Farklı derişimlerdeki sodyum hidroksid (NaOh) çözeltileri ile ön işlem görmüş Kızılçam (Pinus brutia Ten.) odunu yongalarından üretilmiş levhaların bazı kimyasal, fiziksel ve mekanik özellikleri

Some chemical, physical and mechanic properties of boards manufactured from brutian pine (Pinus brutia Ten.) parti̇cles pre–treated with different concentrations of sodium hydroxide (NaOh) solutions

  1. Tez No: 391992
  2. Yazar: BEYHAN KARAKUŞ YET
  3. Danışmanlar: DOÇ. DR. SAMİM YAŞAR
  4. Tez Türü: Doktora
  5. Konular: Ormancılık ve Orman Mühendisliği, Forestry and Forest Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Süleyman Demirel Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Orman Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 124

Özet

Bu çalışmada kızılçam (Pinus brutia Ten.) odunundan elde edilmiş yongalara levha üretiminden önce % 1, 2, 3, 4 ve 5'lik NaOH çözeltileri ile ön işlem uygulanmıştır. Ön işlem uygulanan yongaların ekstraktif madde, lignin ve holoselüloz miktarları belirlenmiştir. Yongalara uygulanan FTIR analizlerinden sonra spektrumlarda ön işlemlerle yongalarda OH grubu miktarında artış olduğu görülmüştür. Bundan dolayıdır ki ekstraktif madde, lignin ve holoselüloz miktarları belirlenmiştir. TGA analizlerinden sonra elde edilen eğriler yongalarda ısıtma soğutma ve aynı izotermal koşullarda bırakılmayla meydana gelen madde kaybı saptanmıştır. TGA sonuçları göstermiştir ki modifiye edilmemiş kontrol yongaları, ön işlem görmüş yongalara oranla daha yüksek termal kararlılığa sahiptir. Yongalevhaların üretiminden sonra fiziksel ve mekanik özellikleri araştırılmıştır. Su alma (SA), kalınlığına şişme (KŞ), eğilmede elastikiyet modülü (EM), eğilme direnci (ED), yüzeye dik çekme direnci (YDÇD) incelenmiştir. Elde edilen bulgulara göre, uygulanan ön işlemlerin özellikle levhaların SA ve KŞ değerleri üzerine etkili olduğu görülmüştür. Bu değerler kontrol levhalarından itibaren % 5'lik NaOH uygulanmış levhalara kadar sürekli olarak bir düşüş göstermiştir. EM ve ED değerlerine bakıldığında, ise % 1, 2 ve 3 NaOH uygulaması ile elde edilen levhalarda diğerlerine oranla daha yüksek olduğu görülmüştür. Holoselüloz değerleri kontrol yongalarından itibaren % 5 NaOH uygulaması ile elde edilen levhalara kadar sürekli bir artış gösterirken, ekstraktif madde ve lignin miktarları ise tam tersi bir şekilde sürekli bir düşüşe sahip olduğu görülmüştür. Çalışmamız sonucunda, kullanılacak yongalevhalarda eğilme direnci ve eğilmede elastikiyet modülünün yüksek değerlere sahip olması arzulandığında yongalara % 1 NaOH ön işleminin uygulanabileceği saptanmıştır.

Özet (Çeviri)

In this study, the chips produced from brutian pine wood (Pinus brutia Ten.) were subjected to chemical pretreatment such as 1, 2, 3, 4 and 5 % NaOH treatment FTIR spectra of chips indicated that, the content of –OH grups was increased by pretreatment. Therefore, chemical component contents (extractives, holocellulose and lignin) of chips were determined. TGA curves were used to determine the weight loss of the chips as. They were hated, cooked or held isothermally. The results of TGA suggest that the unmodified control chips were more stable than pretreated chips. After producing particleboards, physical and mechanical properties namely; water absorption (WA), thickness swelling (TS), modulus of elasticity (MOE), modulus of rupture (MOR) and internal bond strength (IBS) were studied. The results also indicated that pretreatments have significant effects on WA and TS values of the boards. The values decreased continually from control board to board produced using 5 % NaOH pretreated chips. MOE and MOR values of the boards produced from 1, 2 and 3 % NaOH pretreated chips were better than others. Holocellulose content increased continually from control chips to 5 % NaOH pretreated chips, whereas the extractive and lignin contents continually decreased. This study showed that more MOE and MOR values of the boards can be obtained using pretreatment with 1 % NaOH.

Benzer Tezler

  1. Ni(II) iyonlarının poli(2,5-dihidro-2,5-dimetoksifuran) üzerine adsorpsiyonu

    Adsorption of Ni(II) ions on to poly(2,5-dihydro-2,5-dimethoxyfuran)

    NURDAN ATALAY

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    KimyaKırıkkale Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ZEKİ ÖKTEM

  2. Yasadışı olarak kullanılan esrar (kannabinoidler)'ın idrarda tayininde farklı ekstraksiyon yöntemlerinin geliştirilmesi

    Development of different extraction methods for the determination of cannabis which is used as an illegal substance in urine

    SELİN DEMİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Adli TıpEge Üniversitesi

    Bağımlılık Toksikolojisi Ana Bilim Dalı

    PROF. DR. SERAP ANNETTE AKGÜR

  3. Alüminyum hidroksit kristalizasyonu üzerine lityum safsızlığının etkisi

    Effect of lithium impurity upon aluminum hydroxide crystallization

    HALİL İBRAHİM TEMİZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Kimya MühendisliğiKonya Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ. DR. AYHAN ABDULLAH CEYHAN

  4. Akrilonitril/vinil asetat kopolimerinin kimyasal modifikasyonu ve metal iyonu adsorpsiyonunda kullanılması

    Chemical modification of acrylonitrile/vinyl acetate copolymer and its use in metal adsorption

    ALİ EREN ATICI

    Yüksek Lisans

    Türkçe

    Türkçe

    2013

    KimyaHacettepe Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. OLGUN GÜVEN

  5. Hastane atıksularının elektrokimyasal arıtım yöntemleri ile giderilmesi

    Removal of hospital wastewater using electrochemical treatment methods

    ÖZGÜR NAZİKCAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Çevre MühendisliğiAnadolu Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    PROF. DR. ALİ SAVAŞ KOPARAL