Küresel grafitli dökme demir malzemelerin tahribatsız ultrasonik muayene yöntemi ile küresellik özelliğinin incelenmesi

Nodularity characterization of spheroidal graphite cast irons by nondestructive ultrasonic method

PDF İndir

  1. Tez No: 581076
  2. Yazar: EREN YALÇINDAĞ
  3. Danışmanlar: DR. ÖĞR. ÜYESİ İSRAFİL KÜÇÜK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Küresel grafitli dökme demir, ultrasonik muayene, ses hızı, darbe-yankı yöntemi, küresellik, Spheroidal graphite cast iron, ultrasonic inspection, sound velocity, pulse - echo method, nodularity
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Bursa Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İleri Teknolojiler Ana Bilim Dalı
  12. Bilim Dalı: Malzeme Bilimi ve Mühendisliği Bilim Dalı
  13. Sayfa Sayısı: 67

Özet

Küresel grafitli dökme demirler (KGDD), son yıllarda dökme demirler ailesinin en çok kullanılan üyelerinden biri olmuştur. KGDD'ler gri ve beyaz dökme demirler gibi geleneksel dökme demirlerin, istenilen özellikleri karşılayamadığı durumlarda devreye girmiş ve ihtiyacı karşılamıştır. Yıllık üretim miktarı artarken yanında başka ihtiyaçlar da ortaya çıkmıştır. Bunlardan biri küresel grafitli dökme demirlerin üretim kalitesinin belirlenmesidir. Küresel grafitli dökme demirlerin üretim kalitesindeki parametrelerden biri de aynı zamanda bu çalışmanın da konusu olan küresellik oranıdır. KGDD'lerin üretiminde önemli bir özellik olan küresellik değerlerinin yüksek oranlarda olması ürünün kabul edilmesi için en önemli kriterdir. Dökümhanelerde KGDD'lerin mikroyapıları mikroskopla incelenerek, küresellik oranları yüzdesel olarak belirlenir. Belli bir değerin altında kalan numuneler reddedilir. Bu çalışmada bu kalite kontrol yöntemine alternatif olarak, tahribatsız ultrasonik muayene yöntemiyle KGDD küreselliklerinin karakterizasyonu amaçlanmıştır. Küresellik oranlarının belirlenmesinde malzemelerin metalürjik özelliklerinden biri olan ses hızı değerlerinden yararlanılmıştır. Ses hızları farklı malzemelerde farklı değerlere sahiptir. Bu hız ultrasonik ses dalgalarının malzeme içerisinde ilerlediği hızdır ve malzeme iç yapısına bağlıdır. Ultrasonik muayene yöntemlerinden biri olan darbe-yankı metodu bu çalışmada ses hızlarının tespitinde kullanıldı. Küresel grafitli dökme demir numuneleri hali hazırda üretimi yapılan dökme demirlerden elde edildi. Bu nedenle farklı kalınlıklara sahip numuneler üzerinden ölçüm alındı. Kısaca, 1018 karbon çeliğinden imal edilmiş kalibrasyon bloğunda kalibre edilmiş ultrasonik ölçüm cihazıyla KGDD numunelerinin kalınlık ölçümü yapılmıştır. Ultrasonik cihazla ölçülen kalınlık değerleri numunelerin gerçek kalınlıklarından farklı çıkmıştır. Kalibrasyon bloğunun ses hızı, ölçülen kalınlık ve gerçek kalınlık değerleri kullanılarak, dökme demir numunelerinin ses hızları hesaplandı. Ölçülen değer ve gerçek kalınlık değeri arasındaki fark ne kadar büyükse küresellik oranları da o yönde düşüş gösterdi. Ölçülen ses hızlarıyla, numunelerin bilgisayar destekli görüntü işleme yazılımlarıyla belirlenen küresellik oranları karşılaştırılmıştır. Ek olarak küresel grafitli olmayan bir dökme demir numunesinden de ses hızı ölçümü alındı. 1018 karbon çeliği kalibrasyon bloğunun, KGDD numunelerinin ve küresel olmayan dökme demirin ses hızları da karşılaştırıldı. Bu karşılaştırmalarda numunelerin ses hızlarıyla küresellik oranları arasındaki ilişki değerlendirilmiş olup uç noktadaki küresellik oranları arasında (yüksek ve çok düşük yüzdeye sahip olanlar) ses hızı farklılıkları görüldü. Çalışmanın sonucunda yüksek ses hızına sahip numunelerin yüksek küresellik oranlarına sahip olduğu sonucuna varıldı. Ek olarak numunelerin mikroyapılarını yakından incelemek için taramalı elektron mikroskopu (SEM) kullanıldı ve numune yüzeyindeki elementlerin yüzdece ağırlıklarını bulmak için enerji dağılım spektroskopisi (EDS) yöntemi kullanıldı.

