Epoksitlendirilmiş soya yağından tioglikolik asit ve tioglikolik asit metil esteri ile halka açarak oluşan poliollerden yeni poliüretan sentezi ve karakterizasyonu
New polyurethane synthesis and characterization from epoxidized soybean oil by ring-opening polyols with thioglycolic acid and thioglycolic acid methyl ester
- Tez No: 461737
- Danışmanlar: YRD. DOÇ. DR. KEMAL KARADENİZ
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Rijit-esnek biyokökenli poliüretan, halka açılması, iki fonksiyonlu bileşikler, glikolik-tiyoglikolik asit, yenilenebilir kaynaklar, bitkisel kökenli poliol, Rigid-flexible biobased polyurethane, Ring opening, Bifunctional compounds, Glycolic-thioglycolic acid, Renewable sources, Biobased polyol
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Sakarya Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Anorganik Kimya Bilim Dalı
- Sayfa Sayısı: 77
Özet
Bu çalışmada, epoksitlenmiş soya yağının epoksi halka açılması iki farklı işlevsel gruba sahip olan kimyasallarla yapılarak bio kökenli polioller ve poliüretanların sentezi ilk kez bildirilmiştir. Tiyoglikolik asit (TGA), glikolik asit (GA) ve metil tiyoglikolat (MTGA) ile halka açılması yapılarak bunlar poliüretan sentezinde kullanılmıştır. Hidroksil ve karboksil fonksiyonel gruplarına sahip GA ilk kez epoksi halka açılması için kullanılmıştır. TGA ile elde edilen (poliol 1), GA ile elde edilen (poliol2) ve MTGA ile elde edilen (poliol 3), 4,4'-metilenbis(fenil izosiyanat)(MDI) ile reaksiyona sokularak biyo kökenli polüretanlar elde edilmiştir. Elde edilen yeni bileşiklerin FT-IR, 1HNMR, 13CNMR ile yapıları belirlendi. SEM, XRD, GPC, DSC, TGA, XRD ölçümleri yapılarak özellikleri belirlenmiştir. Yeni poliüretanların OH/NCO mol oranı 1.85/1'den 2.12/1'e kadar değişen oranlarda hazırlanmış ve bunların esnekten sertliğe doğru gerilme mukavemetleri (3.44-39.7MPa) olarak ölçülmüştür. Aynı poliol/MDI oranına sahip poliollerden en iyi gerilme özelliklerine sahip olan poliüretanın en yüksek OH işlevselliğine sahip olan poliol 1 den elde edildiği gözlemlenmiştir.
Özet (Çeviri)
In this study, polyols of biodegradation type was firstly synthesized from epoxized soybean oil and polyurethanes obtained from epoxy ring opening with chemicals present in two different functional groups. The thioglycolic acid (TGA), glycolic acid (GA) and methyl thioglycolate (MTGA) were used for ring opening reaction and used in polyurethane synthesis. GA having hydroxyl and carboxyl functional groups was used for the first time for epoxy ring opening. Bio-derived polyurethanes were obtained by reacting with 4,4'-methylenebis (phenyl isocyanate) (MDI) by TGA (polyol 1), GA (polyol 2) and MTGA (polyol 3). The new compounds obtained were identified by FT-IR, 1HNMR, 13CNMR, SEM, XRD, GPC, DSC, TGA, XRD combinations. The molar ratio of the new polyurethanes to OH from NCO was prepared from 1.85 / 1 to 2.12 / 1 and their tensile strengths were measured as flexible to hardness (3.44-39.7 MPa). It has been observed that the polyurethane having the best stretch properties of polyols having the same polyol / MDI ratio results in a polyol having the highest OH functionality.
Benzer Tezler
- Odun korumada bitkisel yağların yanmaya karşı etkinliğinin arttırılması
Increasing fire resistance of plant oils in wood protection
SERDAR DEMİR
Yüksek Lisans
Türkçe
2018
Ağaç İşleriKaradeniz Teknik ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ TEMİZ
- Effect of epoxidized soybean oil and synthetic resins impregnation and densification on poplar and alder wood properties
Epoksitlenmiş soya yağı ve sentetik reçinelerin yoğunlaştırılmış kavak ve kızılağaç odun özellikleri üzerine etkisi
ANTENEH GEZAHEGN KEBEDE
Doktora
İngilizce
2024
Ormancılık ve Orman MühendisliğiKaradeniz Teknik ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ TEMİZ
- Isıl işlem sırasında açığa çıkan katranın odun koruma maddesi olarak kullanılabilirliği
Usability of wood tar from heat treatment process as a wood preservative
GAYE KÖSE
Yüksek Lisans
Türkçe
2012
Ormancılık ve Orman MühendisliğiKaradeniz Teknik ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİ TEMİZ
- Kargı (Arundo donax L.) yıllık bitkisinden elde edilen biyo-yağın odun koruma maddesi olarak etkinliğinin araştırılması
Efficiency of bio-oil obtained from giant reed (Arundo donax L.) as a wood preservative
SELÇUK AKBAŞ
Yüksek Lisans
Türkçe
2011
Ormancılık ve Orman MühendisliğiKaradeniz Teknik ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİ TEMİZ
DOÇ. DR. SAMİ İMAMOĞLU
- Ahşap malzemelerde faz değiştiren maddelerin enerji depolamaya etkisi
The effect of phase change materials on energy storage in wood materials
ÖZGE NUR ERDEYER
Yüksek Lisans
Türkçe
2024
Ormancılık ve Orman MühendisliğiKaradeniz Teknik ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ TEMİZ