Tam seramiklerde kor altyapıların tekrarlanan preslemelerde kırılganlık, mikrosertlik ve opasite değişimleri
Fracture resistance, mikrohardness and opacity changes of all-ceramik materials after repeated pressings
- Tez No: 354070
- Danışmanlar: PROF. DR. ENDER KAZAZOĞLU
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: tam seramikler, kırılma direnci, mikrosertlik, opasite, tekrarlanan preslemeler, geri dönüşüm, All-Ceramics, fracture resistance, microhardness, opacity, repeated pressing, recycling
- Yıl: 2007
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 91
Özet
Bu çalışmada dişhekimliğinde protetik tedavi amaçlı kullanılan çeşitli tür ve markada tam porselen sistemlerinin, pres sonrasında elde kalan artıklarının tekrar preslenmelerinde, hastanın estetiğini etkileyebilecek opasite değişimleri ile protezin uzun süre kullanımını etkileyebilecek kırılganlık ve mikrosertlik değişimleri incelenmiştir. Böylelikle dişhekimliğinde sıklıkla kullanılan bu materyallerin, tekrar kullanabilirliğini ve bunun sonucunda ortaya çıkan materyaldeki değişimler tespit edilmiştir. Çalışmamızda, Matchpress, Empress 2, Empress estetik ingot ve Finesse marka pres seramik materyallerinin, 1 kere preslenerek hazırlanmış disk şeklindeki örneklerin artıklarının kullanılması suretiyle toplam 1, 2, 3 kez preslenmesi sonrası elde edilen örneklerde kırılganlık, mikrosertlik ve opasitelerindeki değişimler incelenmiştir. Spectrofotometre ile yapılan opasite test sonuçlarına göre Empress2 dışındaki tüm seramik materyallerinde tekrarlanan pres sayısı arttıkça, kendi içindeki opasite değişimleri istatistiksel olarak anlamlı derecede azalmıştır. Instron cihazı ile bakılan biaksiyel bükme dayanıklılığı testine göre; bütün materyaller içinde kırılma direnci en fazla olan materyal lityum disilikat içerikli Empress2 materyali olmuştur. Empress2 materyalinde tekrarlanan pres sayısı arttıkça, kırılma direncinde azalma görülmüştür. Empress Esthetic ve Matchpress materyallerinde tekrarlanan presleme sonucu materyallerin kırılma dirençlerinde anlamlı artışlar görülmüştür. Vickers Sertlik değerlerinde, Empress2 materyali, tekrarlanan fırınlamalar sonrasında sertlik değerlerinde istatistiksel olarak anlamlı artış göstermiştir. Lösit içerikli diğer materyallerde Finesse materyali pres sayısı arttıkça sertlik değerlerinde istatistiksel olarak anlamlı azalma göstermiştir. Empress Esthetic materyali 1. ve 2. presde istatistiksel olarak anlamlı azalma göstermiştir. Matchpress materyali hiçbir presde anlamlı farklılık göstermemiştir. Çalışmamızda elde ettiğimiz sonuçlar ışığında, tam seramik materyallerinin artıklarının tekrar kullanımı olumlu sonuçlar versede, pratikte bu uygulamaların kabul edilebilmesi için bu konuda daha fazla bilimsel araştırma yapılmalıdır.
Özet (Çeviri)
The purpose of this study is to investigate the effects of using the remaining material again and again after pressing the All-Ceramic ingots and determine the changes of the opacity which can affect to the esthetic result and fracture resistance and microhardness which can also affect the success of the restoration. 4 different types of All-Ceramic materials like Matchpress, Finesse, Empress2 and Empress Esthetics were used to produce the specimens for the first group. The remaining ceramic material after the press treatment is used again to produce another group of specimens and again the remaining material is used for the last time to produce one more group of specimens. In this 3 groups; fracture resistence, mikrohardness and opacity values were determined. According to the opacity test results measured by using a spectrophetemeter; All of the All-Ceramic materials except the Empress2 material; there is a significant decrease in the opacity results when more the material is pressed. The less opaque material of all was determined as the Empress Esthetics. According to the biaxial flexure strength test, measured by using an İnstron machine; The highest result was determined as the litium disilicate material Empress2 which decreased significantly after repeated pressings. Empress Esthetics and Matchpress materials had shown significant increases in repeated pressings. In the Vickers hardness values Empress2 material has shown us significant increases after repeated pressing. In the leucite type materials Finesse material had shown significant decrease, Empress Esthetic material decreased significantly at the 2.nd. Matchpress material did not show any significant difference in the hardness value. Even though this research had shown us that the repeated pressed All-ceramic materials can be used in practical work, more researches are needed to examine other effects.
Benzer Tezler
- Tam seramiklerde kor alt yapıların tekrarlanan preslemelrde marjinal aralık değişimleri
Marginal fit changes of all ceramic materials after repeated pressings
MEHMET TOPRAKBASTI
Doktora
Türkçe
2008
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ENDER KAZAZOĞLU
- Çoklu fırınlama uygulamasının farklı zirkonya esaslı alt yapı sistemlerinin mekanik özelliklerine etkisi
Effect of repeated firing on mechanical properties of different zirconia based ceramic core systems
BEHİYE DABAKOĞLU
Doktora
Türkçe
2009
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ENDER KAZAZOĞLU
- Farklı kor seramiklerin ışık geçirgenliğinin incelenmesi
Examination of the light transmission of different ceramic cores
ÖZLEM CEYLAN
Doktora
Türkçe
2007
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF.DR. FİLİZ AYKENT
- Er:YAG lazerin farklı seramiklerden transmisyonu
Transmission of Er:YAG laser through different ceramics
FADİME ZEHRA DOLGUN
Doktora
Türkçe
2016
Diş HekimliğiGaziantep ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. FATİH SARI
PROF. DR. ASUDE DİLEK NALBANT
- Zirkonya kor ve üst yapı seramiklerin makaslama bağlanma dayanımlarının farklı test tasarımlarıyla değerlendirilmesi
Evaluating shear bond strength of zirconia cores and veneering porcelain with different test designs
EMİNE SELİN ERKAN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiÇukurova ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. CEM KURTOĞLU