ZnO esaslı varistörlerde yönlenme gelişimi, evrik sınırların yönlenme gelişimine etkisi ve yönlenme ile elektriksel özelliklerin ilişkisi

Texture development in ZnO-based varistors, effects of inversion boundaries on texture development and relationships between texture and electrical characteristics

PDF İndir

  1. Tez No: 269651
  2. Yazar: İSMAİL ÖZGÜR ÖZER
  3. Danışmanlar: DOÇ. DR. ENDER SUVACI
  4. Tez Türü: Doktora
  5. Konular: Seramik Mühendisliği, Ceramic Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2010
  8. Dil: Türkçe
  9. Üniversite: Anadolu Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Seramik Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 198

Özet

Morfolojik ve kristallografik yönlenmenin ZnO-esaslı varistörlerin elektriksel özellikleri üzerine etkileri incelenmiştir. Yönlenmiş çekirdekle kontrollü tane büyümesi tekniği (Templated Grain Growth-TGG) ile yüksek derecede yönlenmeye sahip ZnO-esaslı varistörler üretilmiştir. İğnemsi, anizometrik ZnO çekirdekleri hidrotermal yöntem ile sentezlenmiştir. Çekirdeklerin büyüme davranışı farklı matris kompozisyonlarına bağlı olarak incelenmiştir; çekirdek içeren ve içermeyen ZnO, ZnO/Bi2O3, ZnO/Bi2O3/TiO2, ZnO/Bi2O3/SnO2 ve bir düşük voltaj varistör kompozisyonu. Yönlenme gelişimi ve dağılımının incelenmesi için stereolojik analizler, geri yansıyan elektron difraktometresi (EBSD) ve x-ışınları difraktometresi (XRD) tekniklerinden yararlanılmıştır. Çekirdek içeren varistör sisteminde, (0001) EBSD pole figürü verilerinden hesaplanan yönlenme dağılımı r ve XRD verilerinden hesaplanan yönlenme fraksiyonu f değerleri sırası ile 0.34 ve 0.98 olarak bulunmuştur. Çekirdek içermeyen varistör sisteminde de, şerit döküm sırasında matris tozunun yönlenmesine bağlı olabilecek belirgin derecede yönlenme gözlenmiştir. Bu sistem için hesaplanan r ve f değerleri sırası ile 0.47 ve 0.52'dir. Her iki sistem için de eşik voltajları mikroyapılarla uyumlu şekilde anizotropik olarak ölçülmüştür. Ancak, yüksek derecede yönlemeye sahip varistör sistemlerinde dahi doğrusal olmayan katsayının ( ? ) izotropik olduğu gözlenmiştir. Diğer taraftan, kapasitans-voltaj (C-V) analizlerinin sonuçlarından, Schottky bariyer yüksekliklerinin anizotropik oldukları hesaplanmıştır.

Özet (Çeviri)

Effects of morphological and crystallographic texture on the electrical properties of a ZnO-based varistor system were investigated regarding the texture axes. Highly textured ZnO-based varistors were fabricated via Templated Grain Growth (TGG) technique. Rod-like ZnO templates were produced by hydrothermal synthesis method. Behavior of the templates during heating was investigated by quenching the samples with following compositions to room temperature; pure ZnO, ZnO/Bi2O3, ZnO/Bi2O3/TiO2, ZnO/Bi2O3/SnO2 and a low voltage varistor system. Stereological analysis, electron back scattered diffractometer (EBSD) and x-ray diffractometer (XRD) were conducted to measure the texture distribution. The degree of orientation, r calculated from the (0001) EBSD pole figure was 0.34 and texture fraction, f (Lotgering factor) calculated from the XRD data was 0.98 for templated varistor system. A significant degree of texture was also observed in the template free varistor system probably as a result of initial particle alignment during tape casting. The r and f parameters calculated for this system were 0.47 and 0.52, respectively. The threshold voltages were found to be anisotropic for both systems in consistent with observed morphological texture. However, the nonlinear coefficients ? , did not exhibit a significant difference as a function of direction even in the highly textured samples. On the other hand, Schottky barrier heights calculated from the capacitance-voltage (C-V) measurements were also found to be anisotropic.

Benzer Tezler

  1. Tez No

    150641

    ZnO ve ZnO esaslı seramiklerde çekirdek kullanımı ile mikroyapı kontrolü

    Microstructure control in ZnO and ZnO based ceramics via seeding

    İSMAİL ÖZGÜR ÖZER

    Yüksek Lisans

    Türkçe

    Türkçe

    2004

    Metalurji MühendisliğiAnadolu Üniversitesi

    Seramik Mühendisliği Ana Bilim Dalı

    Y.DOÇ.DR. ENDER SUVACI

  2. Tez No

    106400

    ZnO esaslı varistörlerde V2O5 ile Cr2O3 katkılarının tane büyüme kinetiğine ve elektriksel özelliklere etkisinin incelenmesi

    The Investigation of grain growth kinetics and electrical behaviours of ZnO based varistors with additive V2O5 and Cr2O3

    TANLA ABKAN

    Doktora

    Türkçe

    Türkçe

    2001

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji Ana Bilim Dalı

    PROF. DR. MÜZEYYEN MARŞOĞLU

    PROF. DR. OSMAN ÖZKAN

  3. Tez No

    398630

    Çeşitli oksit bileşiklerinin çinko oksit'in mikroyapı özelliklerine etkisi

    The effect of various oxide compounds on the microstructure properties of zinc oxide

    GÖKHAN HARDAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Metalurji Mühendisliğiİstanbul Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. BERAT YÜKSEL PRICE

  4. Tez No

    755870

    Low temperature sintering of zno-based ceramics and investigation of their varistor applications

    Çinko oksit esaslı seramiklerin düşük sıcaklıklarda sinterlenmesi ve varistör uygulamalarının incelenmesi

    GÖKÇE ÖZARSLAN

    Doktora

    İngilizce

    İngilizce

    2022

    Seramik MühendisliğiEskişehir Teknik Üniversitesi

    Seramik Mühendisliği Ana Bilim Dalı

    PROF. DR. ENDER SUVACI

  5. Tez No

    878719

    ZnO esaslı farklı nanopartiküller kullanılarak su numunelerinde Al giderimi

    Al removal in water samples using different ZnO based nanoparticles

    SERKAN ÇALIŞKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    KimyaKırklareli Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. CEMİLE ÖZCAN

    DOÇ. DR. NURDAN KURNAZ YETİM

Geri Dön