Mineral katkılı hafif betonlarda sülfat etkisi
The effect of the sulfate on the mineral lightweight concrete
- Tez No: 324737
- Danışmanlar: PROF. DR. RÜSTEM GÜL
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Pomza, Uçucu kül, Silis dumanı, Sodyum sülfat, Hafif beton, Basınç dayanımı, Pumice, Fly ash, Silica fume, Sodium sulfate, Lightweight concrete, Compressive strength
- Yıl: 2013
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 91
Özet
Bu çalışmada mineral katkı maddesi ilave edilmesi ile üretilen pomzalı hafif betonların değişik sülfat oranlarında özellikleri incelenmiştir. Deneylerde %15 ve %30 silis dumanı, %15 ve %30 uçucu kül ilaveli dört seri beton üretilmiştir. Karşılaştırma yapmak amacıyla mineral katkı içermeyen karışımlar da üretildi. Toplam 180 adet 10×20 cm silindir beton numuneleri hazırlanmış ve sırasıyla %5 ve %10 sodyum sülfat (Na2SO4) çözeltisinde ve standart kür havuzunda kireçe doygun suda bekletilmiştir. Standart kür havuzuna bırakılan ve sülfat etkisine maruz kalan beton numunelerin üzerinde belli aralıklarla (28, 56 ve 120.) günlerde basınç dayanımı, birim ağırlık, kılcal su emme, ve ultrases geçiş süresi deneyleri yapılmıştır. Deneyler TS EN 1097?6 ve TS 12350?2 standartlarına göre yapılmıştır.Sonuçta standart küre maruz betonlarda en yüksek dayanıma %15 silis dumanı ilaveli betonlarda rastlanmıştır. Bunu sırasıyla %15 uçucu kül ilaveli, mineral katkı içermeyen, %30 silis dumanı ilaveli ve %30 uçucu kül ilaveli betonlar takip etmiştir. En düşük dayanımı veren betonlar %30 uçucu kül ilaveli betonlar olmuştur.%5 ve %10 sodyum sülfat çözeltisinde bekletilen beton numunelerin davranışları ilk yaşlarda standart küre maruz beton numunelerine yakın olduğu görülmüştür. İlerleyen yaşlarda ve 120. günde en iyi performans %15 silis dumanı ilaveli beton numunelerinde rastlandı. Aynı zamanda, 120. günde mineral katkı içermeyen beton numunelerin üzerinde yapılan basınç dayanımı deneylerinde fazla miktarda bir azalma kayd edilmiştir.Mineral katkıların betonun sülfat ortamında performansını artırdığı, araştırma sonucunda tespit edilmiştir.
Özet (Çeviri)
In this study, the properties of pumice based lightweight concrete which is produced by adding mineral admixtures, were examined in different sulfate ratios. In the experiments, 15% and 30% silica fume, 15% and 30% fly ash added to concrete and four series of concrete were produced. For comparing the casting specimens, conventional concrete has been produced without any mineral admixtures. Generally, 180 pieces 10×20 cm cylindrial concrete specimens prepared and has been kept in 5% or 10% sodium sulfate (Na2SO4) in a standard curing pool. The specimens which has been cured in the curing pool. The ones which were exposed to the sulfate attack, after 28, 56 and 120 days has been tested for compressive strength, unit weight, capillary water absorbtion and ultrasonic tests. The experiments have been conducted according to TS EN 1097?6 and TS 12350?2.As a result, in the specimens which were subjected to standard curing, the high compressive strength was found by adding 15% silica fume. This was fallowed by adding 15% fly ash, without any mineral admixtures (Conventional Concrete), 30% silica fume and 30% fly ash. The minimum compressive strength has been obtained by adding 30% fly ash.The specimens which were cured in the 5% and 10% sodium sulfate had close behavior to the control specimens of the first days. By time elapsing at 120?th day, the best performance have been founed in the specimens with 15% silica fume. At the same time, in 120?th day the control specimens had a remarkable reduction in compressive strength.Therefore, in this study it has been identifid mineral admixtures were effective on the concrete while it was exposed to sulfate.
Benzer Tezler
- Pomza katkılı normal ve hafif betonların kimyasal durabilitesinin incelenmesi
Analysis of the chemical stability of normal and lightweight concretes that produced with pumice aggregate
TAHA SALAH WAHHAB AL-ANTAKI
Yüksek Lisans
Türkçe
2020
İnşaat Mühendisliğiİstanbul Gelişim Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ANIL NİŞ
- Pomza ve perlit agregası içeren mineral katkılı taşıyıcı hafif betonların enerji performansı açısından değerlendirilmesi
Evaluation of mineral additives added structural lightweightconcrete containing pumice and perlite aggregates in terms ofenergy performance
SAFA NAYIR
Doktora
Türkçe
2021
İnşaat MühendisliğiKaradeniz Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. ŞAKİR ERDOĞDU
- Silis dumanı ve çelik lif katkılı hafif beton özelliklerinin incelenmesi
Investigation of the properties of lightweight concrete added with silica fume and steel fiber
ABDULLAH SASİ ABDULLAH ALTABEEB
Yüksek Lisans
Türkçe
2021
İnşaat MühendisliğiKastamonu ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SELÇUK MEMİŞ
- Endüstriyel atık katkılı kendiliğinden yerleşen hafif beton üretilebilirliğinin araştırılması
The investigation of producibility self compacting lightweight concrete with industrial wastes additives
ZEHRA FUNDA TÜRKMENOĞLU
Doktora
Türkçe
2017
Maden Mühendisliği ve MadencilikÇukurova ÜniversitesiMaden İşletme Ana Bilim Dalı
PROF. DR. AHMET MAHMUT KILIÇ
- Structural lightweight concrete with natural perlite aggregate and perlite powder
Doğal perlit agregalı ve öğütülmüş perlit katkılı taşıyıcı hafif beton
MESUT AŞIK
Yüksek Lisans
İngilizce
2006
İnşaat MühendisliğiOrta Doğu Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. LUTFULLAH TURANLI