İzosiyanat ilaveli melamin üre formaldehit (MÜF) tutkalının yongalevha endüstrisinde değerlendirilmesi

The evaluation of melamine urea formaldehyde (MUF) glue inparticleboard industry with isocyanate

  1. Tez No: 578588
  2. Yazar: VOLKAN ÇAVDAR
  3. Danışmanlar: DR. ÖĞR. ÜYESİ HALİL İBRAHİM ŞAHİN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Ormancılık ve Orman Mühendisliği, Forestry and Forest Engineering
  6. Anahtar Kelimeler: Tutkal, Üre formaldehit, Yongalevha, Glue, Particleboard, Urea formaldehyte
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Düzce Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Orman Endüstri Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Odun Mekaniği ve Teknolojisi Bilim Dalı
  13. Sayfa Sayısı: 116

Özet

ÖZET İZOSİYANAT İLAVELİ MELAMİN ÜRE FORMALDEHİT (MÜF) TUTKALININ YONGALEVHA ENDÜSTRİSİNDE DEĞERLENDİRİLMESİ Volkan ÇAVDAR Düzce Üniversitesi Fen Bilimleri Enstitüsü, Orman Endüstri Mühendisliği Anabilim Dalı Yüksek Lisans Tezi Danışman: Dr. Öğr. Üyesi Halil İbrahim ŞAHİN Temmuz 2019, 101 sayfa Gelişen teknoloji ve değişen şartlara işletmelerin uyum sağlaması kaçınılmazdır. İşletmeler levha sektöründe kendini bu gelişime ve değişime ayak uydurması zorunlu hale gelmiştir. Firmalar pazar payını arttırıcı önlemler almakta ve yenilikler yapmaktadır. Kullanım koşullarına uygun levhalar yapmak ve bu levhaları dünya standartlarına uygun hale getirmek için birtakım kimyasallar kullanılmaktadır. Bu kimyasallardan en fazla önem arz edeni PMDI tutkalıdır. Bu çalışmada; izosiyanat ilaveli MÜF tutkalı ile yongalevha üretimi yapılmıştır. Levhaların su alma, kalınlık (şişme) ve formaldehit testleri için istenilen şartlar PMDI tutkalı ile sağlanmaktadır. Bu çalışmada kullanılan odun karışımı %15 ladin, %50 çam, %20 meşe, %10 kapak, %5 talaş kullanılarak 18 mm kalınlıkta üretilen yongalevhalar kullanılmıştır. Levhaların üretiminde MÜF ve PMDI tutkalı kullanılmış olup, yapmış olduğumuz çalışmada MÜF tutkalı ile PMDI tutkallarının değerlendirilmesi yapılmıştır. MÜF tutkalı ve PMDI tutkalı için beş ürün (her ürün için 5 deneme) elde edilmiştir. Yapılan denemelerde PMDI tutkalı %0, 0.5, 0,75, 1, 1.5, 2 oranında kullanılmış olup elde edilen levhaların yoğunluk değeri, rutubet miktarı, su alma oranı, kalınlığına şişme, eğilme direnci, eğilmede elastikiyet modülü değeri, yüzeye dik çekme direnci, yüzey sağlamlığı değeri, vida tutma direnci değerleri belirlenmiştir. Sonuçların değerlendirilmesinde SPSS 18.0 istatistik analiz metodu ile varyans analizleri (ANOVA) yapılmıştır. MÜF tutkalı ile PMDI tutkalının levhalar üzerindeki etkisi varyans analizi ile %95 güven aralığında istatistiksel olarak anlamlı olup olmadığı belirlenmiştir. Farklılık gösteren grup veya grupları belirlemek ve birbirinden farklı ve eşit kabul edilebilecek alt grupları tespit etmek için levha gruplarına ait ortalamalar Duncan Testi ile sorgulanmıştır. MÜF tutkalı ile PMDI tutkalının karşılaştırılması amacıyla Bağımsız T-Testi uygulaması yapılmıştır. Sonuç olarak, üretimi gerçekleştirilmiş olan MÜF ve PMDI ilaveli levhaların tüm fiziksel ve mekanik özelliklerine ait değerler, TS EN 312 (2012) standardında belirtilen P3 tipi (nemli şartlarda kullanılan yük taşıyıcı olmayan levhalar) uygulama alanlarında aranan alt sınır veya üst sınır değerlerini karşıladığı tespit edilmiştir.

