Katalizör ve ENG katkılı MgH2 peletlerin yapısal özelliklerinin ve hidrojen kinetiğinin araştırılması

Investigation of structural properties and hydrogen kinetics of the catalyst and ENG doped MgH2 pellets

  1. Tez No: 372828
  2. Yazar: GÖKHAN GİZER
  3. Danışmanlar: PROF. DR. ŞADAN ÖZCAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Fizik ve Fizik Mühendisliği, Kimya, Metalurji Mühendisliği, Physics and Physics Engineering, Chemistry, Metallurgical Engineering
  6. Anahtar Kelimeler: Hidrojen depolama, CSP santralleri, termokimyasal enerji depolama, MgH2, metal hidrürler, hydrogen storage, CSP plants, thermochemical energy storage, MgH2, metal hydrides
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Hacettepe Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Nanoteknoloji ve Nanotıp Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 99

Özet

Metal hidrürler arasında MgH2'nin yüksek sıcaklıkta (300-450oC) ve düşük H2 basınçlarında (0-20 bar) çalışması, bol bulunur olması ve özelliklerinin iyi bilinmesi nedeniyle yoğunlaştırılmış güneş enerji santrallerinde ısı depolama malzemesi olarak uygulama potansiyeli oldukça yüksektir. Magnezyumun hidrojen soğurması egzotermik bir reaksiyondur, 75kJ/molH2 ısı açığa çıkar. Açığa çıkan ısı enerjisi kullanılarak santralin çalışması devam ettirebilir. İyi bir ısı depolama malzemesinin yüksek reaksiyon hızına ve ısıl iletkenliğe sahip olması gereklidir. Fakat MgH2'nin reaksiyon hızı yavaş ve ısıl iletkenliği düşüktür. Bu nedenlerle çalışma kapsamında, MgH2'nin reaksiyon hızını iyileştirmek için metal oksit katalizörler ile birlikte mekanik öğütme işlemi kullanılmıştır. Yüksek ısıl iletkenliğe ulaşmak için ise yapıya yüksek ısıl iletkenliğe sahip genişletilmiş grafit (ENG) katılmıştır. Hacimsel depolama kapasitesini artırmak ve oksijene karşı reaktifliği azaltmak için MgH2-katalizör-ENG karışımı hidrolik pres ile basınçlandırılmıştır. Mekanik öğütme işleminin, presleme basıncının, ENG miktarının, katalizör miktarının ve cinsinin malzemenin yapısal özellikleri ve hidrojen kinetiği üzerindeki etkisi de ayrıca incelenmiştir. Oluşturulan peletlerin hidrojen kinetiği Sievert hacimsel metot ile belirlenirken, yapısal karakterizasyonu taramalı elektron mikroskobu ile irdelenmiştir. Isıl iletkenlik ölçümleri ise çalışma kapsamında tasarlanmış olan ölçüm düzeneği ile yapılmıştır. %90 MgH2, %5 TiO2 ve %5 ENG'den oluşan peletin hidrojen depolama kapasitesi 350oC'ta ağırlıkça %5,6'dır. %5 TiO2 katkısıyla peletlerin hidrojen salınım özellikleri 2 kat geliştirilmiş ve 350oC'ta 15 dakikada tüm hidrojeni salabilmektedir. %5 ENG katılmasıyla ise peletin radyal ısıl iletkenliği 5 kat artarak 4,6 W/mK değerine ulaşmıştır. Pelet, fiziksel özelliklerinde bir değişim olmadan 20 döngü boyunca çalışabilmektedir. Presleme basıncı arttığında fiziksel özelliklerin iyileştiği ve 50 döngüye kadar pelet formunun korunduğu görülmüştür. Bu sonuçlar saf MgH2 peletin hidrojen depolama ve ısıl özelliklerinin, katalizör ve ENG kullanımıyla belirgin olarak iyileştirildiğini göstermektedir. Hazırlanan pelet, 300-450oC sıcaklık aralığında ve 0-20 bar H2 basıncında ısı depolama özelliğiyle yüksek sıcaklık ısı depolama malzemesi olarak kullanılma potansiyeline sahiptir.

