Boraks ve borik asit ile emprenye edilmiş ve ısıl işleme tabi tutulmuş kayın odununun bazı fiziksel ve mekanik özelliklerinin belirlenmesi

Determining some pyhsical and mechanical properties of east beech wood (Fagus orientalis L.) which is heat-treated after impregnated with borax and boric acid

  1. Tez No: 301827
  2. Yazar: OKAN ÇITAK
  3. Danışmanlar: DOÇ. DR. HAMİYET ŞAHİN KOL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Ağaç İşleri, Teknik Eğitim, Wood Products, Technical Education
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2012
  8. Dil: Türkçe
  9. Üniversite: Karabük Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Mobilya ve Dekorasyon Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 101

Özet

Bu çalışmada, boraks ve borik asit ile emprenye edildikten sonra ısıl işleme tabi tutulmuş Doğu Kayını (Fagus Orientalis L.) odununun bazı fiziksel ve mekanik özelliklerindeki değişimler incelenmiştir. Kayın odunundan hazırlanan deney örnekleri önce %2,5' luk boraks ve borik asit çözeltisi ile emprenye edildikten sonra üç farklı sıcaklıkta (170-190 - 210 °C ) ve iki farklı sürede (4-8 saat) ısıl işleme tabi tutulmuştur. Daha sonra deney örneklerinin ağırlık kaybı, eğilme direnci, eğilmede elastikiyet modülü, basınç direnci ve renk değişim değerleri belirlenmiş ve kontrol grubu deney örnekleri ile kıyaslanarak değerlendirilmiştir.Çalışmanın sonucunda, ısıl işlem sıcaklığı arttıkça ağırlık kaybında bir düşüş gözlemlenmiştir. En az ağırlık kaybı 170°C de ısıl işlem görmüş deney örneklerinde görülürken, en yüksek ağırlık kaybı ise 210°C de ısıl işlem görmüş deneyörneklerinde görülmüştür. Isıl işlem sıcaklığı ve süresi arttıkça eğilme direnci değerlerinin düştüğü ve boraksla emprenye edilmiş deney örneklerindeki eğilme direncindeki düşüşün daha fazla olduğu belirlenmiştir. Isıl işlem görmemiş ve emprenye edilmemiş deney örneklerinin elastikiyet modülü değerlerinin emprenyelilerden daha düşük olduğu, 190°C'ye kadar elastikiyet modülünün arttığı; ancak, 210°C 'de ise önemli bir düşüşün olduğu tespit edilmiştir. Emprenye işleminin basınç direncini önemli oranda arttırdığı görülmektedir. 190°C'ye kadar liflere paralel basınç direncinde artış olduğu, ancak daha sonra tekrardan düşüş olduğu gözlenmiştir. Borik asitle muamele edilmiş ve ısıl işlem görmüş örneklerin boraksla muamele edilmiş örneklere oranla biraz daha yüksek değerler verdiği görülmüştür. Basınç direncinin, emprenyeli ısıl işlem görmüş örneklerde daha yüksek değerler verdiği belirlenmiştir. Isıl işlem görmüş deney örneklerinde, sıcaklığın artmasına paralel bir renk değişiminin (renk koyulaşmasının) meydana geldiği belirlenmiştir. Toplam renk değişiminin emprenyeli örneklerde daha az olduğu belirlenmiştir.

Özet (Çeviri)

In this study, aims to investigate the change of some physical and mechanical properties of east beech wood (Fagus Orientalis L.) which is heat-treated after impregnation with borax and boric acid. Firstly beech wood that is impregnated with % 2,5 concentrated at borax and boric acid, then it was heat-treated at three different temperature (170-190-210°C) and for two different time duration (4-8 hours). Physical and mechanical properties such as loss of weight, resistance of bending, elastic module at bending and resistance of pressure end total color change are determined for tested samples. These properties are compared with control group samples.As a result of study, when the heat treatment temperature increases, it has been observed decline in weight. Minimum of weight decline has been seen at heat treatedtest samples at 170°C. Maximum of weight decline has been seen at 210°C. It has been determined that when the temperature and duration of heat treatment increase, resistance of bending values were decrease, but the more decline of bending resistance was observed in test samples which are impregnated with borax. It has been determined that, elasticity module values of test samples which are not been subjected to heat treatment and impregnation, are less than test samples that are subjected to impregnation. It has been identified that elasticity module of test specimens increases up to 190°C degrees, however, at the 210°C a significant decrease was found. Impregnation process is seen to increase significantly the resistance of the pressure. Parallel fibers that increase the pressure resistance up to 190°C, but after that point the decline has been observed. Boric acid treated and heat-treated samples showed higher, pressure resistance values than borax treated samples, it has been seen that impregnated heated samples gave higher values of pressure resistance. it colour change at the heat-treated samples is colour of change was occur in parallel with increase in the temperature. The total colour change was less in impregnated samples.

Benzer Tezler

  1. Boraks ve borik asit ile emprenye edilmiş ve ısıl işlem görmüş karaçam odununun bazı fiziksel ve mekanik özellikleri

    The same physical and mechanical properties of impregnated with borax and boric acid and heat-treated black pine wood

    BİLAL DOĞAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Ağaç İşleriKütahya Dumlupınar Üniversitesi

    İleri Teknolojiler Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ OSMAN PERÇİN

  2. Doğal emprenye maddeleri ve borlu bileşikler ile emprenye edilen sarıçam (Pinus sylvestris L.) odununun fiziksel ve mekanik özelliklerinin incelenmesi

    Determination of physical and mechanical properties of scotch pine (Pinus sylvestris L.) wood which impregnated boron compounds and naturel substances

    ELİF ALKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Ağaç İşleriGümüşhane Üniversitesi

    Ormancılık ve Çevre Bilimleri Ana Bilim Dalı

    DOÇ. DR. SELİM ŞEN

    YRD. DOÇ. DR. MUHAMMED SAİD FİDAN

  3. Borlu bileşikler ile emprenye işleminin bazı ağaç malzeme ve verniklerde sertlik ve aşınma direncine etkisi

    Effects of boric combinations and impregnation process on resistance of hardness and abrasion of some wooden materials and varnishes

    MUTLU SARICA

    Yüksek Lisans

    Türkçe

    Türkçe

    2006

    Ağaç İşleriGazi Üniversitesi

    Mobilya ve Dekorasyon Eğitimi Ana Bilim Dalı

    DOÇ.DR. MUSA ATAR

  4. Yanmayı geciktirici madde olarak bor minerallerinin odun ve odun-plastik kompozitlerde kullanımı

    Using of boron minerals in wood and wood plastic composites as fire retardants

    EVREN TERZİ

    Doktora

    Türkçe

    Türkçe

    2015

    Ağaç İşleriİstanbul Üniversitesi

    Orman Endüstri Mühendisliği Ana Bilim Dalı

    PROF. DR. SAİP NAMİ KARTAL

    PROF. DR. SABRİYE PİŞKİN

  5. Çeşitli kimyasal maddelerle emprenye edilen lamine ağaç malzemelerin yanma mukavemetinin araştırılması

    Research on combustion properties laminated veneer lumber of impregnated with some chemicals materials

    LÜTFİ KÖSE

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Teknik EğitimKarabük Üniversitesi

    Mobilya ve Dekorasyon Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. HAMİYET ŞAHİN KOL