Lamine kompozitlerle istiflenmiş metal malzemelerin delinebilirliğinin araştırılması

Investigation of drillability of metal materials stacked with lamine composites

  1. Tez No: 466619
  2. Yazar: NAFİZ YAŞAR
  3. Danışmanlar: DOÇ. DR. MUSTAFA GÜNAY
  4. Tez Türü: Doktora
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2017
  8. Dil: Türkçe
  9. Üniversite: Karabük Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 196

Özet

Bu çalışmada, karbon fiber takviyeli kompozit (KFTK)/Ti6Al4V istifli malzemelerin delinmesinde oluşan itme kuvveti, moment, delaminasyon, yüzey pürüzlülüğü, delik kalitesi ve kesici takım ömrünün delme parametreleri ile ilişkileri analiz edilmiştir. Üç farklı matkap kalitesi (kaplamasız WC, TiAlN ve elmas kaplamalı WC) ile matkap uç açısı, ilerleme miktarı ve kesme hızının farklı değerleri kullanılarak delme deneyleri gerçekleştirilmiştir. Bu bağlamda, KFTK ve Ti6Al4V alaşım malzemelerinin her biri için L27 deney tasarımına göre yapılan ön deneyler sonucunda itme kuvveti, yüzey pürüzlülüğü, delaminasyon faktörü ve moment değerleri tespit edilmiştir. Bu deneyler sonucunda, her iki deney malzemesi için en düşük itme kuvveti (Fz) kaplamasız WC ile ölçülürken, en yüksek Fz değeri ise TiAlN kaplamalı matkap ile elde edilmiştir. Elde edilen sonuçlara gri ilişki analizi uygulanarak KFTK/Ti6Al4V istifli malzemelerin delinmesinde kesici takım performans deneylerinde kullanılacak parametrelerin optimum değerleri belirlenmiştir. Optimum kesme parametreleri, her bir kesici takım kalitesi ve iş parçası malzemesi için en düşük kesme hızı ve ilerleme miktarı olarak bulunmuştur. Son olarak, optimum delme parametrelerine göre KFTK/Ti6Al4V istifli malzemenin delinmesinde kesici takım performanslarını belirlemek amacıyla takım ömrü deneyleri yapılmıştır. İstifli malzemelerin delinmesinde KFTK için en düşük delaminasyon faktörü ve yüzey pürüzlülüğü elmas kaplamalı WC takımla elde edilirken, Ti6Al4V için en düşük yüzey pürüzlülüğü ve itme kuvveti kaplamasız WC takım ile ölçülmüştür.

Özet (Çeviri)

In this study, the relationship between drilling parameters and delamination, surface roughness, hole quality, cutting tool life, thrust force and moment generated in drilling of carbon fiber reinforced composite (CFRP) / Ti6Al4V stacked materials were analyzed. Drilling experiments were carried out using three different drill qualities (uncoated WC, TiAlN and diamond coated WC) using different values of drill point angle, feed rate and cutting speed. In this context, thrust force, surface roughness, delamination factor and moment values were determined for each of CFRP and Ti6Al4V alloy materials as a result of the preliminary tests made according to the L27 test design. As a result of these experiments, the lowest thrust force (Fz) for both test materials was measured by uncoated WC, while the highest Fz value was obtained by TiAlN coated drill. Gray correlation analysis was applied to the obtained results and optimum values of the parameters used in cutting tool performance tests were determined in drilling of CFRP / Ti6Al4V stacked materials. Optimum cutting parameters were found as the lowest cutting speed and feed rate for each cutting tool quality and workpiece material. Finally, tool life tests were carried out to determine the cutting tool performance in drilling of CFRP / Ti6Al4V stacking material according to optimum drilling parameters. The lowest surface roughness and thrust force for Ti6Al4V was measured with uncoated WC tool, while the lowest delamination factor and surface roughness for CFRP were obtained with diamond coated WC tool in drilling of the stacked materials.

Benzer Tezler

  1. Design and analysis of a prosthetic below-knee socket using composite materials supported by nanomaterials

    Nanomalzemelerle desteklenen kompozit malzemeler kullanılan protez diz altı soket tasarımı ve analizi

    FALAH ABDULKADHIM BRAIBER AL-KHAFAJI

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    Makine MühendisliğiAltınbaş Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. YASER ALAIWI

  2. Strain partitioning and plastic flow in some metal/ metal laminates

    Bazı metal-metal lamine kompozitlerde gerinim bölüşülmesi ve plastik akma

    S.M.JAVIAD MİRMESDAGH

    Yüksek Lisans

    İngilizce

    İngilizce

    1993

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. TAYFUR ÖZTÜRK

  3. Damage detection of laminated composite structures using inverse finite element method

    Lamine kompozit yapılarda ters sonlu elemanlar yöntemi ile hasar tespiti

    FARAZ GANJDOUST

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    Mekatronik MühendisliğiSabancı Üniversitesi

    Mekatronik Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ADNAN KEFAL

  4. Effect of steel fiber on the mechanical properties of the glass and basalt fiber composites

    Cam ve basalt fiber kompozitlerde çelik fiberin mekanik özellikler üzerindeki etkisi

    BAYAN JABBAR FAYZULLA

    Doktora

    İngilizce

    İngilizce

    2023

    Metalurji MühendisliğiFırat Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MEHMET EROĞLU

    PROF. DR. AHMET ERKLİĞ

  5. Production of carbon nanotube reinforced nanoprepregs and their characterization

    Karbon nanotüp takviyeli nanoprepreglerin geliştirilmesi ve karakterizasyonu

    BEYZA BOZALİ

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Tekstil ve Tekstil Mühendisliğiİstanbul Teknik Üniversitesi

    Tekstil Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ELİF ÖZDEN YENİGÜN