Özet (Çeviri)

Spheroidal graphite cast iron has become one of the most used members of the cast iron family in recent years. KGDDs have come into play when conventional cast irons such as gray and white cast irons cannot meet the required specifications. While the annual production amount has increased, other needs have also emerged. One of these is the determination of the production quality of spheroidal graphite cast iron. One of the parameters in the production quality of spheroidal graphite cast iron is the nodularity rate which is also the subject of this study. High rates of nodularity, which is an important feature in the production of KGDDs, is the most important criterion for product acceptance. In foundries, microstructure of KGDDs is examined by microscope and nodularity ratios are determined as a percentage. Samples below a certain value are rejected. In this study, as an alternative to this quality control method, it was aimed to characterize KGDD nodularity by using non-destructive ultrasonic inspection method. Sound velocity, which is one of the spesific metallurgical properties of the materials, were investigated to determine the nodularity ratios. This velocity is the speed at which ultrasonic sound waves travel through the material and depends on the material microstructure. One of the ultrasonic ispection methods, pulse-echo method, was used to determine the sound velocities in this study. Samples of spheroidal graphite cast iron were obtained from the cast iron already in mass production process. Therefore, measurements were taken on samples of different thicknesses. Briefly, the thickness of KGDD samples was measured with an ultrasonic measuring device calibrated in a calibration block made of 1018 carbon steel. The thickness values measured by the ultrasonic device were different from the actual thickness of the samples. The sound velocity of the cast iron samples was calculated using the sound velocity of the calibration block, measured thickness and actual thickness values. The larger the difference between the measured thickness value and the actual thickness value, the more the nodularity rate reduced. The measured sound velocities were compared with the nodularity ratios obtained from the manufacturer of the samples, as well as the nodularity ratios determined by computer-aided image processing softwares. In addition, sound velocity measurement was taken from a non-spheroidal graphite cast iron sample. The sound velocities of the 1018 carbon steel calibration block, KGDD samples and non-spherical cast iron were also compared. In these comparisons, the relationship between the sound velocities of the samples and the sphericity ratios was evaluated and the differences in the velocity of sound between the extreme nodularity ratios (those with high and very low percentages) were observed. Because of the study, it was concluded that samples with high sound velocity had high nodularity ratios. In addition, scanning electron microscopy (SEM) was used to closely examine the microstructures of the samples and energy distribution spectroscopy (EDS) method was used to find the percentage weights of the elements on the sample surface.

Benzer Tezler

  1. Tez No

    418961

    Farklı oranlarda silisyum içeren küresel grafitli dökme demirlerin mikro yapılarına çift kademeli östemperlemenin etkisi

    Two stepped austempering's effects on micro structures of spheroidal graphite cast irons consisting of silicium in different rates

    GİZEM GİDER

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MURAT BAYDOĞAN

  2. Tez No

    633753

    Isıya dayanıklı küresel grafitli dökme demir malzemelerin işlenmesinde kesme parametrelerinin yüzey pürüzlülüğü ve işleme gürültüsüne etkileri

    Effect of the machining parameters on surface roughness and machining noise of heat-resistant nodular cast iron materials

    RAMAZAN KARAKUŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    Makine MühendisliğiKırşehir Ahi Evran Üniversitesi

    İleri Teknolojiler Ana Bilim Dalı

    DOÇ. DR. ŞÜKRÜ YILDIZ

  3. Tez No

    605084

    Optimization of alloying and heat treatment process parameters of austempered ductile iron (ADI) castings

    Östemperlenmiş küresel grafitli dökme demirlerde alaşımlama ve ısıl işlem parametrelerinin optimizasyonu

    MUSTAFA ALP YALÇIN

    Yüksek Lisans

    İngilizce

    İngilizce

    2019

    Metalurji MühendisliğiAtılım Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ KEMAL DAVUT

  4. Tez No

    537831

    Effect of austempering and aluminizing processes on properties of high silicon spheroidal graphite ductile irons

    Yüksek silisyumlu küresel grafitli dökme demirlere uygulanan östemperleme ve alüminyumlama işlemlerinin malzeme özelliklerine etkisi

    YAKUP YÜREKTÜRK

    Doktora

    İngilizce

    İngilizce

    2018

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

  5. Tez No

    75553

    GGG 40 sınıfı küresel grafitli dökme demirlerin yorulma davranışına tin kaplamanın etkisi

    Başlık çevirisi yok

    GÖKHAN BAŞMAN

    Yüksek Lisans

    Türkçe

    Türkçe

    1998

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    DOÇ. DR. M. KELAMİ ŞEŞEN

Geri Dön