Robotik lazer kaynak ve plazma ark kaynak yöntemleri ile birleştirilen AISI 410S ferritik paslanmaz çeliğin mekanik, mikroyapı ve kaynak sonrası ısıl işlem özelliklerinin incelenmesi
Investigation of the mechanical, microstructure and post weld heat treatment (PWHT) properties of the AISI 410S ferritic stainless steel joined using robotic laser beam and plasma arc welding methods
- Tez No: 533891
- Danışmanlar: DOÇ. DR. CEYHUN KÖSE
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mekatronik Mühendisliği, Mechanical Engineering, Mechatronics Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Tokat Gaziosmanpaşa Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Mekatronik Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 131
Özet
Paslanmaz çelikler, adı paslanmaz çelik olarak da adlandırılmasa da ilk olarak 1821 yılında Fransız metalurjist Pierre Berthier tarafından demir-krom alaşımının korozyona karşı direncini fark etmiştir. Ancak bu tarihten sonra ısıl işleme tabi tutulması yetersiz olduğu için pratik üretime geçilememiştir. Paslanmaz çeliklerin asıl başlangıcı, 1913 yılında İngiliz metalurjist Harry Brearly tarafından tüfek namlularını geliştirmek için yaptığı araştırmalar sonucu tesadüfen bulmuştur. Daha sonraki yıllarda piyasaya sürülen paslanmaz çelikler, sanayi ve günümüzde önemli bir yer edinmiştir. İlerleyen yıllarda paslanmaz çelikler türlerine ve kalitelerine göre geliştirilmiştir. Bu tez çalışmasında, AISI 410S ferritik paslanmaz çelik levhalar robotik lazer kaynağı ve plazma ark kaynağı yöntemiyle birleştirilmiştir. Birleştirmelerde koruyucu gaz olarak argon kullanılmıştır. Kaynak yatay pozisyonda, ortam sıcaklığında, ilave metal kullanmadan ve alın alına gerçekleştirilmiştir. Robotik lazer kaynağıyla iki farklı güç ve dört farklı hız kullanılarak birleştirme işlemi gerçekleştirilmiştir. Plazma ark kaynağıyla ise, üç farklı plazma ark akımı ve iki farklı hız kullanılarak birleştirme işlemi gerçekleştirilmiştir. Isıl işlemsiz ve kaynak sonrası ısıl işlem uygulanmış kaynaklı birleştirmelerin mekaniksel özellikleri çekme deneyi, üç nokta eğme deneyi ve sertlik ölçümleriyle tespit edilmiştir. Metalografik incelemeler ise stereo makroskop, optik mikroskop, XRD (X Işını Difraktometresi), SEM (Taramalı Elektron Mikroskobu) ve EDS (Enerji Dağılımı Spektrometresi) analizleriyle gerçekleştirilmiştir.
Özet (Çeviri)
Although stainless steels were not called stainless steel, it was first noticed by French metallurgist Pierre Berthier in 1821. But, it was not possible to pass to practical production as the heat treatment was not enough. The main beginning of stainless steels was coincidentally discovered by British metallurgist Harry Brearly in 1913 as a result of his investigations to develop the rifle gun barrels. In the following years, stainless steels, which were introduced to the market, gained an important place in industry and today. In the following years, stainless steels were developed according to their types and qualities. In this thesis study, AISI 410S ferritic stainless steel sheets were joined with robotic laser beam and plasma arc welding method. Argon was used as shielding gas in the joints. The welding was performed without using filler metal on butt weld joint configuration at horizontal position in the ambient temperature. The jointing was carried out by using two different power and four different speeds with the robotic laser beam welding method. In addition, the jointing was carried out by using three different streams and two different speeds with plasma arc welding method. The mechanical properties of laser welded joints without heat treatment and after welding are determined by tensile, three point bending test and hardness measurements. The metallographic investigation was evaluated by an Optical microscope, Stereo- macroscope, Scanning Electron Microscope (SEM), Energy Dispersive X-ray Spectroscopy (EDS) and X-ray Diffraction (XRD).
Benzer Tezler
- Robotik fiber lazer ile kaynak prosesi tasarımı ve parametrelerinin optimizasyonu
Welding process desing and parameter optimization with robotic fiber laser
HÜSEYİN IŞIK
Yüksek Lisans
Türkçe
2013
Elektrik ve Elektronik MühendisliğiMarmara ÜniversitesiMekatronik Mühendisliği Ana Bilim Dalı
PROF. DR. NİHAT AKKUŞ
- HC420LA çelik saclarının lazer (RLW) ve gazaltı (MAG) teknikleri ile kaynaklı birleştirmelerinin mekanik ve metalurjik özelliklerinin incelenmesi
Investigation of the mechanical and metallurgical properties of welded joints of HC420LA steel sheet with laser (RLW) and gas (MAG) techniques
CEMİL KOBAK
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiPamukkale ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. ARZUM IŞITAN
- Farklı özelliklerdeki otomotiv saclarının lazer kaynak uygulamaları
Laser welding applications of automotive sheet with different features
ONUR YÜCE
Yüksek Lisans
Türkçe
2023
Metalurji MühendisliğiKarabük Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
PROF. DR. NİZAMETTİN KAHRAMAN
DR. MEHTAP HIDIROĞLU
- Otomotiv sektöründe robot kaynak uygulaması
Robotic welding applications in automotive industry
HAKAN KESKİN
Yüksek Lisans
Türkçe
2007
Makine MühendisliğiGebze Yüksek Teknoloji EnstitüsüTasarım ve İmalat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. İLYAS KANDEMİR
- Adaptif robotik ark kaynağı yöntemleri: Robotik kaynak ağzı bulma ve kaynak ağzı takibinde deneysel çalışmalar
Adaptive robotic arc welding methods in manufacturing industry: Experimental studies on robotic seam detection and tracking
MUSTAFA YUVALAKLIOĞLU
Yüksek Lisans
Türkçe
2018
Makine MühendisliğiUludağ ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. GÜLTEKİN KARADERE