Geri Dön

Polistiren/magnezyum hidroksit nanokompozit sentezi ve karakterizasyonu

Synthesis and characterization of polystyrene/magnesium hydroxide nanocomposites

  1. Tez No: 376134
  2. Yazar: HUSSEN ADEB ABAS OUJİ
  3. Danışmanlar: DOÇ. DR. AYLA ALTINTEN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2013
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 154

Özet

Polimerik nanokompozitler akademik ve endüstriyel olarak oldukça ilgi çekmektedir. Darbe direnci, modüler, aleve karşı direnci, ısıl kararlılık ve mekanik özellikleri saf polimerlerle karşılaştırıldığımızda önemli derecede gelişim sergilemektedirler. Bu çalışmada takviye malzemesi olarak kullanılan inorganik magnezyum hidroksit (Mg(OH)2) nanopartiküllerinin, matris olarak kullanılan organik polistiren (PS) içerisinde dağılımını sağlayarak mükemmel özelliklere sahip yeni bir malzemenin iki ayrı yöntemle ve üç farklı işletim koşulu kullanarak sentezlenmesi, bu iki yöntemin kıyaslanması, PS?nin özellikle termal ve alev direnci özelliklerinin geliştirilmesi daha sonra sentezlenen PS/Mg(OH)2 nanokompozitinin karakterizasyonunun yapılması hedeflenmiştir. Deney aşaması, ön hazırlık ve kompozit sentezi olarak planlanmıştır. Ön hazırlıkta başlatıcı olarak kullanılan benzoil peroksit (BPO), içerisindeki safsızlıkların ve nemin uzaklaştırılması için kristallendirme işlemine tabi tutulmuştur, Mg(OH)2 nanopartiküllerinin hidrofilik bir yapıya sahip olmasından dolayı polimer içinde dağılması zordur bu yüzden lipofilik bir hal alması için oleik asit (OA) ile modifiye edilmiştir. Kompozit sentezi işlemi; toluen ortamında, stiren monomeri ve değişik oranlarda Mg(OH)2 kullanarak eş zamanlı (in-situ) üretim yöntemiyle PS/Mg(OH)2 nanokompozit sentezi ve stirenden çözelti polimerizasyonu ile elde edilen PS ve değişik oranlarda Mg(OH)2?ten eriyikle harmanlama yöntemiyle PS/Mg(OH)2 nanokompozit sentezi olmak üzere iki yöntemle gerçekleştirilmiştir. PS?nin radikalik katılma polimerizasyonuyla üretiminin ekzotermik karakterde olması nedeniyle reaktör iç sıcaklık artışı kendinden ayarlamalı PID kontrol yöntemi ile engellenmiş ve deneyler sabit sıcaklıkta gerçekleştirilmiştir. Son olarak her iki yöntemle de hazırlanan kompozit malzemelerin; yapısal özellikleri geçirimli elektron mikroskobu (TEM), termal özellikleri termogravimetrik analiz (TGA), yanmazlık özelliklerin analizi için sınırlayıcı oksijen indisi (LOI) ve mekanik özelliklerin incelenmesinde Shore D sertlik ölçüm yöntemiyle karakterize edilmiştir. Ayrıca elde edilen PS?nin %monomer dönüşümü ve viskozite ortalama molekül ağırlık değerleri hesaplanmıştır. PS/ Mg(OH)2 nanokompoziti eriyikle harmanlama ve eş zamanlı üretim yöntemleriyle başarılı bir şekilde sentezlenmiştir. FTIR sonuçlarından Mg(OH)2 modifiye işleminden sonra, oleik asitin kimyasal olarak Mg(OH)2 yüzeyine bağlandığı görülmüştür. TEM görüntülerine bakıldığında Mg(OH)2 nanopartikülleri her iki yöntem de PS içersinde homojen bir dağılım sergilemiştir. TGA sonuçlarına bakıldığında eklenen Mg(OH)2 nanopartiküllerin miktarının artmasıyla bozunmaya başlama ve bitiş sıcaklıkları artmaktadır, dolaysıyla Mg(OH)2 nanopartikülleri PS?nin ısıl kararlığını olumlu bir şekilde etkilemektedir. LOI değerlerine bakıldığında Mg(OH)2 nanopartikülleri PS?nin yanmazlık özeliklerini geliştirmiş ve aleve karşı daha dayanıklı bir hal almıştır.

