Basınçlı dökümde kalıp hasarına etki eden parametrelerin araştırılması

Invesigation of parameters affecting die damage in high pressure die casting

PDF İndir

  1. Tez No: 374509
  2. Yazar: İBRAHİM FIRAT BALKAYA
  3. Danışmanlar: PROF. DR. FERHAT GÜL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 138

Özet

Bu çalışmada, alüminyum basınçlı dökümünde kalıp hasar mekanizmaları ve buna etki eden unsurlar araştırılmıştır. Deneysel çalışmada, basınçlı döküm kalıp davranışının simüle etmek amacıyla AlTiN, CrN ve CrN-AlTiN gibi PVD yöntemiyle kaplanmış H13 çeliği numuneler, nitrürlenmiş H13 ve Ç1020 çeliği kullanılmıştır. Kaplamasız ve AlTiN, CrN ve CrN-AlTiN kaplamalı numuneler birbirleri ile kıyaslanmıştır. Deneysel çalışma başlamadan önce döküm şartlarını simüle etmek adına bir deneysel düzenek yapılmıştır. 5 mm çap ve 100 mm boya sahip özdeş numuneler farklı sıcaklık ve sayılarda önce ergiyik metale, akabinde 100°C'lik sıcak suya olmak üzere döngüsel olarak daldırılmış ve numune yüzeyindeki hasar incelenmiştir. Bu incelemeler önce kaba olarak gözle, daha sonra stereo mikroskopta yapılmıştır. Son olarak, hassas kesim makinesiyle kesilen numuneler parlatılarak stereo mikroskop altında mikroyapı kıyaslaması yapılmıştır. Kaplamalı numuneler için ileri inceleme taramalı elektron mikroskobu altında yapılmıştır. Kaplamasız Ç1020 numunelerin yüzey dayanım ömrünün oldukça kısa olduğu, PVD yöntemiyle kaplanmayan tüm H13 numunelerinde nispeten uzun ömürlü olmalarına rağmen, yetersiz oldukları görülmüştür. PVD kaplanmış H13 numunelerin başarılı yüzey dayanımı sergiledikleri gözlenmiş, yüzey pürüzlülüğü nispeten fazla olan AlTiN-CrN (multilayer) kaplamanın en başarılı kaplama olduğu görülmüştür.

Özet (Çeviri)

In this study, damage mechanisms and affecting factors in dies used for aluminium die casting were investigated. In the experimental study, coated H13 steel samples like AlTiN, CrN, and CrN-AlTiN by PVD were used for extending the lifetime of samples to simulate of behavior of presure casting die. coated with AlTiN, CrN, and CrN-AlTiN, nitrided H13 and AISI 1020 steel were used. The samples uncoated and coated with AlTiN, CrN, and CrN-AlTiN were compared with each other. Before starting experimental study, experimental set-up is designed to simulate casting conditions. Identical samples which have 5 mm diameters and 100 mm lengths are cyclically dipped into the melted alloy and then into 100oC degree hot water. And damage on sample surface is examined. These examinations were made first roughly in macro scale and followed by a stereo microscope. Finally, samples which are divided into sections by fine cutting machine were polished and comparison of microstructure was done under optical microscope. Further examination for coated samples were made under SEM (Scanning Electron Microscope). The results showed that non-coated AISI 1020 sample's lifetime of surface resistance was rather short and the H13 sample that was non-coated was relatively long-lived but they didn't showed sufficient lifetime. It was also observed that H13 samples coated by PVD shows successful surface resistance and that AlTiN-CrN (multilayer) coating is the most successful coating.

Benzer Tezler

  1. Tez No

    700185

    Yüksek basınçlı dökümde kullanılan kalıp ayırıcı yağın kalıp sıcaklığına ve parça kalitesine etkisi

    The effect of mold release oil used in high pressure casting on die temperature and parts quality

    NACİ EKMEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Makine MühendisliğiSakarya Uygulamalı Bilimler Üniversitesi

    İmalat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. EKREM ALTUNCU

  2. Tez No

    200863

    Basınçlı dökümde kaliteyi etkileyen faktörlerin araştırılması

    Factors affecting the quality of die casting

    OSMAN BARBAROS ASLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Makine MühendisliğiYıldız Teknik Üniversitesi

    Makine Ana Bilim Dalı

    PROF.DR. HÜSEYİN SÖNMEZ

  3. Tez No

    599514

    Investigation of cooling design systems in low pressure casting

    Alçak basınçlı dökümde soğutma tasarım sistemlerinin araştırılması

    EREN BOZKURT

    Yüksek Lisans

    İngilizce

    İngilizce

    2019

    Mühendislik BilimleriDokuz Eylül Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. HÜSEYİN ŞALVARLI

  4. Tez No

    434067

    Al-Si yüksek basınç döküm alaşımlarında Fe intermetaliklerinin kalıp ömrüne etkisi

    Effect of Fe intermetallics on die life of Al-Si high pressure die casting alloys

    İBRAHİM HALİL KALKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Metalurji Mühendisliğiİstanbul Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. DERYA DIŞPINAR

  5. Tez No

    510985

    Enjeksiyon döküm kalıplarına uygulanan farklı kaplamaların kalıp ömrüne etkisi

    Effect of different coatings applied to injection casting molds on mold life

    AHMET TURAN KARAOĞLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

Geri Dön