Farklı yüzey tedavileri uygulanmış bulk fill ve posterior kompozitlerde bağlanma kuvvetlerinin karşılaştırılması
Comparison shear bond strenght of bulk composite and posterior composites with different surface treatments
- Tez No: 481022
- Danışmanlar: DOÇ. DR. BAYRAM İNCE
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Er:YAG, bağlanma dayanımı, bulk fill, Dental bonding, Dental materyaller, Dental restorasyon, Dentin, Kompozit reçineler, Lazerler, Yüzey pürüzlülüğü, Dental bonding, Dental materials, Dental restoration, Dentin, Composite resins, Lasers, Surface roughness
- Yıl: 2017
- Dil: İngilizce
- Üniversite: Dicle Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç; Dentin yüzeyinin asitle ve lazerle pürüzlendirilmesi bağlanma kuvvetlerini artırmak amacıyla yapılmaktadır. Bu çalışmada kompozitlerin hem tabakalama yöntemleri hem de pürüzlendirme yöntemlerinin dentine olan bağlanma dayanımı üzerinde etkisi incelenmiştir. Materyal ve metod; Çalışmamızda 180 adet çürüksüz, restorasyonsuz üçüncü molar diş kullanıldı. Dişler dentin yüzeyi yere paralel olacak şekilde 3cm ve 6cm kenarlara sahip ve 4cm boyunda dikdörtgen plastik kalıplara kökleri içinde kalacak şekilde soğuk akril yardımıyla yerleştirildi. Örnekler rastgele üç ana gruba (n=60) ayrıldı. 1.grup asitle pürüzlendirme, 2.grup lazerle(Er:YAG) pürüzlendirme ve 3.grup kontrol grubu olacak şekilde gruplandırıldı. Her grupta 4 alt gruba ayrıldı. Alt gruplardaki örneklerin dentin yüzeylerinde dört farklı restoratif dolgu materyali kullanıldı. Restoratif dolgu materyalleri çapı 3 mm, yüksekliği 4 mm olan silikon şeffaf kalıplar içerisine konularak dentin yüzeyinde polimerize edildi. 3M P60, 3M Bulk fill,Tetric N Ceram and Tetric N Ceram Bulk fill restoratif materyalleri kullanıldı. Tek aşamalı self-etch Universal Single Bond kullanıldı. İnstron universal test cihazına yerleştirilen örneklere 1 mm/dak. hızda makaslama kuvveti uygulanarak kırılıncaya kadar kuvvet uygulandı. Elde edilen değerler MPa cinsinden kaydedildi. Kırılan yüzeyler, x40 büyütmede stereomikroskopta incelenerek kırık tipleri tespit edildi. Bulgular: 3M posterior ve bulk fill uygulanan örneklerde asit ile pürüzlendirmenin lazer ile pürüzlendirmeye göre, lazer ile pürüzlendirmenin pürüzlendirme yapılmayan gruba göre makaslama bağlanma dayanımlarının istatistiksel olarak anlamlı derecede yüksek olduğu bulunmuştur (p<0,05). Tetric N Ceram ve Tetric N Ceram bulk fill uygulanan örneklerde asitle pürüzlendirme, lazerle pürüzlendirme ve kontrol grupları arasında istatistiksel olarak anlamlı bir fark bulunmamıştır (p<0,05). Bu çalışmada lazer uygulanan gruplarda Tetric N Ceram ile Tetric N Ceram bulk fill arasındaki fark istatistiksel olarak anlamlı bulunmuştur (p<0,05). Diğer gruplarda tabakalama ve bulk fill tekniği arasında istatistiksel olarak anlamlı bir fark bulunmamıştır (p<0,05). Sonuç: Lazerle pürüzlendirme asitle pürüzlendirmeye alternatif bir yöntem olarak kullanılabilir. Bulk fill yöntemi de tabakalama yöntemine alternatif olarak bağlanma dayanımı açısından kliniklerde kullanılabilir.
Özet (Çeviri)
Aim; Acid and laser etching is applied on the dentin surface to increase the bond strength. In this study, the effects of both the layering methods and the etching methods on dentin bonding strength of composites were investigated. Materials and Methods; In our study, 180 noncarious and unrestored third molar teeth were used. All of the teeth were embeded to the auto polimerisan acryl in the rectangular plastic mold which were at the 3cm and 6cm edges and 4cm long as occlusal surface facing paralel with ground. The samples were randomly divided into three main groups (n = 60). Group 1 acid etching Group 2 Laser (Er: YAG) etching, and Group 3 control group. After that each group divided 4 sub groups. Four different restorative fillings materials were used on dentin surfaces of the samples in the subgroubs. The restorative filling materials were polymerized on the dentin surface by placing them in silicone transparent molds 3 mm in diameter and 4 mm in height. 3M P60, 3M Bulk fill,Tetric N Ceram and Tetric N Ceram Bulk fill restorative materials were used. Self-etch Universal Single Bond was used. In the Instron Universal test machine power applied as 1mm/minute speed till restoration broken from sample. Data recorded as a MPa. Fracture tips established on the broken samples surface with stereo microscope 40X magnification. Results; It was found that in 3M posterior and bulk fill groups while acid etching had higher shear bond strength compared to laser-etching statistically, laser-etching had higher shear bond strength compared to non-etching statistically (p<0,05). No statistically significant differance was found between laser etching,acid etching and control groups in Tetric N Ceram and Tetric N Ceram bulk fill applied samples. In this study, the difference between Tetric N Ceram and Tetric N Ceram bulk fill in the laser treated groups was found to be statistically significant (p<0,05). Conclusion; Laser etching may be used as an alternative to acid etching. Bulk fill method may be used in clinics in terms of bonding strength as an alternative to layering method. Keywords; Er:YAG, bond strength, bulk fill
Benzer Tezler
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Testosteron dihidrotestosteron ve östrojenin benign prostat hiperplazisindeki etyolojik rolleri
The roles of testosterone, dihydrotestosterone and estradiole on the etiology of benign prostatic hyperplasia
HALUK TOKUÇOĞLU
- Süt formüllerinin tüketim uygulamaları ve süt formüllerinin C vitamini içeriği ile pH değerleri
Başlık çevirisi yok
GÖNÜL VAROL
Yüksek Lisans
Türkçe
1986
Besin Hijyeni ve Teknolojisiİstanbul ÜniversitesiÇocuk Gelişimi Ana Bilim Dalı
DOÇ. DR. TÜRKAN KUTLUAY
- Türkiye'de aile planlaması çalışmalarında erkeklerin önemi, hastane personeli ile fabrika işçilerinin doğum kontrol yöntemlerine karşı tutum ve davranranışlarında farklılığın araştırılması
Başlık çevirisi yok
KAMİL MALKOÇLU
Yüksek Lisans
Türkçe
1987
Demografiİstanbul ÜniversitesiAile Sağlığı Ana Bilim Dalı
DOÇ. DR. DERİN KÖSEBAY