Farklı rezin matriks seramik bloklarınkalınlıklarının rezin simanlarınpolimerizasyonlarına etkisi
The effect of thickness of different resin matrixceramic blocks on polymerization of resin cements
- Tez No: 607109
- Danışmanlar: DR. ÖĞR. ÜYESİ ERSAN ÇELİK
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Rezin matriks seramik, polimerizasyon, mikrosertlik, Resin matrix ceramic, polymerization, microhardness
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu tez çalışmasının amacı farklı kalınlıklardaki üç farklı rezin matriks seramik blokların, rezin simanın mikrosertliği üzerindeki etkilerinin değerlendirilmesidir. Gereç ve Yöntem: Çalışmamızda; polimer infiltre ceramic (Vita Enamic, Vita Zahnfabrik), rezin nano seramik (Lava Ultimate, 3M ESPE) ve nanoseramik (GC Cerasmart, GC) olmak üzere üç farklı rezin matriks seramik blok değerlendirilmiştir. Her bir seramik bloktan 0,5 mm, 1 mm ve 1,5 mm kalınlıklarında ve 8 mm çapında kesitler alınmıştır ve her bir grupta 10 resin matriks seramik disk içeren 9 grup oluşturulmuştur (n=10). Tranlusent light cure rezin siman (RelyX Veneer; 3 M ESPE) 6 mm çapında ve 0.5 mm yüksekliğindeki paslanmaz çelik kalıba yerleştirilmiştir. Simanın üzerine rezin matriks seramik örnekler yerleştirilmiş ve LED ışık cihazı (Venus VE-215I, Venus Foshan Medical Company) kullanılarak örneklerle temas sağlayacak şekilde 30 sn ışık uygulanmıştır. Vicker's mikrosertlik ölçümleri rezin simanın alt yüzeyinden, 50 g kuvvet 15 sn süresince uygulanarak, her örnek için üç defa ölçüm yapılmıştır. Üç ölçümün ortalaması alınmış ve bu değer örneğin Vicker's mikrosertlik değeri olarak belirlenmiştir. Verilerin analizi için SPSS 20 (SPSS Inc; Chicago, ABD) programı kullanılarak çift yönlü ANOVA ve Tukey çoklu karşılaştırma testleri yapılmıştır. Bulgular: 0,5 mm ve 1 mm kalınlığındaki gruplarda; GC Cerasmart ve Vita Enamic gruplarının Vicker's mikrosertlik değerleri, Lava Ultimate grubuna göre istatistiksel olarak anlamlı düzeyde daha yüksek bulunmuştur (p<0.05). 1,5 mm'lik örneklerde Vita Enamic grubu, Lava Ultimate ve GC Cerasmart gruplarına göre istatistiksel olarak anlamlı düzeyde daha yüksek mikrosertlik değerleri sergilemiştir (p<0.05). Sonuç: Resin matriks seramiğin kalınlığı ve tipi, tüm gruplarda rezin simanın mikrosertlik değerlerini belirgin ölçüde etkilemiştir.
Özet (Çeviri)
Aim: The aim of this study was to evaluate the effects of the different thickness of three types of resin matrix ceramics on microhardness of the underlying light-cured resin cement material. Material and Method: Three types of resin matrix ceramics were analyzed in this study: polymer infiltrated ceramic (Vita Enamic, Vita Zahnfabrik), resin nano ceramic (Lava Ultimate, 3M ESPE) and nano ceramic (GC Cerasmart, GC). Each ceramic block was sectioned 0.5 mm, 1 mm and 1.5 mm thickness with a diameter of 8 mm. The combination of all parameters rendered a total of 9 groups, each containing 10 resin matrix ceramic discs (n = 10). A translucent light-cured luting resin (RelyX Veneer; 3 M ESPE) was applied on a stainless steel with a central hole measuring 6 mm in diameter and 0.5 mm in depth. The resin cements were polymerized through prepared resin matrix ceramic discs for 30 seconds with the LED curing unit held (Venus VE-215I, Venus Foshan Medical Company) in direct contact with the ceramic. Vickers measurements were performed from the bottom of the resin cement samples by 3 different indentation points under a load of 50 g and 15 seconds of indentation time. The average value of the 3 readings for each sample was recorded as the Vickers hardness number. Data were analyzed using two way ANOVA and Tukey post hoc analysis. Results: The mean microhardness of the resin cements for 0.5 mm and 1 mm thickness in the Vita Enamic and GC Cerasmart groups were significantly higher than Lava Ultimate group (p<0.05). The mean microhardness of the resin cements for 1.5 mm thickness in the Lava Ultimate group was significantly lower than Vita Enamic and GC Cerasmart groups (p<0.05). Conclusions: Ceramic thickness and types had significant influences on microhardness values in all types of resin matrix ceramics.
Benzer Tezler
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Testosteron dihidrotestosteron ve östrojenin benign prostat hiperplazisindeki etyolojik rolleri
The roles of testosterone, dihydrotestosterone and estradiole on the etiology of benign prostatic hyperplasia
HALUK TOKUÇOĞLU
- Süt formüllerinin tüketim uygulamaları ve süt formüllerinin C vitamini içeriği ile pH değerleri
Başlık çevirisi yok
GÖNÜL VAROL
Yüksek Lisans
Türkçe
1986
Besin Hijyeni ve Teknolojisiİstanbul ÜniversitesiÇocuk Gelişimi Ana Bilim Dalı
DOÇ. DR. TÜRKAN KUTLUAY
- Türkiye'de aile planlaması çalışmalarında erkeklerin önemi, hastane personeli ile fabrika işçilerinin doğum kontrol yöntemlerine karşı tutum ve davranranışlarında farklılığın araştırılması
Başlık çevirisi yok
KAMİL MALKOÇLU
Yüksek Lisans
Türkçe
1987
Demografiİstanbul ÜniversitesiAile Sağlığı Ana Bilim Dalı
DOÇ. DR. DERİN KÖSEBAY