Sol-jel yöntemiyle üretilen HfO2 ince filmlerin karakterizasyonu

Characterization of sol-gel derived HfO2 thin films

  1. Tez No: 522604
  2. Yazar: SEDA KOL
  3. Danışmanlar: PROF. DR. AHMET YAVUZ ORAL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2018
  8. Dil: Türkçe
  9. Üniversite: Gebze Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 103

Özet

HfO2 yüksek kırılma indisi (~2) ve yüksek bant boşluğu (5.4 eV) sayesesinde en uygun dielektrik malzemedir. Bu yüzden hem optik hem de mikroelektronik cihazlarda yaygın olarak kullanılmaktadır. Bu çalışmada, sol-jel yöntemiyle üretilen HfO2 tozların ve ince filmlerin mikroyapı ve optik özellikleri incelenmiştir. Hafniyum tetraklorür, etanol içinde çözüldükten sonra, asetik asit ve saf su eklenerek berrak bir çözelti hazırlanmıştır. Çözeltinin bir kısmı hava ortamında kurutulup, farklı sıcaklıklarda sinterlenerek toz elde edilmiştir. Kalan çözelti 0,45 µm'lik mikro filtreden geçirilmiştir. HfO2 ince filmler 20, 30 ve 40 kat olarak, cam altlıklar üzerine daldırmalı kaplama yöntemi kullanılarak kaplanmıştır. Her kattan sonra, filme 2 dk ara tavlama yapılmıştır. Son olarak üretilen filmler, fırında farklı sıcaklıklarda, 1 saat tavlanmıştır. Üretilen numuneler, X-ışını kırınımı (XRD), atomik kuvvet mikroskobu (AFM), taramalı elektron mikroskobu (SEM), ultraviyole-görünür bölge (UV-Vis) spektroskopisi ve prizma çiftleyici kullanılarak karakterize edilmiştir. XRD sonuçlarında, 450℃ üzerindeki sıcaklıklarda sinterlenen HfO2 tozlarının monoklinik faz yapısında, 450℃ altındaki sıcaklıklarda ise amorf yapıda olduğu sonucuna varılmıştır. İnce filmlerin XRD sonuçlarında ise, 400 ve 500℃'de tavlanan HfO2 ince filmlerin amorf yapıda, 600℃'de tavlanan HfO2 ince filmlerin monoklinik faz yapısında olduğu gözlemlenmiştir. AFM sonuçlarında, 600°C'de tavlanan 40 kat kaplı HfO2 ince filmin yüzey pürüzlülüğü 2.260 nm olarak en yüksek değerde ölçülmüştür. SEM görüntülerinde, 30 kat kaplı HfO2 filmin kalınlığı yaklaşık 1 μm olarak ölçülmüştür. UV-vis spektroskopisi ile 400℃'de tavlanan 30 kat kaplı HfO2 ince filmin bant boşluğu 5,06 eV'luk değeri ile en yüksek bant boşluğu elde edilmiştir. Prizma çiftleyici ile 750-850 nm'lik kalınlığa sahip ince filmlerin, kırılma indisinin yaklaşık 2 olduğu saptanmıştır.

Özet (Çeviri)

HfO2 is a suitable candidate dielectric material with high refractive index (~ 2) and high band gap (5.4 eV). Therefore, it is widely used in both optical and microelectronic devices. In this study, microstructure and optical properties of HfO2 thin films fabricated by sol-gel method have been investigated. The solution is formed by dissolving hafnium tetra-chloride in ethanol, and mixing with acetic acid and DI water. Part of the solution was dried in the air and sintered at different temperatures to obtain powders. The solution was filtrered by a micro-filter of 0.45 μm. HfO2 thin films have been deposited on glass substrates as 20, 30 and 40 layers by dip coating. After the deposition, the films were heat treated for 2 minutes. Finally, the films were calcinated at different temperatures for 60 minutes. The powders and the films were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM), ultraviolet-visible spectroscopy (UV-Vis) and prism coupler. XRD results showed that HfO2 powders were amorphous up to 450℃, over that temperature HfO2 powders were in monoclinic phase. On the other hand, XRD results showed that the thin films annealed at 400 and 500 °C were amorphous, while at 600 °C were monoclinic phase. In AFM results, the highest surface roughness value was obtained as 2.260 nm with 40-layered HfO2 thin films annealed at 600 °C. SEM images showed that the thickness of 30-layered HfO2 films was determined around 1 μm. UV- Vis spectrophotometer results showed that the highest optical band gap value was determined as 5,06 eV with the 30-layered HfO2 thin film annealed at 400 °C. In prism coupler analyses, refractive index of HfO2 thin films with thickness between 750-800 nm was obtained as around 2.

Benzer Tezler

  1. Sol-jel yöntemiyle üretilen alüminanın fizikokimyasal özelliklerinin incelenmesi

    Investigation of the physicochemical properties of alumina produced by sol-gel method

    DİLEK CANTÜRK ÖZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Kimya MühendisliğiHitit Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ NİHAN KAYA

  2. Characterization of titanium dioxide thin films prepared by sol-gel processing

    Sol-jel yöntemi ile üretilen TiO2 ince filmlerin karakterizasyonu

    ÖZLEM KAYA

    Yüksek Lisans

    İngilizce

    İngilizce

    2002

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. MACİT ÖZENBAŞ

  3. TM yöntemiyle üretilen AZ91 magnezyum alaşımının sol-jel yöntemiyle Ta2O5 kaplanması ve karakterizasyonu

    Characterization of AZ91 magnesium alloy produced by PM method coated with tantalum oxide by using sol-gel method

    CANSER GÜL

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    BiyomühendislikGazi Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ HENİFİ ÇİNİCİ

  4. (La1-XPrX)0.85Ag0.15MnO3 (0.0 ≤ x ≤ 1.0 ) manganitlerinin yapısal manyetik ve manyetokalorik özelliklerinin araştırılması

    Investigation of structural magnetic and magnetocaloric properties of (La1-XPrX)0.85Ag0.15MnO3 (0.0 ≤ x ≤ 1.0 ) manganites

    ALİ OSMAN AYAŞ

    Doktora

    Türkçe

    Türkçe

    2014

    Fizik ve Fizik MühendisliğiÇukurova Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ. DR. AHMET EKİCİBİL

  5. Vanadium oxide (VOx) thin films elaborated by sol-gel method for microbolometer applications

    Mikrobolometre uygulamarı için sol-gel yöntemiyle hazırlanan Vanadyum oksit (VOx) ince filmler

    KADİR KARSLI

    Yüksek Lisans

    İngilizce

    İngilizce

    2012

    Mühendislik BilimleriOrta Doğu Teknik Üniversitesi

    Mikro ve Nanoteknoloji Ana Bilim Dalı

    PROF. DR. TAYFUN AKIN

    DOÇ. DR. CANER DURUCAN