Karbon siyahı çeşidi ve miktarının, doğal kauçuk/butadıen kauçuk karışımının reolojik, mekanik ve termomekanik özellikleri üzerine etkisi
The effect of carbon black on the rheological, mechanical and termomechanical properties of natural and butadiene rubber blends
- Tez No: 374105
- Danışmanlar: DOÇ. DR. ENGİN BURGAZ
- Tez Türü: Yüksek Lisans
- Konular: Mühendislik Bilimleri, Polimer Bilim ve Teknolojisi, Engineering Sciences, Polymer Science and Technology
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Ondokuz Mayıs Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 89
Özet
Bu çalışmada, farklı partikül büyüklüklerine ve yapılara sahip karbon siyahları ile güçlendirilmiş doğal kauçuk-butadiyen kauçuk karışımı kompozit malzemelerin reolojik, mekanik ve termomekanik özellikleri incelenmiştir. Kauçuk proses analiz cihazı kullanılarak doğal kauçuk-butadiyen kauçuk/karbon siyahı bileşenlerinden oluşan karışımların vulkanizasyon karakteristikleri belirlenmiştir. Tüm çalışma boyunca hızlandırıcılar ve kükürt gibi vulkanizasyon kimyasalları sabit tutulmuştur. NR/BR karışımlarına yüksek yapılı karbon siyahları ve geleneksel karbon siyahları çeşitleri eklenerek (45 - 90 phr aralığında) aşınma direncini artırmak ve tandelta, gerilim gevşemesi değerlerini düşürmek amacıyla güçlendirici etkisi çalışılmıştır. Kayıp faktörü (tandelta) DMA (dinamik mekanik analiz) testlerinin yanısıra, RPA (Rubber Process Analyser - Kauçuk Proses Analizi) cihazı ile, 3 Hz frekans, %1 açısal gerinim ve 50 °C sıcaklıkta ölçülmüş; sonuçlar DMA datası ile birbirini sağlamaktadır. Gerilim gevşemesi testleri 0.2 değerinde sabit gerinim altında basma plakaları ile gerçekleştirilmiştir. Sonuçlar değerlendirildiği zaman, NR/BR-karbon siyahı kompozitlerinde kullanılan karbon siyahının partikül büyüklüğü azaldıkça (yüzey alanı arttıkça) kauçuk malzemenin aşınma direncinin, modülüs değerinin ve gerilim gevşemesine olan direncinin arttığı görülmektedir. Kauçuk malzemenin sertlik ve yoğunluk değeri karbon siyahi miktarı arttıkça artmaktadır. Kullanılan karbon siyahının partikül büyüklüğünün küçüldükçe tandelta değerinin arttığı bilinmektedir. Bu çalışmada NR/BR-karbon siyahı kompozit malzemelerinde istenen mekanik özelliklere ve aynı zamanda düşük tandelta değerine ulaşılması için deneysel parametreler optimize edilmeye çalışılmıştır.
Özet (Çeviri)
In this study, a number of natural rubber(NR)-butadiene rubber(BR) composite materials reinforced with carbon black particles (with different size and structure) were manufactured to determine the rheological, mechanical and thermomechanical properties. The rubber process analyzer (RPA) test was used to identify the curing characteristics of NR-BR/carbon black composites. The vulcanization chemicals (accelerators and sulfur) were kept constant during the study. Different types of highly structured and conventional carbon black particles (in the range of 45-90 phr) were incorporated into the NR-BR matrix as reinforcements in order to decrease the loss factor (tan δ) and stress-relaxation, and increase the abrasion resistance. The loss factor was also determined by using the RPA instrument at 50 ºC, 3 Hz frequency, %1 angle strain, and the results are in good agreement with the DMA data. The stress-relaxation tests were carried out by using the compression plates at a constant strain of 0.2. The results showed that the wear strength, storage modulus, tensile strength and resistance to stress-relaxation of NR-BR/carbon black composite materials increase with the decrease of carbon black particle size. The hardness, and density increases as the weight percent of carbon black increases in NR-BR/carbon black composite materials. It is known that tan δ increases with the decrease of particle size. In this work, desired mechanical properties and low tan δ values were tried to reach at the same time by optimizing the experimental parameters of NR-BR/carbon black composites.
Benzer Tezler
- Investigation of effect of bitumen chemical composition, polymer and warm mix asphalt additives on the properties of bitumen by using response surface method
Bitüm kimyasal içeriği, polimer ve ılık karışım asfalt katkılarının bitüm özellikleri üzerine etkisinin tepki yüzeyi yöntemiyle incelenmesi
EMEL BAŞKENT
Yüksek Lisans
İngilizce
2016
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. MUSTAFA HULUSİ ÖZKUL
- Bursa siyahı incir çeşidinin meristem kültürü yöntemiyle çoğaltılması
In vitro propagation of ficus carica l. var. bursa Siyahı through meristem culture
AYŞE DEMİRALAY
Yüksek Lisans
Türkçe
1997
ZiraatÇukurova ÜniversitesiBahçe Bitkileri Ana Bilim Dalı
DOÇ. DR. SELİM ÇETİNER
- Enerji depolanmasında elektrot malzemesi olarak kullanılabilen nanoyapılı karbon malzemelerin biyokütle atıklarından üretimi
Production of nanostructured carbon materials from biomass wastes that can be used as anode materials for energy storage
BURAK ERDEMİR
- Gemlik çeşidi siyah sofralık zeytinlerin doğal fermantasyonlarında yer alan mayaların ve teknolojik özelliklerinin incelenmesi
Investigation of yeasts and their technological properties in natural fermentations of gemlik cultivar black table olives
GAMZE NUR MÜJDECİ
Yüksek Lisans
Türkçe
2012
Gıda MühendisliğiHacettepe ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
PROF. DR. ZEKİYE YEŞİM ÖZBAŞ
- Görünmez parmakizlerinin görünür hale getirilmesinde kullanılan normal toz , normal fluoresant toz ve manyetik fluoresant tozun etkinliklerinin karşılaştırılması
The comparison of the efficiency of regular, magnetic, regular fluorescent and magnetic flurescent powders used for the visualisation of lagent fingerprints
BAYCAN GÖRÜCÜ
Yüksek Lisans
Türkçe
2003
Adli TıpAnkara ÜniversitesiDisiplinlerarası Adli Tıp Ana Bilim Dalı
YRD. DOÇ. DR. CEMAL ATAKAN