Özet (Çeviri)

ABSTRACT THE EVALUATION OF MELAMINE UREA FORMALDEHYDE (MUF) GLUE IN PARTICLEBOARD INDUSTRY WITH ISOCYANATE Volkan CAVDAR Duzce University Graduate School of Natural and Applied Sciences, Department of Wood Mechanics and Technology Master's Thesis Supervisor: Dr. Faculty Member Halil Ibrahim SAHIN July 2019, 101 pages Developing technology and changing conditions are inevitable. Businesses have become obliged to keep up with this development and change in the plate industry. Firms take measures to increase their market share and make innovations. A number of chemicals are used to make plates that are suitable for the conditions of use and to make them suitable for world standards. The most important of these chemicals is PMDI glue. In this study; isocyanate added MUF glue and particleboard production. PMDI glue is used for water intake, thickness (swelling) and formaldehyde tests. The wood mixture used in this study was 15% spruce chip, 50% pine, 20% oak, 10% cover, 5% chip and 18 mm thick were used. In the production of plates, MUF and PMDI adhesives were used. In our study, PMDI adhesives were evaluated with MUF adhesive. Five products (5 trials for each product) were obtained for the MUF glue and PMDI glue. PMDI glue was used in 0%, 0,5, 0.75, 1, 1,5, 2% of the tests, and the density, moisture content, water absorption, thickness swelling, modulus of rupture and modulus of elasticity in bending, internal bond, surface soundness and screw holding performance were tested. Variance analysis (ANOVA) was performed with SPSS 18.0 statistical analysis method. The effect of MUF glue and PMDI glue on the plates was determined to be statistically significant in the 95% confidence interval by the analysis of variance. In order to identify different groups or groups and to identify subgroups that could be considered different and equal, the averages of the plate groups were questioned by the Duncan Test. The Independent T-Test was applied for the comparison of MUF adhesive and PMDI glue. As a result, it has been determined that the values of all physical and mechanical properties of the manufactured MUF and PMDI added particleboard meet the lower limit or upper limit values required in the application areas of P3 type (non-load bearing plates used in humid conditions) specified in TS EN 312 (2012) standard.

Benzer Tezler

  1. Synthesis and characterization of phosphine oxide and sulfone containing polyurethanes

    Fosfin oksit ve sülfon içeren poliüretanların sentezi ve karakterizasyonu

    BETÜL TÜREL

    Doktora

    İngilizce

    İngilizce

    2013

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. İBRAHİM ERSİN SERHATLI

  2. Fenilüre içeren siyanopiridin türevlerinin sentezi

    Synthesis of phenylurea containing cyanopyridine derivatives

    AYŞEGÜL DİNÇER

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    KimyaGaziosmanpaşa Üniversitesi

    Kimya Ana Bilim Dalı

    YRD. DOÇ. DR. MELİHA BURCU GÜRDERE

    YRD. DOÇ. DR. HAYREDDİN GEZEGEN

  3. UV ışınları ile sertleştirilen çeşitli akrilik fimler

    UV-cured ocrylic films

    OYA İNAN

    Yüksek Lisans

    Türkçe

    Türkçe

    1995

    Kimyaİstanbul Teknik Üniversitesi

    PROF.DR. AHMET AKAR

  4. Karaçam (Pinus nigra Arnold.) kabuklarının izolasyon levhası üretiminde değerlendirilmesi

    Evaluation of black pine (Pinus nigra Arnold.) barks in the production of insulation board

    İSMAİL ÖZLÜSOYLU

    Doktora

    Türkçe

    Türkçe

    2022

    Ağaç İşleriBartın Üniversitesi

    Orman Endüstri Mühendisliği Ana Bilim Dalı

    PROF. DR. ABDULLAH İSTEK

  5. Synthesis of reactive polyurethane adhesives and studying the effect of ketonic resins

    Reaktif poliüretan yapıştırıcıların sentezi ve ketonik reçinelerin etkilerinin araştırılması

    SERDAR AYDIN

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Kimyaİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    DOÇ. DR. NESRİN KÖKEN