(Sm1-xNdx)Ba2Cu3O7- süper iletkenlerinin elektrik, manyetik ve yapısal özelliklerinin incelenmesi

The investigation of electrical, magnetic and structure properties os (Sm1-xNdx)Ba2Cu3O7- superconductors

  1. Tez No: 342893
  2. Yazar: ELVAN COŞKUN
  3. Danışmanlar: DOÇ. DR. ŞÜKRÜ ÇELİK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
  6. Anahtar Kelimeler: Sm123, Nd123, Magnetik Levitasyon Kuvveti, Kritik Akım Yoğunluğu, Kritik Geçiş Sıcaklığı, Aktivasyon Enerjisi, Sm123, Nd123, Magnetic Levitation Force, Critical Current Density, Critical Transition Temperature, Activation Energy
  7. Yıl: 2013
  8. Dil: Türkçe
  9. Üniversite: Recep Tayyip Erdoğan Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Fizik Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 82

Özet

(Sm1-xNdx)Ba2Cu3O7-Süperiletkenlerinin Elektrik, Manyetik ve Yapısal Özelliklerinin İncelenmesi (Sm1-xNdx)Ba2Cu3O7-yapısına ait x=0.0, 0.2, 0.4, 0.6, 0.8 ve 1.0katkı oranlarında süperiletken örnekler katıhal tepkime yöntemiyle hazırlandı. İlk olarak, farklı sıcaklıklarda sinterlenerek Sm123 (SmBa2Cu3O7-) örnekleri üretildi ve manyetik kaldırma kuvvetleri karşılaştırılarak serinin örnekleri için en uygun sinterleme sıcaklığı belirlendi. Serideki örneklere aynı ısıl işlemleruygulandı. Üretilen örneklerin XRD spektrumları, farklı hızlarda hava ortamında sıvı azot sıcaklığında manyetik kaldırma kuvveti, farklı manyetik alanlarda alansız soğutma sonrası direncin sıcaklığa göre değişimi ve SEM ölçüldü. XRD ölçümlerinden hesaplanan c örgü parametresi katkı arttıkça S02 örneği dışında 11.7278Å- 11.7399 Å arasında değişmektedir. Sıcaklığa göre direnç ölçüm sonuçları ve hesaplanan aktivasyon enerjileri katkıya göre karşılaştırıldığında, katkı x=0.4ten daha yüksek değerlere arttıkça yapıda yarıiletken fazın arttığı, özellikle x=0.8 değerinden sonra süperiletkenlik özelliğinin azaldığı ve yarıiletken fazın belirgin bir şekilde arttığı görüldü. Aktivasyon enerjisi (S02 örneği hariç) katkı arttıkça azalmaktadır. S02 örneğinin aktivasyon enerjisi diğerlerine göre hayli yüksek değerde ve direnç sıcaklık değişimleri kıyaslandığında çok düşük ikincil fazın bulunmasına rağmen en dar geçiş sıcaklık aralığı S02 örneğine ait olduğu görülmektedir. Katkı arttıkça, manyetik kaldırma kuvveti azalmakta hatta x=0.6 katkısından sonra kaldırma kuvvetinin yanında çekme kuvvetinin belirginleştiği ve bu çekmenin x=1.0 katkılı örneğin kaldırma kuvvetinde hemen hemen çekme kuvveti görülmektedir. Seride uygulanan ısıl işlemde seçilen sinterleme sıcaklığı Sm123ün peritektik reaksiyon sıcaklığına çok yakın fakat Nd123?ün peritektik reaksiyon sıcaklığından daha düşük olması sonucunda x=0.4ten daha büyük katkılı örneklerde Nd123ün daha baskın faz olması sonucunda yapının kötüleştiği görülmektedir. Sonuç olarak, üretilen örnekler içinde elektriksel ölçümler S02 örneğinin en iyi örnek olduğunu ve aynı örneğin manyetik kaldırma kuvveti sonuçlarında S00 örneğinin sonuçlarına yakın olduğu görülmektedir. Dolayısıyla örnekler içinde x=0.2 katkılı örnek en uygun katkılı örnek olduğu belirlendi. Bu katkıda Sm123 yapısında Nd123ün etkisinin aktivasyon enerjisini artırdığı görülmektedir. Bu da yapı içinde akı çivileme kuvvetini artırmaktadır.

