Bor katkılı 316L paslanmaz çeliklerin korozyon davranışlarının elektrokimyasal yöntemle incelenmesi
Electrochemical investigation of corrosion behavior for boron added 316L stainless steels produced by powder injection molded (PIM) method
- Tez No: 304638
- Danışmanlar: DOÇ. DR. HASAN KILIÇ
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2012
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Fizikokimya Bilim Dalı
- Sayfa Sayısı: 135
Özet
Bu çalışmada bor katkılı 316L paslanmaz çelik elektodunun korozyon davranışı farklı çözelti ortamlarında elektrokimyasal yöntemler ile karakterize edilmiştir. Bu paslanmaz çelik elektrot ağırlıkça % 1.5 oranında bor ilave edilerek Toz Enjeksiyon Kalıplama (TEK) yöntemi ile üretilmiştir. Elektrokimyasal karakterizasyon işlemi potensiyodinamik polarizasyon (Tafel eğrileri) ve alternatif akım empedans spektroskopisi (Nyquist eğrileri) yöntemleri ile gerçekleştirilmiştir. Deneysel çalışmalar 1M HCl, 1M H2SO4, 1M NaCl, 0.5M Na2SO4 ve SBF (biyolojik vücut sıvısı eşdeğeri) çözeltileri ortamında gerçekleştirilmiştir. SBF çözeltisinin pH değeri 7.40'dır. 0.5M Na2SO4 çözeltisi ortamında ise pH değerleri 2.00, 3.00, 4.00 ve 5.00 olarak ayarlanmıştır.Bor katkılı 316L paslanmaz çelik elektrodun korozyon davranışı döküm yöntemi ile üretilen 316L (W 316L) ve TEK yöntemi ile üretilen 316L (316L) paslanmaz çelik elektrotlar ile karşılaştırılmıştır. W 316L ve 316L elektrotlarda bor katkısı bulunmamaktadır. Elektrotlar arasındaki karşılaştırma 1M HCl, 1M H2SO4, 1M NaCl ve SBF çözeltileri ortamında yapılmıştır. 0.5M Na2SO4 çözeltisi ortamında ise 316L+NiB elektrodunun korozyon davranışı farklı pH değerlerinde incelenmiştir.1M HCl, 1M H2SO4 and SBF çözeltileri ortamlarında W 316L elektrodunun korozyon akım yoğunluğunun ve korozyon oranının diğer elektrotlara göre (316L ve 316L+NiB) daha az olduğu bulunmuştur. Ayrıca 316L+NiB elektrodunun korozyon akımının da 316L elektrottan daha az olduğu görülmüştür. Böylece en yüksek korozyon direncine sahip elektrodun W 316L, en düşük korozyon direncine sahip elektrodun ise 316L elektrodu olduğu bulunmuştur. Böylece elektrotların korozyon dirençleri sıralamasının da W 316L > 316L+NiB > 316L şeklinde olduğu görülmüştür. Bu sıralama 1M NaCl çözeltisi ortamında 316L+NiB > W 316L > 316L şeklinde elde edilmiştir. Diğer taraftan 0.5M Na2SO4 çözelti ortamında pH değeri arttıkça 316L+NiB elektrodun korozyon direncinin de arttığı bulunmuştur.Mart - 2012Özay ER
Özet (Çeviri)
In this study, corrosion behavior of boron added 316L stainless steel electrode was characterized by electrochemical methods in different solution media. The electrode was made of 1.5 wt % boron added and produced by powder injection molded (PIM) method. The electrochemical characterizations were carried out both by potentiodynamic polarization (Tafel curve) method and ac impedance spectroscopy (Nyquist curve) method. The experiments were conducted in 1M HCl, 1M H2SO4, 1M NaCl, 0.5M Na2SO4 solution media. Similar experiments were also conducted in SBF (simulated body fluid) solution medium at a pH value of 7.40. However, the 0.5M Na2SO4 solution was prepared at different pH values such as 2.00, 3.00, 4.00 and 5.00.Corrosion behavior of boron added 316L (or 316L+NiB) stainless steel electrode was compared with both a wrought 316L (W 316L) stainless steel and a PIM 316L (316L) electrodes which were not containing boron addition. These comparison were made through the results obtained in 1M HCl, 1M H2SO4, 1M NaCl and SBF solution media. On the other hand, the same corrosion characterization processes of boron added 316L (or 316L+NiB) electrode was carried out in 0.5M Na2SO4 solutions prepared at different pH values given above.Corrosion current density and corrosion rate for W 316L electrode were found to be less than that of the 316L and 316L+NiB electrodes in 1M HCl, 1M H2SO4 and SBF solution media. Similarly, 316L+NiB electrode was found to show less corrosion current density and corrosion rate with respect to the 316L electrode. Therefore, W 316L electrode was found to have the biggest corrosion resistance. In contrast, 316L electrode was found to have the smallest corrosion resistance. Thus, the corrosion resistances for the electrodes were W 316L > 316L+NiB > 316L. However, it was found as 316L+NiB > W 316L > 316L in 1M NaCl solution medium. On the other hand, the corrosion resistance of 316L+NiB electrode was found to increase on increasing the pH from 2.00 to 5.00.March ? 2012Ozay ER
Benzer Tezler
- Bor ilaveli ostenitik paslanmaz çeliklerin toz enjeksiyon kalıplama metodu ile üretilmesi ve karekterizasyonu
Production and characterization of boron added austenitic stainless steel by powder injection molding method
ESRA BAYRAKTAROĞLU
Yüksek Lisans
Türkçe
2012
Metalurji MühendisliğiMarmara ÜniversitesiMetal Eğitimi Ana Bilim Dalı
DOÇ. DR. H. ÖZKAN GÜLSOY
- Toz metalurjisi yöntemiyle elde edilen gözenekli martensitik paslanmaz çeliğin mikroyapısı ve mekanik özellikleri
Microstructural and mechanical properties of porous martensitic stainless steel obtained by powder metallurgy method
İLVEN MUTLU
Doktora
Türkçe
2011
Metalurji Mühendisliğiİstanbul ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ENVER OKTAY
- AISI 316L paslanmaz çelik matrisli, bor karbür ve karbon nanotüp takviyeli nanokompozitlerin toz metalurjisi ile üretimi ve karakterizasyonu
Production and characterization of AISI 316L stainless steel matrix, boron carbide and carbon nanotube reinforced nanocomposites by powder metallurgy
ESRA ZENGİN
Yüksek Lisans
Türkçe
2021
Metalurji MühendisliğiKarabük ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. HAYRETTİN AHLATCI
- Bor katkılı portland çimentosu ile üretilen betonların mühendislik özellikleri ve yüksek sıcaklık etkisi
The engineering properties and high temperature effects of concrete produced with portland cement boron mixtured
HAVVA ECE PEHLİVANOĞLU
Yüksek Lisans
Türkçe
2014
İnşaat MühendisliğiSüleyman Demirel ÜniversitesiYapı Eğitimi Ana Bilim Dalı
DOÇ. DR. ŞEMSETTİN KILINÇARSLAN
DOÇ. DR. METİN DAVRAZ
- Bor katkılı özellikli beton üretimi
Specified concrete production containing boron
HAKAN SARIKAYA
Doktora
Türkçe
2014
Mühendislik BilimleriSüleyman Demirel ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
PROF. DR. RAŞİT ALTINDAĞ