Özet (Çeviri)

Among metal hydrides, MgH2 operates at high temperatures (300-450oC) and low H2 pressures (0-20 bar). It is an abundant and well-studied material. These properties show that MgH2 can be used as a thermal energy storage material for concentrating solar power plants. H2 absorption of magnesium is exothermic, 75kJ/molH2 heat energy is released. This released energy can be used to carry on power plant's operation. Suitable thermochemical energy storage material should have high thermal conductivity and fast hydrogen kinetics. However reaction kinetics of MgH2 is slow and it has low thermal conductivity. In this work, mechanical milling process and metal oxide catalysts are used to improve reaction kinetics. Expanded natural graphite (ENG) is added to increase thermal conductivity of samples. MgH2-catalyst-ENG mixture is compacted with uniaxial press to reduce oxidation rate and increase volumetric hydrogen capacity. Effect of mechanical milling, pellet pressure, ENG concentration, catalyst type and concentration on material is investigated. Hydrogen kinetics of prepared samples are measured with Seivert's volumetric method. SEM and TEM analysis are done for structural analysis. Thermal conductivity measurement system, designed by SNTG members is used to measure thermal conductivities of pellets. Pellet consist of %90 MgH2, %5 TiO2 and ENG can store 5,6 wt. % hydrogen at 350oC. With %5 TiO2 addition, reaction kinetics are two times faster respect to sample without catalyst. Pellet can fully desorb hydrogen in 15 minutes. With %5 ENG addition, radial thermal conductivity of pellet is reached to 4,6 W/mK. This result is 5 times higher than MgH2 itself. There is not any physical distortion on pellet surfaces up to 20 hydrogen absorption-desorption cycle. Increasing pellet pressure improves the physical properties and pellet pressed under 600 MPa can keep pellet form until 50 cycle. These results show that catalyst and ENG addition clearly improves properties of pure MgH2 pellet. Prepared pellet can operate at 300-450oC temperature range and 0-20 bar H2. It has the potential to be used as a high temperature thermal energy storage material.

Benzer Tezler

  1. Esterification of phthalic anhydride with 2-ethyl hexanol over superacidic and heteropolyacidic catalysts

    Süper asidik ve heteropoliasidik katalizörler üzerinde fitalik anhidrit ile 2-etil hegzanolun esterifikasyonu

    HÜLYA YILDIZ

    Yüksek Lisans

    İngilizce

    İngilizce

    2001

    Kimya MühendisliğiEge Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. GÖNÜL GÜNDÜZ

  2. Isomerization of alpha-pinene over acid treated natural zeolite, clinoptilolite

    Asit ile muamele edilmiş doğal zeolit, klinoptilolit üzerinde alfa-pinen izomerizasyonu

    ERCAN ÜNVEREN

    Yüksek Lisans

    İngilizce

    İngilizce

    2001

    Kimya MühendisliğiEge Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. GÖNÜL GÜNDÜZ

    YRD. DOÇ. DR. FEHİME ÖZKAN

  3. Katalizör ve katalizör desteği olarak kullanılmak üzere Al-sütunlandırılmış kil sentezi ve karakterizasyon çalışmaları

    Synthesis of Al-pillared layered clays as catalyst and catalyst support and characterization studies

    FUNDA TURGUT BAŞOĞLU

    Doktora

    Türkçe

    Türkçe

    2004

    Kimya MühendisliğiGazi Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF.DR. SUNA BALCI

  4. İmal edilen ve ticari PEM tipi yakıt hücrelerinin performanslarının kıyaslanması

    Performance comparison of a manifuctured PEM to a commercial pem fuel cell

    RESÜL KAPLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Makine MühendisliğiDumlupınar Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. NİMETİ DÖNER

  5. Homojen ve heterojen demir katalizör ile aktifleştirilmiş persülfat ile sulu çözeltilerden reactive yellow 37 boyar madde gideriminin incelenmesi

    Investigation of reactive yellow 37 dye removal from aqueous solutions by persulfate activated with homogeneous and heterogeneous iron catalyst

    SÜMEYRA KAYA

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Çevre MühendisliğiFırat Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ MÜSLÜN SARA TUNÇ