CAD/CAM sistemi ile farklı yapı ve formdaki bloklardan üretilen tam seramik kronların mikro çatlak analizi ve kırılma dayanımlarının karşılaştırılması
Comparison of fracture strength and micro crack analysis of all ceramic CAD/CAM crowns manufactured with three blocks in different form and structure
- Tez No: 460407
- Danışmanlar: DOÇ. DR. İLGİ BARAN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 115
Özet
Bu çalışmada CAD/CAM ile üç farklı bloktan üretilen tam seramik monolitik kronların yüzeyindeki oluşan mikro çatlakların incelenmesi ve kronların kırılma dayanımlarının karşılaştırılması amaçlanmıştır. Feldspatik içerikli (Priticrown-Vita Mark II) ve lityum disilikat içerikli (EmaxCAD) materyallerden (n=30) olmak üzere aynı tasarıma sahip 90 adet kron üretilmiştir. Her grup test(n=15) ve kontrol(n=15) olmak üzere iki gruba ayrılmıştır. Test grubunda CAD/CAM ile üretildikten hemen sonra floresan penetrant yöntemiyle mikro çatlak analizi yapılmış ve Cr-Co daylara çinko fosfat simanla simante edildikten sonra 5°C-55°C arasında 5000 döngü uygulanmıştır. Termal döngünün ardından ikinci mikro çatlak incelemesi yapılmış ve kronlara universal test cihazında 0,5 mm/dk hızla kırılana kadar kuvvet uygulanmıştır. Kontrol grubundaki kronlar da CAD/CAM ile üretim işleminden sonra Cr-Co daylara çinko fosfat simanla simante edilmiş ve kırılma dayanımı testine tabi tutulmuştur. Kırık şekilleri incelendikten sonra taramalı elektron mikroskobuyla fraktografik belirteçler belirlenmeye çalışılmıştır. Mikro çatlak değerleriyle kırılma dayanımı arasındaki ilişki Spearman Korelasyon testiyle, kırılma dayanımı değerleri Kruskal Wallis H testi ve Mann Whitney U testiyle, mikro çatlak değerleri Kruskal Wallis H testi ve Wilcoxon İşaretli Sıralar testiyle değerlendirilmiştir. Mikro çatlak sayısı ile kırılma dayanımı değerleri arasında Priticrown materyalinin termal döngü uygulanmayan grubu(r=-,532) hariç istatistiksel olarak anlamlı bir ilişki bulunmamıştır(p>0.05).EmaxCAD kronların kırılma dayanımları diğer iki gruba göre termal döngüden önce ve sonra anlamlı derecede yüksek bulunmuştur(p=0.000). Termal döngünün mikro çatlak sayısı ve kırılma dayanımı üzerinde istatistiksel olarak anlamlı bir etki oluşturmadığı görülmüştür (p>0.05) ve kron formundaki blok yapısına sahip Priticrown materyalinin mikro çatlak oluşumu açısından avantaj sağlamadığı sonucuna ulaşılmıştır.
Özet (Çeviri)
This study intended to analyze micro cracks those occur on the surface of the all ceramic monolithic crowns and compare the crowns' fracture strength values. Totally 90 crowns in same design were manufactured from feldspathic (Priticrown-Vita Mark II) and lithium disilicate(EmaxCAD) blocks, each material grup had 30 crowns. Test (n=15) and control (n=15) groups were prepared for every material. In the test group the crowns were analyzed by florescence penetrant method for micro crack evaluation following the manufacturing process and after cementation onto the Cr-Co die structures with zinc-phospate cement, thermal cycling consists of 5000 cycles between 5°C-55°C was carried out. Second micro crack analysis was applied on crowns that were treated with thermal cycling and the crowns were loaded to fracture at a crosshead speed of 0.5 mm/min in a universal testing machine. The other half of the crowns in each group, after manufacturing process, were directly cemented onto the Cr-Co dies with zinc-phospate cement and loaded to fracture. After evaluating fracture modes, fractographic markings were analyzed by scanning electron microscopy. Spearman Correlation analysis was applied for detecting if there was a relation between micro crack numbers and fracture strength values. Fracture strenth values were analyzed by Kruskal Wallis H and Mann Whitney U tests, micro crack values were analyzed by Kruskal Wallis H and Wilcoxon Signed Rank tests. Except the group of Priticrown material that wasn't treated with thermal cycling(r= -,532), statistically significant relation was not found between micro crack numbers and fracture strength values(p>0.05). There was significant difference between fracture strength values of EmaxCAD crowns and other groups(p=0.000), before and after thermal cycling. Thermal cycling didn't have significant effect on micro crack numbers and fracture strength values (p>0.05) and crown shaped Priticrown blocks didn't provide advantage against micro crack formation.
Benzer Tezler
- İmplant destekli sabit protezlerde CAM/CAM sistemleri ile üretilen destek ve üst yapı restorasyonlarının sonlu elemanlar stres analiz yöntemi ve kırılma direnci testi ile karşılaştırmalı olarak incelenmesi
The comparatively investigation of abutment and crown restorations produced by CAD/CAM systems in implant supported fixed prostheses using the finite element stress analysis method and fracture resistance test
NAZİRE ESRA BAĞDATLI
Doktora
Türkçe
2016
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. AHMET ERSAN ERSOY
- CAD/CAM sistemi ile üretilmiş farklı yapıdaki seramik kronlarda siman film aralığı değişiminin renk ve dayanım üzerine etkisi
The effect of the cement film thickness on colour and strentgh in different all ceramic crowns fabricated with CAD/CAM system
ABDURRAHMAN ŞAHİNBAŞ
Doktora
Türkçe
2015
Diş HekimliğiYüzüncü Yıl ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GÜRCAN ESKİTAŞCİOĞLU
- The evaluation of the influence of different finishing line depth on strength of CAD/CAM restorations
CAD/CAM restorasyonlarında farklı basamak genişliklerinin dayanım üzerine etkisinin incelenmesi
LANA BAHRAM KHIDHER
Doktora
İngilizce
2019
Diş HekimliğiVan Yüzüncü Yıl ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MURAT ESKİTAŞCİOĞLU
- CAD/CAM sistemi ile üretilen hibrit abutment destekli anterior restorasyonda kemik rezorpsiyon riskinin ve stres dağılımının sonlu elamanlar analizi ile incelenmesi
Investigation of bone resorption risk and stress distribution in hybrid abutment supported anterior restoration produced with CAD/CAM system by finite element analysis
CİHAN AKDOĞAN
Doktora
Türkçe
2024
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HATİCE ÖZDEMİR
- Monolitik ve çift katmanlı zirkonya seramik kuronların kenar uyumlarının ve kırılma dirençlerinin in vitro olarak değerlendirilmesi
In vitro evaluation of marginal adaptation and fracture strength of monolithic and double-layered zirconia ceramic crowns
DAMLA KARA
Diş Hekimliği Uzmanlık
Türkçe
2016
Diş HekimliğiAdnan Menderes ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. BAYKAL YILMAZ