Fe-%17.2Mn%4.5Mo alaşımında difüzyonsuz faz dönüşümlerinin elektron mikroskop ve mössbauer spektroskopi yöntemleri ile incelemesi
Investigation of diffusionless phase transformation in Fe17.2%Mn4.52%Mo alloy by means of electron microscopy and mössbauer spectroscopy
- Tez No: 344029
- Danışmanlar: DOÇ. DR. UĞUR SARI
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Fe-Mn-Mo alaşımı, martensitik dönüşüm, homojenleştirmesıcaklığı, deformasyon, elektron mikroskop, mössbauer spektroskopi, Fe-Mn-Mo alloy, martensitic transformations, annealing temperature, deformation, electron microscopy, Mössbauer spectroscopy
- Yıl: 2012
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 102
Özet
Bu çalışmada, Fe-%17.2Mn-%4.5Mo alaşımının mikroyapısı ve manyetik özellikleri üzerinde homojenleştirme sıcaklığı ve deformasyon etkisi elektron mikroskop ve mössbauer spektroskopisi yöntemleri kullanılarak incelendi. Deneysel çalışmalar sonucunda alaşımın yüksek sıcaklıklardan hızla soğutulduğunda martensitik dönüşüm gerçekleştiği ve austenite ana fazın (b.c.c.) ve ? (h.c.p.) martensite yapılara dönüştüğü görüldü.Alaşımın mössbauer spektrum analizinde, ? austenite ve ? martensite fazların tekli pik ile paramanyetiklik gösterdiği martensitenin ise altılı pik ile ferromanyetik özellik gösterdiği belirlendi.Homojenleştirme sıcaklığına bağlı olarak ve ? martensite miktarı ve manyetik özellikleri değişmiştir. 1200 homojenleştirme sonrası martensite en yüksek değere, (?+?) faz ise en düşük değere sahiptir. 1050 ise ? martensite oluşumu için en uygun sıcaklık olarak tespit edilmiştir.Ayrıca austenite fazın deformasyonunun martensite fazın miktarını ve türünü etkilediği belirlenmiştir. Deformasyon oranı arttıkça martensitenin miktarı artmıştır.
Özet (Çeviri)
In this study, the effects of deformation and homogenization temperature on microstructure and magnetic properties in Fe?17.2%Mn?4.52%Mo alloy have been investigated by means of electron microscopy and Mössbauer Spectroscopy. Experiments showed that martensitic transformation occurred when the alloy quenched into water from high temperatures and austenite phase transformed ? (hcp) and (bcc) martensite phases. Mössbauer spectra of the alloy reveal a ferromagnetic character with a broad sextet for martensite phase and a paramagnetic character with a singlet for the ? austenite and ? martensite phases. The amounts of thermally ? and martensites change depending on annealing temperature in the alloy. While the ?+? phase has a minimum value, the amount of martensite has a maximum value after annealing at 1200 . The most suitable temperature is 1050 for formation ? martensite. In addition, the deformation on austenite phase significantly affects the type and amount of martensite phases. The amount of martensite increases with increasing of plastic deformation rate.
Benzer Tezler
- Tavas manganez cevherlerinden laboratuvar tipi ark fırınında ferromanganez/ferrosilikomanganez üretim koşullarının belirlenmesi
Başlık çevirisi yok
MEHMET EMİN ARI
- Diğer metallerle karşılaştırmalı olarak piritin (FeS2) korozyon davranışı üzerinde bazı maddelerin etkisi
Investigation of the corrosion behaviour of pyrite by comparison with other metals
ESMA SEZER
- 2-metilnaftalinin metillenmesine metal yüklü zeolit katalizörlerin etkisi
Effect of metal doped zeolite catalyst on methylation of 2-methylnaphthalene
ÜMİT SERDAR EROL
Yüksek Lisans
Türkçe
2016
Kimya MühendisliğiAnkara ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ KARADUMAN
- Fe-%17.3Mn-%4.6Co alaşımında termal etkili martensitik dönüşümler ve martensitik dönüşümlerin manyetik özellikler üzerine etkisinin incelenmesi
Investigation of thermally induced martensitic transformations and effect of martensitic transformations on magnetic properties in Fe-%17.3Mn-%4.6Co alloy
OSMAN ARMAĞAN
Yüksek Lisans
Türkçe
2011
Fizik ve Fizik MühendisliğiKırıkkale ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. TALİP KIRINDI
- Fe-17, 1% Ni-O. 85%C alaşımında faz dönüşümü ve birim hücre şekil değişimi
Başlık çevirisi yok
ERGÜN KASAP