were separated using NaAlg membranes by pervaporation. The optimum operating temperature and membrane thickness were determined as 40 oC and 60 ? m for %20 DMF (v/v) solutions.In the second part; NaAlg/PVA blend membranes were prepared. Using PV technique, optimum NaAlg/PVA ratio was determined as 80/20 (m/m) for 20 wt% DMF mixtures at 40 oC.In the third part of the study; NaAlg/zeolite and NaAlg/PVA/zeolite composite membranes were prepared and the membranes prepared were used for DMF-water separation by three different methods (PV, VP and TDVP). It was determined that the permeation rate increased, the separation factor decreased by using NaAlg/zeolite and NaAlg/PVA/zeolite composite membranes.It was concluded that the permeation rates and separation factors change depending on the method used for four different membranes. The highest separation factors were attained in the TDEV method. Whereas the flux values obtained in PV was found to be higher than in VP and TDVP methods.
Benzer Tezler
- Dimetilformamit/su karışımlarının sodyum aljinat, sodyum aljinat/poli (vinil pirolidon) ve (N-vinil-2-pirolidon)-aşı-(sodyum aljinat) membranlar kullanılarak ayrılması
Separation of dimethylformamide-water mixtures using sodium alginate, sodium alginate/poly(vinyl pyrrolidone) and N-vinyl-2-pyrrolidone-g-sodium alginate membranes
EBRU KONDOLOT SOLAK
- Production and characterization of poly(acrylonitrile-co-butyl acrylate) /polypyrrole composites and nanoparticles
Poli̇(akri̇loni̇tri̇l-ko-büti̇l akri̇lat)/poli̇pi̇rol kompozi̇tleri̇n ve nanoparti̇külleri̇n üreti̇mi̇ ve karakteri̇zasyonu
CEM ÜNSAL
Doktora
İngilizce
2014
Kimyaİstanbul Teknik ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. FATMA KALAOĞLU
PROF. DR. ABDÜLKADİR SEZAİ SARAÇ
- Iki bileşenli sıvı karışımların aşırı molar hacimlerinin ölçülmesi
Excess molar volume measurements of binary liquid mixtures
MELTEM DEMİRTAS
Yüksek Lisans
Türkçe
2012
Kimya MühendisliğiKocaeli ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. OSMAN BOZDAĞ
- PVB/PANI esaslı grafen oksit ve sülfolanmış grafen oksit katkılı nanofiber elektrot malzemelerinin geliştirilmesi ve elektrokimyasal, fizikokimyasal ve morfolojik özelliklerinin incelenmesi
Development of PVB/PANI based graphene oxide and sulfonated graphene oxide enhanced nanofiber electrode materials and investigation of their electrochemical, physicochemical and morphological properties
SİNEM YAZICIOĞLU
Yüksek Lisans
Türkçe
2024
Kimya MühendisliğiGazi ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. NURSEL DİLSİZ
- Alternatif yöntemler kullanılarak proton değişim membran yakıt hücreleri için yeni membranların geliştirilmesi
Development of new membranes for proton exchange membrane fuel cells by alternative methods
YILSER DEVRİM