Kitre katkılı genleştirilmiş kil agregalı betonların ısıl ve mekanik özelliklerinin analizi

Analysis of thermal and mechanical properties of tragacanth additive expanded clay aggregate concretes

  1. Tez No: 306953
  2. Yazar: ATİLLA GENCER DEVECİOĞLU
  3. Danışmanlar: PROF. DR. YAŞAR BİÇER
  4. Tez Türü: Doktora
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2012
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Enerji Bilim Dalı
  13. Sayfa Sayısı: 115

Özet

Bu çalışmada, genleştirilmiş kil agregası, doğal bir reçine olan kitre ve çimentonun farklı oranlarda karışımı ile hem depreme dayanıklı hem de enerji tasarrufu sağlayan hafif betonun üretilmesi amaçlanmıştır.Deneysel numunelerde, 0-2, 2-4 ve 4-8 mm tane çaplı genleştirilmiş kil agregası, çimento ile ağırlıkça %20, %40, %60 ve %80 oranında karıştırılmıştır. Karışımlara ayrıca ağırlıkça %0.5, %1, %1.5 oranında kitre eklenmiştir. Karşılaştırma yapmak için üretilen kitre katkısız numunelerle birlikte toplam 48 adet numune üretilmiştir. Kullanılan genleştirilmiş killer Liapor firmasından temin edilmiştir. Çalışmada CEM IV/B 32.5 R tipi puzolanik çimento ve yaprak kitre kullanılmıştır. Üretilen numunelere ısı iletim katsayısı k, hacimsel özgül ısı cp, basınç dayanımı fck, su emme, kuruma hızı, aşınma oranı ve ultrases geçiş hızı deneyleri uygulanmıştır. Isı iletim katsayısının teorik olarak tespiti için matematiksel bir model geliştirilerek, deneysel sonuçlarla mukayese edilmiştir. Teorik hesaplamaların, deneysel sonuçlarla uyumlu olduğu görülmüştür.Numunelere eklenen kitre miktarı arttıkça, ısı iletim katsayısı ve basınç dayanımı düşmektedir. En düşük ısı iletim katsayısı 0.133 W/mK ile 4-8 mm tane çapına sahip, %80 genleştirilmiş kil agregası içeren ve %1.5 kitre katkılı numunede olduğu görülmüştür. 0-2 mm tane çaplı, %20 genleştirilmiş kil katkılı numunelerde, kitre katkısız numune ile %0.5 kitre katkılı numunenin ısı iletim katsayıları arasında %21 oranında fark bulunmuştur. %20 oranında genleştirilmiş kil agregası içeren ve %0.5 kitre katkılı numunenin yoğunluğu 1.8 g/cm3 gibi çok düşük bir değer bulunmuştur. Bu yoğunluk değeriyle numune hafif beton sınıfına girmektedir. En yüksek basınç dayanımı 22.3 MPa ile %20 genleştirilmiş kil agregası içeren kitre katkısız numunelerin sahip olduğu görülmüştür. Numunelerin su emme oranı kritik değer olan %30 sınırının üzerinde veya çok az altında çıkmıştır.

Özet (Çeviri)

In this study, production of lightweight concrete, which is both earthquake resistant and energy saving, was aimed by mixing of expanded clay, natural resin tragacanth and cement with different ratios.0-2 mm, 2-4 mm and 4-8 mm grain diameter expanded clays were mixed with cement by weight of 20%, 40%, 60% and 80% for the experimental samples. The tragacanth was also added to the mixtures by weight of 0.5%, 1%, 1.5%. For making comparison, 48 samples produced totally with and without tragacanth. The expanded clays used in study were obtained from Liapor Company, Austria. CEM IV / B 32.5 R type pozzolanic cement and leaf tragacanth were used in the study. The thermal conductivity k, volumetric specific heat cp, compressive strength fck, water absorption, drying rate, wear rate and ultrasonic experiments were applied on samples. A mathematical model was developed to determine thermal conduction coefficient theoretically and it was compared to the experimental results. It was seen that theoretical calculations agreed with the experimental results.As a result, both thermal conduction coefficient and the compressive strength decreased as the amount of tragacanth increased. The lowest thermal conduction coefficient was measured to be 0.133 W / mK for 4-8 mm grain diameter with 80% expanded clay aggregates and 1.5% tragacanth additive. For the 0-2 mm grain diameter samples with 20% expanded clay aggregates, the difference in thermal conduction coefficient between the tragacanth-free and 0.5% tragacanth additive samples was found to be 21%. The density of the sample with 20% expanded clay aggregate and 0.5% tragacanth was determined as low as 1.8 g/cm3. The sample can be classified as lightweight concrete because of this density value. It was seen that the highest compressive strength value was 22.3 MPa for the samples of 20% expanded clay aggregate without tragacanth additive.

Benzer Tezler

  1. Genleştirilmiş polistren (EPS) atığının çeşitli bağlayıcı kombinasyonlarında yeniden değerlendirilmesi

    Reuse of expanded polystyrene (EPS) waste in various binding combinations

    AYŞE KAYA

    Doktora

    Türkçe

    Türkçe

    2016

    Kimya MühendisliğiFırat Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ. DR. FİLİZ KAR

  2. Pomza agregası, atık mermer tozu ve kitre katkılı çimento esaslı kompozit malzemenin mühendislik özelliklerinin incelenmesi

    Pumi̇ce aggregates of marble dust and analysis of waste tragacant mixed cement based composite material properties of engineering

    ŞERMİN KOÇYİĞİT

    Doktora

    Türkçe

    Türkçe

    2016

    Teknik EğitimFırat Üniversitesi

    Yapı Eğitimi Ana Bilim Dalı

    PROF. DR. SERVET YILDIZ

  3. Stratejik iletişim yönetiminin sürdürülebilirliğe ve sağlık okuryazarlığına katkısı: Deneysel bir çalışma

    The contrubition of strategic communication management to sustainability and health literacy: An experimental study

    FİGEN SABIRCAN

    Doktora

    Türkçe

    Türkçe

    2017

    Halkla İlişkilerİstanbul Üniversitesi

    Halkla İlişkiler ve Tanıtım Ana Bilim Dalı

    PROF. DR. AYLA OKAY

  4. Dijital kamusal alan oluşumu üzerine bir inceleme: Twitter'da Kanal İstanbul tartışmaları

    A review on digital public sphere formation: Canal İstanbul discussions on twitter

    BÜŞRA KAYA

    Doktora

    Türkçe

    Türkçe

    2022

    Siyasal BilimlerPamukkale Üniversitesi

    Siyaset Bilimi ve Kamu Yönetimi Ana Bilim Dalı

    PROF. DR. İSMET PARLAK

  5. Hybrides sprachlerncoaching - am beispiel der vorbereitungsklasse der Uludağ Universität

    Hibrit dil öğrenme koçluğu - Uludağ Üniversitesi hazırlık sınıfları örneği

    MEHMET DOĞAN

    Doktora

    Almanca

    Almanca

    2021

    Alman Dili ve EdebiyatıTrakya Üniversitesi

    Yabancı Diller Eğitimi Ana Bilim Dalı

    PROF. DR. MUKADDER SEYHAN YÜCEL