Geri Dön

Farklı özelliklerdeki otomotiv saclarının lazer kaynak uygulamaları

Laser welding applications of automotive sheet with different features

  1. Tez No: 830674
  2. Yazar: ONUR YÜCE
  3. Danışmanlar: PROF. DR. NİZAMETTİN KAHRAMAN, DR. MEHTAP HIDIROĞLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Otomotiv Mühendisliği, Teknik Eğitim, Metallurgical Engineering, Automotive Engineering, Technical Education
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Karabük Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: İmalat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 140

Özet

Bu çalışmada otomotiv endüstrisinde yaygın olarak kullanılan ve ileri mukavemet özelliklerine sahip DP800(GA), DP800(GI), DP980, 22MnB5 ve TBF1180 malzemelerin lazer kaynak yöntemi ile kaynaklanabilirlikleri araştırılmıştır. Birleştirme işlemlerinde aynı ve farklı kalınlıklara sahip malzemeler kullanılmış, benzer ve benzer olmayan malzemeler kendi aralarında ve birlikte birleştirilmiştir. Kaynak işlemlerinde endüstride yoğunlukla kullanılan fiber lazer kaynak yöntemi tercih edilmiş ve kaynak işlemleri robotik olarak yapılmıştır. Kaynak işlemleri esnasında, malzemelerin distorsiyonunu önlemek için fikstür kullanılmıştır. Kaynak parametrelerinin belirlenmesi için pilot çalışmalar yapılmış ve bulunan en uygun parametreler uygulanmıştır. Birleştirilen numunelerin mekanik özelliklerini belirlemek için çekme ve Erichsen çökertme testleri yapılmıştır. Ayrıca numunelerin kaynak bölgeleri sertlik testi ve mikroyapı incelemeleriyle karakterize edilmiştir. Kaynaklı numuneler gözle muayene edilmiş, hiçbirinde gözle görülebilir bir kaynak hatasına (gözenek, makro çatlak, kaynak kökü hataları vb.) rastlanmamıştır. Mikroyapı incelemelerinde kaynak metalinin ağırlıklı olarak martenzitik yapıda olduğu görülmüştür. Sertlik testlerinde birleştirmelerin birçoğunda genellikle kaynak metalinin sertliğinin diğer bölgeler göre daha yüksek olduğu ve ısı tesiri altında kalan bölgenin (ITAB'ın) temperlenmiş bölgelerinde yumuşak bölgenin (soft zone) bulunduğu tespit edilmiştir. Çekme testleri sonucunda kopmaların bazı birleştirmelerde kaynak metalinden, diğerlerinde ise ITAB ve dayanımı daha düşük olan ana malzemeden gerçekleştiği görülmüştür. Elde edilen çekme test sonuçlarına göre, kaynaklı numunelerin çekme dayanımı açısından verimleri %70-100 olarak hesaplanmıştır. Erichsen çökertme testinde, yırtılmaların kaynak metaline paralel ancak kaynak metalinin dışından (ergime sınırı, ITAB) gerçekleştiği görülmüştür.

Özet (Çeviri)

In this study, the weldability of DP800(GA), DP800(GI), DP980, 22MnB5, and TBF1180 materials, widely used in the automotive industry and have advanced strength properties, were investigated by laser welding. Materials with the same and different thicknesses were used in the joining processes, and similar and dissimilar materials were joined among themselves and together. The fiber laser welding method, widely used in the industry, was preferred in welding processes and performed robotically. During the welding processes, fixtures were used to prevent distortion of the materials. Pilot studies were conducted to determine the welding parameters, and the most suitable parameters were applied. Tensile and Erichsen cupping tests were performed to determine the mechanical properties of the joined samples. In addition, the weld zones of the samples were characterized by hardness tests and microstructure examinations The welded samples were visually examined, and no visible welding defects (pores, macro cracks, weld root defects, etc.) were found. In the microstructure investigations, it was observed that the weld metal was predominantly in martensitic structure. In hardness tests, it has been determined that in many of the joints, the hardness of the weld metal is generally higher than the other regions and that there is a soft zone in the tempered regions of the heat-affected zone (HAZ). As a result of the tensile tests, it was observed that the ruptures occurred from the weld metal in some joints and the base material with lower strength and HAZ in others. According to the tensile test results obtained, the efficiency of the welded samples in terms of tensile strength was calculated as 70-100%. In the Erichsen cupping test, it was observed that the tearing occurred parallel to the weld metal but outside of the weld metal (melting boundary, HAZ).

Benzer Tezler

  1. Soğuk haddelenmiş çift fazlı DP600 kalite çeliklerin yaşlanma davranışının incelenmesi

    Investigation of aging behaviour of cold rolled dual phase DP600 steels

    GÖZDE KARAÇALI

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MURAT BAYDOĞAN

  2. Farklı kalınlıklardaki sacların üretilmesi için sistem geliştirilmesi

    System development for production of different thickness sheets

    OĞUZMERT ŞAHİN

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Makine MühendisliğiYıldız Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. RAHMİ GÜÇLÜ

  3. Bir otomobil fabrikası kaporta departmanı'nda kaynak parametre çalışması

    Welding parameters work in the body shop department in an automobile factory

    UMUT İŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Mühendislik BilimleriUludağ Üniversitesi

    Otomotiv Mühendisliği Ana Bilim Dalı

    DOÇ. DR. RUKİYE ERTAN

  4. Alaşımsız düşük karbonlu çelikten soğuk haddeli sacların kalitesini etkileyen faktörlerin incelenmesi

    Investigation of the factors that are effecting the quality of unalloyed low carbon flat steel sheet

    A. İLHAN TAŞKIRAN

    Doktora

    Türkçe

    Türkçe

    2003

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MÜZEYYEN MARŞOĞLU

  5. AISI301 kalite yay çeliğinin ısıl işlem şartlarının mekanik özelliklerine etkisi

    The effect of AISI301 quality spring steel on mechanical properties of heat treatment conditions

    ŞEYDA BULUT

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Metalurji MühendisliğiDumlupınar Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. VELİ UZ