Özet (Çeviri)

The investigation of electrical, magnetic and structure properties os (Sm1-xNdx)Ba2Cu3O7-? superconductors (Sm1-xNdx)Ba2Cu3O7-?samples were fabricated by solid-state reaction method for the values of x=0.0, 0.2, 0.4, 0.6, 0.8 and 1.0. Firstly, Sm123 (SmBa2Cu3O7-?) samples with different sintering temperatures are produced, and compared with magnetic levitation force measurements of them, then, the optimum sintering temperature was determined. The same thermal processes wereapplied to all the samples. The measurement of X-ray diffraction, magnetic levitation force under various velocities at liquid nitrogen temperature in air atmosphere, the resistivity versus temperature in various magnetic fields after zero cooling regime (ZFC) and SEM of samples were performed. c latticeparameter of the samples,calculated from XRD patternsvaried between 11.7278 Åand 11.7399 Å with increasing of x, except for S02. According to resistivity versus temperature measurements and calculated activation energy results from them, it was observed that semiconducting phase increased with the increasing of x above x=0.4, and, superconductor properties decreased and semiconductor phase clearly increasedespecially above x=0.8. Activation energy (except for S02) decreasedwith increase of x. Activation energy of S02 has higher value than that of the others. When the resistivity-temperature variations of the samples were compared, although S02 contains very low secondary phase, it is shown that the narrowest transition temperature range belongs to S02. Magneticlevitation force decreased with increase of the content x. Even for higher values of x above 0.6, there is not only magnetic levitation force but also pulling force and this pulling force was observed nearly in the magnetic levitation force measurement results of S10. Because the selected sintering temperature which was appliedto the samples is near to the peritectic reaction temperature of Sm123 andto lower than that of Nd123. Consequently it was observed that samples of (Sm1-xNdx)Ba2Cu3O7-?structure with high values of x especially above 0.4 got worse because the dominant is Nd123. Finally;electrical measurement results showed that S02 is the best among the others, and it is observed that magnetic levitation force measurement results of S02 is near to that of S00. So, the best value of x is 0.2 among the samples according to the results. It was estimated that the effect of x in the S02 increased of the activation energy, and resulted in increase of the pinning force.

Benzer Tezler

  1. Sm1-xTbxNi4B bileşiklerinin fiziksel özelliklerinin araştirilmasi

    Investigation of physical properties of Sm1-xTbxNi4B compounds

    ONUR NANE

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    Fizik ve Fizik MühendisliğiÇukurova Üniversitesi

    Fizik Bölümü

    PROF. DR. BEKİR ÖZÇELİK

  2. Sm1-xGdxNi4B bileşiklerinin fiziksel özelliklerinin araştırılması

    Investigation of physical properties of Sm1-xGdxNi4B compounds

    NİLAY KANTARCI

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    Fizik ve Fizik MühendisliğiÇukurova Üniversitesi

    Fizik Bölümü

    PROF. BEKİR ÖZÇELİK

  3. Nano bor katkısının yüksek sıcaklık süperiletken seramiklere etkilerinin incelenmesi

    Investigation of nano boron doping effects into high temperature superconductor

    MÜNİR TANER GÜLER

    Doktora

    Türkçe

    Türkçe

    2021

    Fizik ve Fizik MühendisliğiNiğde Ömer Halisdemir Üniversitesi

    Fizik Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ SELVA BÜYÜKAKKAŞ

  4. Yüksek sıcaklık süperiletkenlerine nano parçacık katkılama etkilerinin incelenmesi

    Investigation of effects of doping of nanoparticles on high-temperature superconductors

    DENİZ YILDIRAN

    Doktora

    Türkçe

    Türkçe

    2017

    Fizik ve Fizik MühendisliğiNiğde Ömer Halisdemir Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ. DR. İBRAHİM KARACA

  5. Üstten tohumlama yöntemi ile YBCO süper iletkeni üretimi ve fiziksel özelliklerinin incelenmesi

    Producing and investigating of physical properties of the YBCO superconductor by the top seed method

    NİHAT ŞİMŞEK

    Doktora

    Türkçe

    Türkçe

    2016

    Fizik ve Fizik MühendisliğiNiğde Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ. DR. İBRAHİM KARACA