Östenitik paslanmaz çeliğin kendi kendine ilerleyen yüksek sıcaklık sentezlenmesi yöntemiyle (SHS-kkiyss) Ni-Al-Cr metallerarası bileşiğin kaplanması

Coating of austenitic stainless steel with Ni- Al -Cr intermetallic by self propagating high temperature synthesis (SHS)

  1. Tez No: 355497
  2. Yazar: BURHAN YILMAZ
  3. Danışmanlar: PROF. DR. NURİ ORHAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: SHS, AISI 304, Ni3Al-Cr, kaplama, intermetalik, SHS, AISI 304, Ni3Al-Cr, coating, intermetallic
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Kaynak Eğitimi Bilim Dalı
  13. Sayfa Sayısı: 84

Özet

Bu çalışmada, AISI 304 paslmaz çelik yüzeyine Ni3Al-Cr intermetaliği kaplanmıştır. Kaplama SHS (Self Propagating High Temperature Synthesis) + sinterleme yöntemiyle yapılmıştır. İşlem parametrelerinin arayüzey mikroyapısı üzerindeki etkileri araştırılmıştır. Atomik olarak 3:1 oranında Ni-Al toz karışımına ağırlıkça %8 ve %10 Cr ilave edilerek eksantrik bir mile bağlı 2 ayrı kap içersinde karıştırılmıştır. Karışımın homojen bir dağılım sergilemesi için tozlar 24 saat boyunca 18 devir/dakika hızında karıştırılmıştır. Hazırlanan tozlar 12mm çapındaki kalıba yerleştirilerek 100 ve 200 MPa basınçla soğuk preslenmiştir. Hazırlanan altlık ve kaplama katları aralarına yüzey ıslatmayı sağlamak amacı ile ince nikel tabaka serilerek reaksiyon odacığına yerleştirilmiştir. İşlem 50 N luk yük altında 1000 ve 1100 0C de 45 dakika süreyle sinterlenerek gerçekleştirilmiştir. Numuneler metalografik incelemeler için parlatılıp dağlanmıştır. Üretilen kaplama tabakalarının ve ara yüzeylerin faz analizleri taramalı elektron mikroskobu (SEM-EDS) ve x-ışınları difraksiyon (XRD) analizi kullanılarak yapılmıştır. Analizler irdelenerek değerlendirilip sonuç ve öneriler verilmiştir. Bu çalışmanın birinci bölümünde konuya giriş yapılmıştır. İkinci bölümde temel bilgiler sunuldu. Üçüncü bölümde deneysel çalışmanın yöntemine yer verildi, dördüncü bölümde ise deney sonuçları verildi. Beşinci ve son bölümde çalışma sonunda elde edilen genel sonuç ve öneriler verildi.

Özet (Çeviri)

SUMMARY COATING OF AUSTENITIC STAINLESS STEEL WITH Ni- Al -Cr INTERMETALLIC BY SELF PROPAGATING HIGH TEMPERATURE SYNTHESIS (SHS) In this thesis, Ni3Al-Cr intermetallic was coated on an austenitic stainless steel by Self Propagating High Temperature Synthesis (SHS) method and following sintering and the effects of process parameters on the microstructure of the coating was investigated. Ni and Al powders of 3:1 in atomic ratio were mixed with Cr in 8 and 10 % in weight and mixed by a mixer connected to a eccentric shaft in different containers at 18 rpm for 24 hours for a homogenous mixture. The mixture then cold compacted in the metal dies with a diameter of 1 mm under 100 and 200 MPa. A thin Nickel layer from Ni powder was placed on the stainless steel substrate and this combination (Ni3Al compact Ni layer and austenitic stainless steel rod) was placed in the reaction chamber. The process was realized by applying a fixing load of 50 N and sintering at 1000 and 1100 C for 45 minutes after ignition completed. The specimens were investigated by optical SEM microscopy and the microstructures occurred were determined by EDS and XRD. In the first chapter of the study, the subject is introduced. In the second chapter a literature research was given on the materials and the method (SHS) itself. In the third chapter, the experimental studies, materials and method were presented. In the fourth chapter the results and in the fifth and last chapter conclusion and recommendations are given.

Benzer Tezler

  1. Östenitik paslanmaz çeliğin bor katkılı Ni3Al ile kaplanabilirliğinin araştırılması

    Investigation of boron doped Ni3Al coating of austenitic stainless stell

    MEHMET AKKAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2013

    Metalurji MühendisliğiFırat Üniversitesi

    Metalurji Eğitimi Ana Bilim Dalı

    DOÇ. DR. SERMİN OZAN

  2. Design of a stainless steel composite bridge according to the eurocodes and cost analysis

    Paslanmaz çelik ile kompozit bir köprünün eurocode'a göre tasarımı ve maliyet analizi

    TİJEN BAYER

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. BARLAS ÖZDEN ÇAĞLAYAN

  3. Farklı seramik parçacıkların AISI 304 östenitik paslanmaz çelik üzerine elektrokimyasal yöntem ile kaplanabilirliğinin araştırılması

    Investigation of electrochemical coating of different ceramic particles on AISI 304 austenitic stainless steel

    GİZEM TUGÇE GÜNGÖR

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiFırat Üniversitesi

    Makine Mühendisliği Teknolojileri Ana Bilim Dalı

    DOÇ. DR. FARUK KARACA

    DR. ÖĞR. ÜYESİ SALİH CİHANGİR

  4. Effect of laser surface hardening parameters on impact sliding wear behavior of a hot work tool steel

    Lazer yüzey sertleştirme parametrelerinin sıcak iş takım çeliğinin darbeli kayma aşınma davranışına etkisi

    ELİF NÖBET

    Yüksek Lisans

    İngilizce

    İngilizce

    2019

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ MOHAMMADREZA NOFAR

  5. 316L paslanmaz çeliğin kaynak prosesi sonrası oluşan mekanik davranışların incelenmesi

    Investigation of the mechanical behavior of 316L stainless steel after the welding process

    TAYFUN KARAGÖZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Makine MühendisliğiAlanya Alaaddin Keykubat Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. İSMAİL TOPCU