Bazı polimerler, şeker pancarı küspesi ve karışımlarının termal parçalanma kinetiklerinin termogravimetrik analiz cihazı kullanılarak incelenmesi

Investigation of thermal degradation kinetics of some polymers, sugar-beet pulp and their blends by thermogravimetric analyzer

PDF İndir

  1. Tez No: 392743
  2. Yazar: MEMİ SERDAR SURAT
  3. Danışmanlar: PROF. DR. BEDRİYE TÜLAY DURUSOY
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2015
  8. Dil: Türkçe
  9. Üniversite: Hacettepe Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 160

Özet

Polistiren, polietilen glikol, polivinil klorür ve polietilen ile laboratuvar ortamında üretilen etilen glikol dimetakrilat / metil metakrilat (EGDMA/MMA) kopolimeri örnekleri, şeker pancarı küspesi ve polimer-küspe karışımlarının azot ve hava varlığında termal parçalanma deneyleri, SEIKO INSTRUMENTS EXSTAR6000 TG/DTA termal analiz cihazı kullanılarak gerçekleştirilmiştir. Elde edilen veriler yardımıyla, en yüksek ağırlık kaybı hızları, en yüksek ağırlık kaybı hızına karşılık gelen sıcaklık değerleri bulunmuş ve toplam dönüşüm yüzdeleri hesaplanmıştır. Polimer ile küspe karışımlarının, gerek hava ve gerekse azot varlığında termal parçalanması sonucunda elde edilen termal parametrelerin değerlerinin saf polimerden elde edilenlere göre daha düşük olduğu saptanmıştır. En yüksek toplam dönüşüm hava varlığında termal parçalanmada PVC için %97.7 olarak elde edilmiştir. Coats & Redfern kinetik modeli ile deney verilerinden yararlanılarak kinetik parametreler hesaplanmıştır. Küspenin aktivasyon enerjisinin polimerlere göre daha düşük olduğu görülmüştür. Polimerlere küspe karıştırıldığında, karışıma ait kinetik parametre değerlerinin, küspe ve saf polimerlerin değerlerinin arasında yer aldığı tespit edilmiştir. Hem azot hem de hava varlığında termal parçalanmada en düşük aktivasyon enerjisine sahip olan polimerin 101 kJ/mol ve 98 kJ/mol değerleri ile Polietilen olduğu tespit edilmiştir. Reaksiyon derecesinin polimerler için genel olarak 2, küspe için ise farklı tanecik boyutuna sahip olsalar bile 3/2 değeri ile daha iyi uyum sağladığı saptanmıştır. Laboratuvar ortamında üretilen EGDMA/MMA kopolimeri örneklerinin termal özelliklerinde meydana gelen değişikliklerin karşılaştırılması amacıyla, üretim aşamasında karıştırma hızı, başlatıcı miktarı ve monomer oranında değişime yapılmış, farklı varyasyonlarla sentez gerçekleştirilmiştir. Tüm örnekler içi en yüksek ağırlık kaybı hızları, en yüksek ağırlık kaybı hızına karşılık gelen sıcaklık değerleri, toplam dönüşüm yüzdeleri, ve aktivasyon enerjisi değerlerinin değişimleri azot ve hava varlığında termal parçalanma için ayrı ayrı olmak üzere incelenmiştir.

Özet (Çeviri)

