Üç farklı adeziv sistemiyle uygulanan kompozit rezinlerin farklı uygulama basamaklarında meydana gelen tükürük kontaminasyonu etkisinin mikro-makaslama kuvvetleri açısından incelenmesi
Evaluation of influence of salivary contamination during different stages on microshear bond strength of composite resin applied with three different adhesive systems
- Tez No: 400007
- Danışmanlar: PROF. DR. HİKMET SOLAK
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Tükürük kontaminasyonu, mikro-makaslama testi, dentin adeziv sistemler, kompozit rezin, Saliva contamination, microshear bond strength, dentin adhesive systems, composite resin
- Yıl: 2012
- Dil: Türkçe
- Üniversite: Yakın Doğu Üniversitesi
- Enstitü: Yurtdışı Enstitü
- Ana Bilim Dalı: Restoratif Diş Tedavisi ve Endodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı, 3 farklı adeziv sistemin farklı uygulama basamaklarında oluşan tükürük kontaminasyonunun, adeziv sistemlerin dentine bağlanma dayanımları üzerine etkisini incelemektir. Çalışmamızda, 2 basamaklı total-etch adeziv sistem 2 basamaklı self-etch adeziv sistem ve tek basamaklı self-etch adeziv sistem örnekleri test edilmiştir. Yirmi dört adet çürüksüz molar dişin kullanıldığı çalışmamızda, mikro kesit alma cihazıyla her bir dişten 2 adet olmak üzere toplam 48 adet 1 mm'lik horizontal dentin kesidi elde edilmiş ve bu kesitler, test edilen adeziv sistemin tipine göre rastgele 3 gruba ayrılmıştır. Daha sonra her adeziv sistem için biri kontrol grubu olmak üzere tükürük kontaminasyonunun olduğu aşamaya göre adeziv öncesi, adeziv sonrası ve polimerizasyon sonrası 4 alt grup oluşturulmuştur. Kontaminasyon için tek bir bireyden elde edilen doğal tükürük kullanılmıştır. Bütün gruplarda, mikro-makaslama bağlanma dayanım testi için dentin diskler üzerine kompozit rezin yerleştirilirken 0,7 mm çapında ve 1 mm yüksekliğinde şeffaf plastik tüpler kullanılmış, her dentin diski üzerine 3 adet kompozit rezin silindir yerleştirilmiştir. Böylece her grup için 12 adet kompozit rezin örnek elde edilmiştir. Bu örnekler 1 gün boyunca 370C distile suda bekletildikten sonra, üniversal test cihazına yerleştirilmiş ve 1mm/dk'lık hızla makaslama kuvveti uygulanmıştır. Veriler tek yön varyans analizi (ANOVA) testi ve Tukey çoklu karşılaştırma testi kullanılarak değerlendirilmiştir. İki basamaklı self-etch adezivin polimerizasyon sonrası grubu hariç diğer bütün grupların bağlanma dayanım değerlerinde kontrol grubuna göre düşüş saptanmıştır (p<0,05). Tükürük kontaminasyonunun olduğu aşamaya göre bağlanma dayanım değerleri karşılaştırıldığında, bütün adeziv sistemlerin bağlanma dayanım değerlerindeki en az düşüşün polimerizasyon sonrası grupta olduğu sonucuna varılmıştır. Adeziv öncesi oluşan tükürük kontaminasyonunda, tek basamaklı self-etch sistemin 2 basamaklı self-etch sisteme göre, adeziv sonrası oluşan tükürük kontaminasyonunda ise 2 basamaklı total-etch sisteme göre istatistiksel olarak daha yüksek bağlanma dayanım değerleri gösterdiği tespit edilmiştir (p<0,05). Bu çalışmanın sınırları dâhilinde, tükürük kontaminasyonunun adeziv sistemlerin dentine bağlanma dayanımlarını etkilediği ve bu etkinin adeziv sistemin tipine ve kontaminasyonun olduğu basamağa göre değişiklik gösterdiği sonucuna varılabilir.
Özet (Çeviri)
The aim of this study was to investigate the influence of salivary contamination on bond strength to dentin during different application stages of 3 different adhesive systems. Two-step total-etch adhesive, two-step selfetch adhesive and one-step self-etch adhesive were used in this study. Twenty-four caries-free human molars were sectioned horizontally with a diamond saw to expose 1 mm thick dentin disks. Totally 48 disks (two dentin disks from each tooth) were obtained and these disks were randomly divided into 3 groups according to adhesives used. Each adhesive group was further subdivided into 4 groups according to contamination methods as follows: no contamination which was the control group, contamination before adhesive application, contamination after adhesive application and contamination after polymerization of the adhesive. For contamination, fresh saliva was collected from a single individual. In order to test the microshear bond strength of the groups, transparent plastic cylindrical molds with an internal diameter of 0,7 mm and a height of 1 mm were used to place composite resin on dentin disks. Three resin cylinders were attached on each dentin surface and 12 specimens were made for each group. All specimens were stored in distilled water at 370C for 24 hours. Microshear bond strength test was measured at a cross-head speed of 1mm/min using an universal test machine. Data were analyzed by one way analysis of variance (ANOVA) and Tukey's Honestly Significant Difference post hoc test. Except when contamination occurred after the polymerization of two step self-etch adhesive, bond strength values of all groups showed statistically significant reduction compared with control groups (p<0,05). The values of contamination after polymerization groups exhibited highest values among subgroups for all adhesives. One-step self-etch adhesive system showed statistically higher values compared to two-step self-etch adhesive system when saliva contamination occurred before adhesive application. Two-step total-etch adhesive system showed lower bond strength values compared to one-step self-etch adhesive system at contamination after adhesive application group. Within the limitations of this study, it can be concluded that, saliva contamination affects the bond strength to dentin of all adhesives used in this study and the type of adhesive and the stage of contamination can be effective on the bond strength of adhesive contaminated with saliva.
Benzer Tezler
- Florozisli daimi insan dişlerinde, iki farklı bağlanma sisteminin, mineye bağlanma üzerine olan etkilerinin, in vitro olarak incelenmesi
Başlık çevirisi yok
ÇİĞDEM KÜÇÜKEŞMEN
- Kompozit tamirinde farklı yüzey hazırlama yöntemlerinin ve yaşlandırma sürelerinin bağlanma dayanıklılığına etkisi
The effect of different surface preparation methods and various aging periods on bond strength for composite repair
MELTEM NERMİN DURSUN
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiHacettepe ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ESRA ERGİN
- Farklı estetik restoratif materyallerin bağlanma dayanımına yüzey işlemlerinin etkisi
The effect of surface treatments on the bond strength of different aesthetic restorative materials
AYŞENUR ŞAHİN
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiOrdu ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. SERDAR BAĞLAR
- Self-adeziv rezin simanlarla yapıştırılan seromerlerin dentin yüzeyine bağlantısının incelenmesi
Evaluation of bond strengths of ceromers luted by self-adhesive resin cements to dentin
MERAL DURKAN
Doktora
Türkçe
2007
Diş HekimliğiMarmara ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
DOÇ.DR. CAFER TÜRKMEN
- Ön dişlerdeki estetik kompozit restorasyonların uzun dönemli incelenmesi
Clinical evaluation of direct anterior composite restorations: A 2 year follow up
HAVVA ASUMAN ÇANDIR
Doktora
Türkçe
2001
Diş HekimliğiEge ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF.DR. BEYSER PİŞKİN