Polipropilen (PP)/polietilen tereftalat (PET) harmanlarının reolojik davranışları ve viskoelastik özelliklerinin incelenmesi
Investigation of rheological behaviors and viscoelastic properties of polypropylene (PP)/polyethylene terephthalate (PET) blends
- Tez No: 490192
- Danışmanlar: DOÇ. DR. ALİ DURMUŞ
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2018
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Kimyasal Teknolojiler Bilim Dalı
- Sayfa Sayısı: 115
Özet
Bu tez çalışmasında, polipropilen (PP), poli(etilen tereftalat) (PET) ve maleik anhidrit aşılanmış polipropilen (PP-g-MA) kullanımıyla farklı bileşimlerde PP/PET harmanları, çift vidalı ekstruderde eriyik harmanlama yöntemiyle hazırlanmıştır. Harmanların mikro yapıları, erime ve kristallenme davranışları, eriyik hal reolojik davranışları ve viskoelastik özellikleri bileşime bağlı olarak incelenmiştir. Harmanların mikro yapısı ve morfolojik özellikleri taramalı elektron mikroskobundaki (SEM) incelemelerle, erime ve kristallenme davranışları ise, diferansiyel taramalı kalorimetre (DSC) cihazında gerçekleştirilen analizlerle belirlenmiştir. Salınımlı rotasyonel reometre cihazında gerçekleştirilen eriyik-hal reolojik testleri ile harmanların kayma modülleri (G', G'') ve dinamik viskozite (η*) değerlerinin uzama, frekans ve kayma hızına bağlı değişimleri ölçülmüştür. Ayrıca harmanların eriyik hal gerilim gevşeme davranışları incelenmiştir. Reolojik ölçüm verileri çeşitli matematiksel yaklaşımlarla modellenmiş ve reolojik parametreler hesaplanmıştır. Mikro yapı incelemelerinde, 90/10, 80/20 ve 70/30 bileşimindeki PP/PET harmanlarının uyumsuz matris-damlacık yapısında oldukları, 60/40 bileşimine sahip harmanın ise eş-süreklimorfolojiye sahip olduğu gözlenmiştir. Diğer yandan, ekstrüzyon prosesi, bileşim ve uyumlaştırıcı kullanımına bağlı olarak bazı harmanlarda“matris-fibril”morfolojisi de gözlenmiştir. DSC bulgularına göre, PET'in PP'nin kristalizasyon hızını arttırdığı, kristallenme oranını ise azalttığı tespit edilmiştir. Harmanların eriyik elastikliğinin, bileşime ilave edilen PET miktarının artışına bağlı olarak azaldığı, uyumlaştırıcı miktarına bağlı olarak ise arttığı tespit edilmiştir. Gerilim gevşeme testlerinden, PET'in bileşimdeki miktarının artmasıyla harmanların gevşeme modülünün daha hızlı şekilde düştüğü ve gevşeme sürelerinin azaldığı belirlenmiştir.
Özet (Çeviri)
In this thesis, PP/PET blends having different compositions were prepared by melt blending method in a twin-screw extruder by using polypropylene (PP), poly (ethylene terephthalate) (PET) and maleic anhydride grafted polypropylene (PP-g-MA). Microstructures, melting and crystallization behaviors, melt-state rheological behaviors and viscoelastic properties of blends were investigated depending on the composition. Microstructures and morphological properties of blends were examined by scanning electron microscopy (SEM), their melting and crystallization behaviours were determined by analysis performed in a differential scanning calorimeter (DSC). Shear modulus (G', G“) and dynamic viscosity (η*) values of blends were measured in an oscillatory rotational rheometer depending on shear strain, frequency and shear rate. Furthermore, melt-state stress relaxation behaviors of blends were studied. Rheology data were modeled by various mathematical approaches and rheological parameters were calculated. It was observed that the PP/PET blends having the compositions of 90/10, 80/20 and 70/30 exhibited immiscible matrix-droplet morphology in microstructural characterization studies, while the 60/40 blends showed co-continuous morphology. On the other hand, ”matrix-fibril" morphology was also observed in some blends depending on extrusion process, composition and using of compatibilizer. It was found that PET increased the crystallization rate of PP, but decreased the crystallinity ratio based on DSC data. It was also found that the melt elasticity of blends reduced with the increasing amount of added PET and increased with the increasing amount of compatibilizer. Stress relaxation tests indicated that the increasing amount of PET into blend composition resulted in faster decrease in relaxation modulus of blends and decreased the relaxation times.
Benzer Tezler
- Poli(etilen tereftalat)-polipropilen harmanlarının kristalizasyon özelliklerinin incelenmesi
Investigation of crystallization properties of poly(ethylene terephthalate)-polypropylene blends
EBRU GÜMÜŞ
Yüksek Lisans
Türkçe
2014
Kimya Mühendisliğiİstanbul ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. TUNCER YALÇINYUVA
- Investigation of mechanical and physical properties of spunlaced nonwoven fabrics containing bicomponent fibers
Bikomponent elyaf içeren spunlace dokunmamış kumaşların fiziksel ve mekaniksel özelliklerinin incelenmesi
EYÜP ALİ SATIL
Yüksek Lisans
İngilizce
2021
Tekstil ve Tekstil MühendisliğiGaziantep ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET DAŞDEMİR
- PET, polipropilen, polietilen atıkların ve cam tozunun çimento harçlarının özelliklerine etkisi
The effect of PET, polypropylene, polyethylene wastes and glass powder on the properties of cement mortars
GÖKSU PILSIM
Yüksek Lisans
Türkçe
2023
İnşaat MühendisliğiEge Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. ŞEMSİ YAZICI
- Farklı plastik atıkların birlikte pirolizinden elde edilen katı ürünle modifiye edilmiş bitümlü sıcak karışımların mühendislik özelliklerinin araştırılması
Investigation of engineering properties of hot mix asphalt modified with solid product obtained from co–pyrolysis of different waste plastics
MUHAMMET MEVLÜT AKMAZ
Doktora
Türkçe
2020
UlaşımKonya Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. OSMAN NURİ ÇELİK
- Plastikler ve mermer çamuru atıklarına simbiyotik bir çözüm olarak katalitik piroliz
Catalytic pyrolysis as a symbiotic solution to plastic and marble sludge wastes
AFRA ÖZGAN
Yüksek Lisans
Türkçe
2022
Çevre MühendisliğiKonya Teknik ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
PROF. DR. ESRA YEL