Ethylene glycol dimethachrylate / methyl methacrylate (EGDMA/MMA) copolymer samples, and sugar beet pulp and the concoct of polymer-pulp within the medium of Nitrogen and atmospheric existence the experimental studies based on thermal destruction SEIKO INSTRUMENTS EXSTAR6000 TG/DTA alongside with Polystyrene, polyethylene glycol, polyvinyl chloride side by side polyethylene there of the thermal analyses instrument produced in the laboratory itself adding to them have been realized. Abovementioned laboratory conditions through the findings linked to the highest speed, in weight losing, have been evaluated and the counterpoints regarding to the changing temperature values were taken into account after having been found. Considering the concoct of Polymer and pulp it has been shown that the thermal destruction under the conditions co-existence wherefrom atmospheric paradigm and nitrogen the outshot of the values of the parameters pointed the results showing the declining values having been declined much more less in numerical findings than those produced thereof belonging to the pure pulp cases. The highest from the point of total turning out was gained 97.7 percent within the presence of atmosphere of the laboratory for PVC. Pursuing the model of the kinetic by Coats & Redfern and sustained over the results of the experiments the kinetic parameters were counted. The energy of activation of pulp proved its lesser degrees compared with/to that of polymers. After mixing the polymer wit pulp the aforesaid results based on those attained as briefed above it has been proved that the results regarding to the procedure were to take place between the findings linked to both mere pulp and the polymer purified. Both under the condition of atmosphere and nitrogen the least activation energy in thermal destruction it was seen that the 101 kJ/mol and 98kJ/mol was of Polyethylene. Regarding reaction rate the polymers proved the degree of, generally, 2, and for 3/2 even if they have various dimensions with the accommodation ability to the changeable conditions. EGDMA/MMA produced in the proper conditions of laboratory the samples of co-polymer alongside with the changing within thermal peculiarities in order to mix with each other, and in the phase of production the speed of mixture attainment plus debut of velocity and quantity would be changed adding to it the changing proper were scrutinized regarding to the proportions of the monomer. For all the samples handled hereby the gravest weight loss and the counter point values of thermal inducing the other, and the percentage of total changing rates, and considered activation energy were scrutinized alternatively depending on the presence of of nitrogen and atmosphere properly.

Benzer Tezler

  1. Tez No

    620858

    Türkiye'de şeker pancarı üretim alanlarında enfeksiyon oluşturan beet necrotic yellow vein virus (BNYVV) izolatlarının p31 proteininin moleküler karakterizasyonu

    Molecular characterization of p31 protein of beet necroticyellow vein virus (BNYVV) isolates in sugar beet production areas of Turkey

    MURAT GÜNGÖR

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    ZiraatOndokuz Mayıs Üniversitesi

    Bitki Koruma Ana Bilim Dalı

    PROF. DR. NAZLI DİDE KUTLUK YILMAZ

  2. Tez No

    356093

    Şeker pancarı atığından geri kazanılan selülozun biyokompozit olarak değerlendirilmesi

    Evaluation of cellulose recovered from sugar beet bagasse as biocomposite

    EMİNE EVKAYA

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. OYA ATICI

  3. Tez No

    439561

    Isolation and characterization of genomic and cDNA sequences encoding the laccase CpLcc2 from Coriolopsis polyzona MUCL 38443

    Coriolopsis polyzona MUCL 38443 suşundaki CpLcc2 lakkazını kodlayan genomik ve cDNA dizilerinin izolasyonu ve karakterizasyonu

    DİCLE MALAYMAR

    Yüksek Lisans

    İngilizce

    İngilizce

    2016

    Biyoteknolojiİstanbul Teknik Üniversitesi

    Moleküler Biyoloji-Genetik ve Biyoteknoloji Ana Bilim Dalı

    PROF. DR. AYTEN KARATAŞ

  4. Tez No

    647532

    Bazı gıdalardaki mikroplastik kirliliğinin tespiti

    Determination of microplastic in some foods

    SEMA ZÜLAL BALCI

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    Çevre MühendisliğiSakarya Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MERAL YURTSEVER

  5. Tez No

    414357

    Nanokompozit ambalaj filmi üretimi ve bazı gıdaların ambalajlanmasında kullanım olanaklarının araştırılması

    Nanocomposite film production and investigation of its possible usage on some foods packaging

    SÜLEYMAN POLAT

    Doktora

    Türkçe

    Türkçe

    2016

    Gıda MühendisliğiÇukurova Üniversitesi

    Gıda Mühendisliği Ana Bilim Dalı

    PROF. DR. HASAN FENERCİOĞLU

Geri Dön