Beton deney numune atıklarının geri dönüşüm agregası olarak betonda kullanılabilirliğinin incelenmesi

Investigation of the usability of concrete experiment sample wastes as recycled aggregate

  1. Tez No: 518499
  2. Yazar: MÜSLÜM BATMAN
  3. Danışmanlar: DOÇ. DR. AHMET FERHAT BİNGÖL
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Geri dönüşüm agregası, beton numune atıkları, inşaat ve yıkım atıkları, kılcal geçirimlilik, eğilmede çekme dayanımı, Recycled concrete aggregate, concrete sample wastes, construction and demolition wastes, capillary water absorption, flexural tensile strength
  7. Yıl: 2018
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Yapı Bilim Dalı
  13. Sayfa Sayısı: 78

Özet

Günümüzde, atık malzemelerin geri dönüşümü çalışmaları; ekonomik kazanımın sağlanması, çevre kirliliğinin engellenmesi ve hammadde kaynaklarının korunması gibi sonuçlar sağlamasından dolayı önemli bir başlık haline gelmiştir. Bu tez çalışmasında, hazır beton santrallerinde basınç dayanımına tabi tutulan 3, 7, 28 günlük beton numunelerin öğütülerek geri dönüşüm işlemleri sonucunda elde edilen geri dönüşüm agregasının (GDA) farklı oranlarda kullanılarak üretilen beton numuneler ile kırmataş agrega (KA) kullanılarak üretilen beton numunelerin 28 günlük basınç dayanımı, eğilmede çekme dayanımı, su emme ve kılcal geçirimlilik özellikleri karşılaştırılmıştır. Beton karışımı hesaplarında su/çimento oranı 0,57 olarak seçilmiş olup beton tasarımları belirlenmiştir. Beton tasarımlarında, %100 KA'nın kullanıldığı beton numuneler referans beton numuneleri olarak kabul edilmiştir. İnce (0-4 mm) ve iri (4-12 mm) GDA %15, %30, %45 ve %60 oranlarında beton karışımına ikame edilerek beton numuneleri hazırlanmıştır. %100 KA ve %15 oranında GDA kullanılan beton karışımlarına çimento ağırlığının %1,25'i oranında akışkanlaştırıcı ve %30, %45 ve %60 oranlarında GDA kullanılan beton karışımlarına çimento ağırlığının %1,20 oranında süper akışkanlaştırıcı kullanılmıştır. Beton numunelerinin basınç dayanımı, eğilmede çekme dayanımı, kılcal geçirimlilik ve su emme oranı belirleme deneylerinin sonuçları karşılaştırıldığında; GDA ikame edilerek elde edilen beton numunelerin deney sonuçları ile referans betonun deney sonuçları arasında belirgin fark olmadığı görülmüştür. %60 GDA kullanılan betonun basınç dayanımı %100 KA kullanılan referans betonun basınç dayanımına göre yaklaşık olarak %13 oranında düşük olduğu görülmüştür. %60 oranında GDA içeren beton numunelerinin basınç dayanımı deneyinde beton sınıfı olarak C 30 sınıfında çıkması sonucunda, hazır beton santrallerinde basınç dayanımı vb. deneylere tabi tutulan beton deney numune atıklarından elde edilen GDA'ların beton üretiminde kullanılabileceği düşünülmektedir.

Özet (Çeviri)

Nowadays, the assessment of waste materials has become an important topic because it provides economic gains, prevents environmental pollution, protection of raw material resources. In this study, concrete specimens were produced by using crushed aggregate (CA) and recycled aggregate (RA) and 28 days compressive strength, flexural tensile strength, water absorption and capillarity water absorption values were compared after tests. The recycled aggregate is obtained from the waste specimens which were exposed to compressive and flexural strength tests at 3,7 and 28 days age in ready mixed concrete plants. In concrete mixture calculations, water / cement ratio was chosen as 0.57 and concrete designs were determined. In concrete designs, 100% of the crushed aggregate (CA) were used as reference concrete specimens. The concrete samples were prepared by replacing the fine (0-4 mm) and coarse (4-12 mm) RA with 15%, 30%, 45% and 60% of the concrete mixture. Plasticizers and Superplasticizers were used for concrete mixes using 100% of CA and 15% of RA, 1.25% of cement weight and 1.20% of cement weight for concrete mixes using 30%, 45% and 60% of RA, respectively. The values of compressive strength, flexural tensile strength, capillarity water absorption and water absorption ratio of concrete samples using of RA did not show any significant difference with the values of concrete specimens produced with reference concrete. It is seen that the 60% of RA used concrete approximately 13% lower compressive strength compared to 100% of CA used concrete. By the result of C30 class as a concrete class at the compressive strength experiment for 60% RA included concrete samples, the RA's that obtained from concretes experiment samples wastes exposed to experiments such as compressive strength.

Benzer Tezler

  1. Taban külü atığı ve pomza agregası kullanılarak çimento esaslı ve geri dönüştürülmüş polietilen tereftalat (PET) içerikli kompozit üretimi ve optimizasyonu

    Production and optimization of cement based and recycled polyethylene terephthalate (PET) composite using bottom ash waste and pumice aggregate

    ARZU ÇAKMAK

    Doktora

    Türkçe

    Türkçe

    2023

    MimarlıkAkdeniz Üniversitesi

    Mimarlık Ana Bilim Dalı

    PROF. DR. HACER MUTLU DANACI

    DOÇ. DR. SALİH TANER YILDIRIM

  2. Mermer çamur atıklarının yapı malzemesi olarak kullanılması

    Using of marble mud waste in the production of building materials

    AYDIN APAYDIN

    Doktora

    Türkçe

    Türkçe

    2024

    MimarlıkSüleyman Demirel Üniversitesi

    Mimarlık, Planlama ve Tasarım Ana Bilim Dalı

    PROF. ATİLA GÜL

  3. Endüstriyel bir atık olan demir talaşının betonarme kirişlerinin eğilme dayanımına etkisi

    Başlık çevirisi yok

    ÇAĞATAY ASLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    İnşaat MühendisliğiEskişehir Osmangazi Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. MİZAN DOĞAN

  4. Serpantinin asfalt betonunda filler olarak kullanılması

    Using serpentine as filler in asphalt concrete

    BEKTAŞ SÜMEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    İnşaat MühendisliğiIsparta Uygulamalı Bilimler Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. NİHAT MOROVA

  5. An investigation of fresh and hardened properties of cementitious grout made with combined use of waste marble powder and fly ash

    Atık mermer tozu ve uçucu külün birlikte kullanımıyla üretilen çimento esaslı enjeksiyon harcının taze ve sertleşmiş özelliklerinin araştırılması

    MUHAMMET ÇINAR

    Doktora

    İngilizce

    İngilizce

    2019

    İnşaat MühendisliğiHasan Kalyoncu Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. MEHMET KARPUZCU