Geri Dön

Effect of the ester (R) groups on the controlled/living ATRP cyclopolymerization of alkyl alpha-(hydroxymethyl) acrylate (RHMA) ether dimer

Ester (R) gruplarının alkil alfa-(hidroksimetil) akrilat (RHMA) eter dimerlerinin kontrollü yaşayan ATRP halkalı polimerizasyonu üzerindeki etkileri

  1. Tez No: 245983
  2. Yazar: SEZGİN BAYRAK
  3. Danışmanlar: DOÇ. ALİ ERSİN ACAR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2009
  8. Dil: İngilizce
  9. Üniversite: Boğaziçi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Bölümü
  12. Bilim Dalı: Kimya Ana Bilim Dalı
  13. Sayfa Sayısı: 72

Özet

Önceki halkalı polimerizasyon çalışmalarında, alkil alfa-(hidroksimetil) akrilat (RHMA) eter dimerlerin, halkalı olmayan düz polimerlere göre daha yüksek ısısal dayanıklığa ve camsı geçiş sıcaklığına sahip oldukları görülmüştür.Daha önce literatürde hacimce daha küçük alkil (R) gruplarına sahip; etil, n-butil ve tert-butil ve bunlara ek olarak hacimce daha büyük adamantil ve siklohekzil alfa-(hidroksimetil) akrilatlarların kontrollü yaşayan ATRP yöntemi kullanılarak halkalı polimerleşmeleri araştırılmıştır. Bağlı olan alkil (R) gruplarının hacimce büyümesinin, halkalaşma etkinliğini ve moleküler ağırlık dağılımını belirli bir hacme kadar (t-butil) iyileştirdiği, fakat daha sonrasında hacmin daha da büyütülmesinin bu değerleri kötü yönde etkilediği gözlemlenmiştir. Bu tezde hacimce büyük olan diğer bir grup, isobornil ile yapmış olduğumuz çalışmalar, moleküler ağırlık dağılımının hacimce daha küçük t-butil türevinin sahip olduğu kadar küçük olduğunu ortaya koymuştur. Bu, ATRP sisteminin, adamantil'dekinden daha kontrollü olduğunu göstermiştir. Ayrıca hacimce küçük olan isopropil grubu da çalışılmış olup, moleküler ağırlık dağılımının, hacimce büyük isobornil ve hacimce benzer t-butil gruplarından çok daha yüksek olduğu görülmüştür. Bu ATRP polimerizasyonunun daha az kontrollü olduğunu göstermektedir.Bu araştırmada, CuBr/PMDETA katalizör olarak kullanılmış olup, isobornil ve isopropil alfa-(hidroksimetil) akrilat eter dimerlerin siklopolimerizasyonları ksilende gerçekleştirilmiştir. Polimerlerin yaşayan olma özelliğini ispat etmek için IBHMA ve IPHMA eter dimerlerin halkalı polimerleri, t-butil akrilat komonomerleriyle kopolimerleşme çalışmalarında, makrobaşlatıcı olarak kullanılmıştır. SEC analizleri tüm halkalı polimerlerin yaşayan özelliğe sahip olduğunu göstermiştir. Halkalı polimerler üzerinde yapılan fiziksel çalışmalar, polimerlerin yüksek camsı geçiş sıcaklığına (Tg) ve oldukça yüksek ısısal dayanıklılığa sahip oldukları gözlemlenmiştir.

Özet (Çeviri)

Previous cyclopolymerization studies of alkyl alpha-(hydroxymethyl) acrylate (RHMA) ether dimers showed that they are superior to non-cyclic linear ones due to improved thermal stability and high glass transition temperatures.Cyclopolymerizations of RHMA ether dimers via controlled living ATRP have been formerly investigated in the literature where smaller alkyl groups such as ethyl, n-butyl and tert-butyl and bulkier groups such as; adamantyl and cyclohexyl groups were used as the alkyl group. It was found out that as the bulkiness of the alkyl group (R) increased, cyclization efficiency and polydispersities were improved up to certain size (t-butyl), but became worse when the size was increased further. However, the present study with another bulky group, isobornyl, exhibited polydisperties as low as the ones obtained with smaller t-butyl derivative, indicating that the ATRP process was more controlled than other bulky groups such as adamantyl. In addition to this, smaller isopropyl derivative was also studied and polydisperties was found to be much higher than the monomers with bulkier isobornyl and t-butyl groups, indicating that the ATRP polymerization was less controlled.In this study, CuBr/PMDETA catalyst system was employed and cyclopolymerizations of isobornyl and isopropyl alpha-(hydroxymethyl) acrylate ether dimers were carried out in xylene. Cyclopolymers of IBHMA and IPHMA ether dimers were employed as macroinitiators in copolymerization studies with t-butyl acrylate comonomer in order to prove the livingness. SEC analysis showed that the cyclopolymers obtained were all living. Fortcoming studies on the physical properties of the cyclopolymers were also carried out and high Tg values and thermal stabilities were investigated.

Benzer Tezler

  1. Structure-reactivity relationship of acrylic acid ester ether dimers by ATRP

    ATRP halkalı polimerleştirilmesinde yapı-özellik ilişkisi

    GÜLHAN KOCASAKAL

    Yüksek Lisans

    İngilizce

    İngilizce

    2007

    KimyaBoğaziçi Üniversitesi

    Kimya Ana Bilim Dalı

    YRD. DOÇ. DR. ERSİN ACAR

  2. Kitosan/ZnFe2O4 nanokompozit malzemesi hazırlanması, karakterizasyonu ve kanser ilacı yüklenen malzemeden ilaç salımının incelenmesi

    Preparation, characterization and examination of drug release from cancer drug loaded nanocomposite chitosan/ZnFe2O4 material

    MERVE ECE TEMELKURAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Biyokimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. FATMA BEDİA BERKER

    ÖĞR. GÖR. ZEYNEP KALAYCIOĞLU

  3. Yeni bir fakoemülsifikasyon cihazı tasarımı ve uygulaması

    Design and application of a new phacoemulsification device

    HÜSEYİN HALICI

    Doktora

    Türkçe

    Türkçe

    2004

    Elektrik ve Elektronik Mühendisliğiİstanbul Teknik Üniversitesi

    Elektronik ve Haberleşme Mühendisliği Ana Bilim Dalı

    PROF. DR. İNCİ ÇİLESİZ

    PROF. DR. MUSTAFA ELÇİOĞLU

  4. Açıklanamayan infertilite olgularında erken foliküler fazda ölçülen LH seviyesinin kontrollü overyen hiperstimülasyon protokolündeki ilaç seçimine etkisi

    The effect of LH level measured in the early follicular phase on drug selection in the controlled ovarian hyperstimulation protocol in unexplained infertility cases

    BURAK HAZİNE

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2020

    Kadın Hastalıkları ve DoğumSağlık Bilimleri Üniversitesi

    Kadın Hastalıkları ve Doğum Ana Bilim Dalı

    DOÇ. DR. SEMRA KAYATAŞ ESER

  5. Poli (stiren) esaslı reçineler üzerinde sekonder amin sentezi ve aldehit ayrılması

    Başlık çevirisi yok

    BAHİRE FİLİZ ŞENKAL

    Doktora

    Türkçe

    Türkçe

    1996

    Kimyaİstanbul Teknik Üniversitesi

    PROF.DR. NİYAZİ BIÇAK