Aktif karbon katkılı zirkonyum-silisyum karışık oksit jel kürecikleri ile stronsiyum adsorpsiyonunun merkezi kompozit tasarım yöntemi kullanılarak incelenmesi
Investigation of strontium adsorption on active carbon added zirconia-silica mixed oxide gel spheres by central composite desing method
- Tez No: 304832
- Danışmanlar: PROF. DR. HÜSEYİN TEL
- Tez Türü: Yüksek Lisans
- Konular: Nükleer Mühendislik, Kimya, Nuclear Engineering, Chemistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2012
- Dil: Türkçe
- Üniversite: Ege Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Nükleer Bilimler Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada aktif karbon katkılı ZrO2?SiO2 jel kürecikleri sentezlenmiş ve elde edilen adsorbanın karakterizasyonu XRD, SEM, yüzey alanı ve porozite, DTA/TGA ve FT-IR analizleri ile yapılmıştır. Karakterize edilen adsorbanın stronsiyum adsorpsiyonunda kullanımı incelenmiştir.Stronsiyum alım denemeleri kesikli yöntem ile gerçekleştirilmiş, adsorpsiyona etki eden parametreler deneysel tasarım yöntemi içerisinde, merkezi kompozit tasarım kullanılarak incelenmiştir. Çalışmada, dört bağımsız değişken olarak ortamın başlangıç pH'ı, sıcaklık, başlangıç derişimi ve çalkalama süresi belirlenmiştir. En küçük kareler yöntemi kullanılarak regresyon katsayıları bulunmuş, merkezi kompozit tasarımdan elde edilen polinomal denkleme göre cevap yüzey grafikleri oluşturulmuştur. Uygulanan modelin %95 güven aralığı içerisindeki ANOVA (analysis of variance) analizi incelenmiş ve model ile deneysel bulguların uyumuna bakılmıştır. Modelin önemlilik F değerinin P<0.05 ve model F değerinin 26.20 olarak elde edilmesi, regresyonunun istatistikî olarak yüksek değer gösterdiğini belirtmektedir. Korelasyon katsayısı (R2) değerinin %97 olarak belirlenmesi, gözlenen değerlerle öngörülen değerler arasında yüksek bir uyumluluk olduğunu göstermektedir. Her bir etkenin, karelerinin ve etkenler arasında etkileşimin istatistiksel incelenmesi ve adsorpsiyon prosesine olan etkilerinin değerlendirilmesi gerçekleştirilmiştir.Adsorpsiyon üzerinde; pH, sıcaklık, başlangıç derişimi ve çalkalama süresi ana etkilerinin önemli, fakat ana etkinin karesine bağlı olarak önemsiz olduğu, buna karşılık ikili etkileşimlerden; pH ve derişim, sıcaklık ve derişimin adsorpsiyon üzerinde etkili olduğu görülmüştür. Optimum adsorpsiyon koşulları; pH= 8.2, sıcaklık 20 oC, başlangıç Sr+2 konsantrasyonu 90 ppm ve çalkalama süresi 382 dakika olarak hesaplanmış ve maksimum değer 24 mg/g olarak elde edilmiştir.
Özet (Çeviri)
In this work, activated carbon added ZrO2?SiO2 gel spheres were synthesized and the characterization of obtained adsorbent were made by XRD, SEM, surface area and porosity analyses, DTA/TGA and FT-IR. This use of the characterized adsorbent on strontium adsorption was investigated.The strontium uptake experiments have been carried out by the batch method. The parameters affecting the adsoprtion were analyzed by using central composite design as the experimental design method. For this study four parameters; initial pH, temperature, initial concentration and shaking time were selected as indipendent variables. The regression coefficents were obtained by the least squares method and the responce surface plots were generated according to polynomial equation which is derived from central composite design. The ANOVA (analysis of variance) data were carried out in 95% confidence level and checked to fitting of experimental value and predicted value. The significant F was P<0.05 with a model F value of 26.20 which revealed that this regression is statistically significant. The correlation coefficient value (R2) of 97% showed that there was a high correlation between the observed values and the predicted ones. The main effects, main affects squares and the interactions of main affects were statistically analyzed and influences of affects on the adsorption process were considered.The influences of initial pH, temperature, initial concentration and shaking time on the adsorption process were evaluated. pH, temperature, initial concentration were considered statistically significant. The shaking time was considered as statistically significant according to square of main affect, although its main affect was considered statistically non-significant. On the other hand, binary interaction effects of initial pH and initial concentration, temperature and initial concentration were considered as significant parameters on the adsorption process.The optimum Adsorption conditions were: pH= 8.2, temperature= 20 oC, intial Strontium concentration 90 ppm, shaking time 182 minutes and the maximum Sr2+ adsorption in these conditions were found to be (24 mg/g adsorbent).
Benzer Tezler
- Synthesis and characterization of hafnium boride-based ceramic powders
Hafniyum borür-esaslı seramik tozlarının sentezlenmesi ve karakterizasyonu
NAZLI AKÇAMLI
Doktora
İngilizce
2016
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. İSMAİL DUMAN
- Aktif karbon katkılı nanoliflerin adsorpsiyon özelliklerinin incelenmesi
Investigation of the adsorption properties of activated carbon doped nanofibers
RAGIPHAN ÖZTURAN
Yüksek Lisans
Türkçe
2022
Mühendislik BilimleriUşak ÜniversitesiMalzeme Bilimi ve Nanoteknoloji Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GAMZE TETİK
- Aktif karbon katkılı çimentolu yonga levhaların bazı mekanik ve fiziksel özelliklerinin incelenmesi
Investigation of some mechanical and physical properties of activated carbon added cement composite materials
MÜBERRA DEMİRBÜK
Yüksek Lisans
Türkçe
2023
Mühendislik BilimleriKahramanmaraş Sütçü İmam ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GONCA DÜZKALE SÖZBİR
PROF. DR. İBRAHİM BEKTAŞ
- Aktif karbon katkılı PVA/nişasta membranın doku onarımında kullanabilirliğinin değerlendirilmesi
Evaluation of activated carbon-modified PVA/starch membrane for tissue repair applications
NESLİŞAH ÇELİKKAYA
Yüksek Lisans
Türkçe
2025
Polimer Bilim ve TeknolojisiYıldız Teknik ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. CENK DENKTAŞ
- Levha endüstrisi atıklardan üretilmiş aktif karbon katkılı düşük formaldehit emisyonlu ekolojik lif levha üretimi
Production of ecological fiber board with low formaldehyde emission with activated carbon made from board industry wastes
AYŞE EBRU AKIN
Yüksek Lisans
Türkçe
2022
Kimya MühendisliğiSüleyman Demirel ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. MUSTAFA KARABOYACI