Özet (Çeviri)

A considerable attention has been focused on the Polymer matrix nanocomposites both academically and industrially. Impact resistance, modular, flame resistance, thermal stability and mechanical properties exhibit improvements when compared to the pure polymer. In this study magnesium hydroxide (Mg(OH)2) nanoparticles that used as inorganic material has been well distributed on organic polystyrene (PS) that used as matrix of the nanocomposite and the results were a new material having excellent properties. The distribution process has been provided by two different methods and using three different operating conditions of synthesis. Comparing between these two different methods and conditions, the PS properties especially flame resistance development and PS/Mg(OH)2 nanocomposites material characterization has been targeted in this study. The experiment contains the pre-preparation and synthesis levels as planned, in the pre-preparation level Benzoil Peroxide (BPO) used as a precursor, to remove the impurities and moisture the crystallization process has applied on the precursor. The hydrophilic property of the Mg(OH)2 construction makes it hard to distribute within polymer material, therefore it was modified to the lipophilic construction by using Oleic Acid (OA). Composite synthesis carried out by two process, first in toluene environment, styrene monomer and using various ratio of Mg(OH)2 obtaining PS/Mg(OH)2 nanocomposite material by using in-stiu method, and the second process was using PS that acquired from styrene solution polymerization process and various ratio of Mg(OH)2 to synthesis PS/Mg(OH)2 nanocompsite by using melt intercalation method. Due to the exothermic character of radical participation polymerization production of PS, self tuning PID temperature control method was used to keep the increase of temperature, however, the experiments has carried out at constant temperature. The composite materials prepared by both methods, was analyzed by the structural characteristics of transmission electron microscopy (TEM), thermal properties thermo gravimetric analysis (TGA), the flame retardancy (LOI) and mechanical characterization properties using Shore D hardness method. Also on the obtained PS, average viscosity and molecular weight values according to % monomer conversion has calculated. PS/Mg(OH)2 nanocomposites synthesis by using both melt intercalation and in-situ method was successfully completed. According to results that given by FTIR after the modification process that applied on Mg(OH)2 its appear that oleic acid has been chemically binding on the surface of the Mg(OH)2. TEM images shows that Mg(OH)2 nano particles in two methods distributed homogenously within PS. TGA results shows the increases of the Mg(OH)2 nano particles increases the temperature of the degradation start and end , therefore the Mg(OH)2 has a positive effect on the thermal stability of the PS. LOI values shows the nano particles of Mg(OH)2 has affected the positively to the flame resistance properties of the PS.

Benzer Tezler

  1. Alev geciktirici nanokompozit kaplamaların sentezi ve karakterizasyonu

    Synthesis and characterization of fire-retardant nanocomposite coatings

    HAVVA KAHRAMAN

    Doktora

    Türkçe

    Türkçe

    2014

    Kimya MühendisliğiSelçuk Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. EROL PEHLİVAN

  2. Yeni bir şelat yapıcıyla borun sıvı-sıvı ekstraksiyonu

    A Novel chelating agent for liquid-liquid extraction of boron

    MUSTAFA GAZİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2000

    Kimyaİstanbul Teknik Üniversitesi

    PROF.DR. NİYAZİ BIÇAK

  3. New functional polyols for polyurethanes

    Poliüretanlar için yeni fonksiyonel polioller

    BAŞAR YILDIZ

    Doktora

    İngilizce

    İngilizce

    2016

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. AHMET AKAR

  4. Halojensiz alev geciktirici içeren AYPE/PLA karışımların alev dayanımı özelliklerinin incelenmesi

    Flame resistant properties of LDPE/PLA blends containing halogen-free flame retardant

    FİGEN ARSLAN

    Doktora

    Türkçe

    Türkçe

    2019

    Kimya MühendisliğiGazi Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. NURSEL DİLSİZ

  5. Alev geciktirici polimer kompozitlerin ekstrüzyon yöntemi ile hazırlanması ve karakterizasyonu

    Preparation and characterization of flame retardant polymer composites through extrusion method

    AYKUT YÜCESOY

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Mühendislik BilimleriYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. HALE BERBER YAMAK