Vital pulpa tedavisinde kullanılan biyomateryallerin farklı restoratif materyallere bağlanma dayanımının değerlendirilmesi
Evaluation of bond strength of different restorative materials to biomaterials in vital pulp treatment
- Tez No: 525427
- Danışmanlar: PROF. ŞULE BAYRAK
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Biyomateryal, Makaslama Bağlanma Dayanımı, Vital Pulpa Tedavisi, Biyomalzemeler, Dental bonding, Dental materyaller, Dental pulpa, Dental restorasyon, Dental stres analizi, Çocuk diş hekimliği, Biomaterial, Shear Bond Strength, Vital Pulp Treatment, Biomaterials, Dental bonding, Dental materials, Dental pulp, Dental restoration, Dental stress analysis, Pediatric dentistry
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Çocuk Diş Hekimliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Araştırmamızda, vital pulpa tedavilerinde kullanılan kalsiyum silikat içerikli biyomateryallerin farklı restoratif materyallere makaslama bağlanma dayanımının karşılaştırmalı olarak değerlendirilmesi amaçlandı. Materyal ve Metot: 4 mm çapında ve 2 mm derinlikte boşlukları bulunan 208 adet akrilik blok hazırlandı. Üretici firmaların talimatları doğrultusunda hazırlanan kalsiyum silikat içerikli biyomateryaller (ProRoot MTA, BioAggregate, Biodentine ve ThereCal) akrilik bloklardaki boşluklara yerleştirildi ve sertleşmeleri için önerilen sürelerde bekletildi. Biyomateryal örnekleri, uygulanacak restoratif materyale göre rastgele 4 gruba ayrıldı; cam iyonomer siman, rezin modifiye cam iyonomer siman, kompomer ve kompozit rezin. Adeziv işlemlerin ardından biyomateryallerin üzerine 2 mm çapında ve 2 mm yüksekliğinde silindirik kalıplar yardımıyla restoratif materyaller uygulandı. Tüm örnekler 24 saat 37°C'lik etüvde bekletildikten sonra makaslama bağlanma dayanım değerleri universal test cihazı kullanılarak ölçüldü. Elde edilen verilerin istatistiksel değerlendirilmesinde tek yönlü varyans analizi (One-way-ANOVA) ve Tukey testleri kullanıldı. Bulgular: Tüm biyomateryaller için en düşük ortalama makaslama bağlanma dayanım değeri cam iyonomer siman grubunda, en yüksek ortalama makaslama bağlanma dayanım değeri ise Biodentin hariç diğer biyomateryaller için kompomer grubunda gözlendi. TheraCal'in diğer biyomateryallerden istatistiksel olarak daha yüksek ortalama makaslama bağlanma dayanımına sahip olduğu tespit edildi (p<0.05). Biodentine'nin rezin modifiye cam iyonomer siman ve kompozit rezine bağlanma dayanımının ise ProRoot MTA ve BioAggregate'den anlamlı olarak yüksek olduğu saptandı (p<0.05). Sonuç: Sonuç olarak vital pulpa tedavilerinde kullanılan kalsiyum silikat içerikli biyomateryallerin üzerine restoratif materyal olarak rezin bazlı materyaller olan kompomer ve kompozit rezinler tercih edilebilir.
Özet (Çeviri)
Aim: The purpose of this study was to provide a comparative evaluation of the shear bond strengths of calcium silicate‑based biomaterials used in vital pulp treatment to different restorative materials. Materials and Methods: 208 acrylic blocks with a hole measuring 4 mm diameter and 2 mm height were prepared. Calcium silicate‑based biomaterials (ProRoot MTA, BioAggregate, Biodentine and ThereCal) were prepared in line with the manufacturers' instructions, inserted into hole and waited the recommended time for the setting. The biomaterials specimens were divided into 4 groups according to the restorative materials used; glass ionomer cement, resin modified glass ionomer cement, compomer and composite resin. After adhesive procedures, restorative materials were applied over the biomaterials with the help of cylindrical mold (2 mm in diameter and 2 mm in height). All specimens were stored at 37°C for 24 h and shear bond strength was then measured by universal testing machine. Data were analyzed using one-way ANOVA and Tukey tests. Results: The lowest mean shear bond strength values were observed in glass ionomer cement groups for all biomaterials while the highest mean shear bond strength values were observed in compomer groups for other biomaterials specimens except Biodentine. The mean shear bond strength values for TheraCal were significantly higher than the other biomaterials (p<0.05). The mean shear bond strengths of Biodentine to resin modified glass ionomer cement and composite resin were significantly higher than ProRoot MTA ve BioAggregate (p<0.05). Conclusion: In conclusion, resin-based materials such as compomer and composite resin could be preferred as a restorative material upon the calcium silicate‑based biomaterials used in vital pulp treatment.
Benzer Tezler
- Genç daimi dişlerin tedavisinde kullanılan mineral trioksit agregat (MTA) uygulamasının klinik başarısının değerlendirilmesi
Treatment outcomes of mineral trioxide aggregate application in theimmature permanent teeth
AYŞE NUR SADIKOĞLU
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiMarmara ÜniversitesiPedodonti Ana Bilim Dalı
DOÇ. DR. FİGEN EREN GİRAY
DOÇ. DR. IŞIL ÖZGÜL KALYONCU
- Süt dişi pulpa amputasyonlarında kullanılan kanama kriterinin enflamatuar belirteçlerle ilişkisinin incelenmesi
The evaulation of relationship between bleeding criteria and inflamatuar markers used in primary teeth pulp amputation
MERVE KARATAŞ
Doktora
Türkçe
2016
Diş HekimliğiKırıkkale ÜniversitesiPedodonti Ana Bilim Dalı
YRD. DOÇ. VOLKAN ARIKAN
PROF. DR. ŞAZİYE SARI
- Parsiyel amputasyon tedavisinde farklı kalsiyum silikat içerikli ajanların mikrosızıntısının değerlendirilmesi
Evaluation of the micro effects of different calcium silicate containing agents in the treatment of partial amputation
UTKU YASEMİN YILMAZ
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiAnkara ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
PROF. DR. TUĞBA BEZGİN
- Otolog trombositten zengin plazmanın (TZP), direkt pulpa kaplama materyali olarak kullanımının histolojik olarak incelenmesi
Histological investigation of autologous platelet rich plasma as a pulp caping agent
MUSTAFA AYDINBELGE