Cam matriks ve rezin matriks seramik materyallerine termal yaşlandırma işleminin etkisi: Bükülme dayanımı, mikrosertlik değerlendirmesi
Effect of thermal aging on glass matrix ceramic and resin matrix materials: Flexural strength and microhardness evaluation
- Tez No: 960063
- Danışmanlar: DOÇ. DR. ERKUT KAHRAMANOĞLU
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Biyomedikal ve dental materyaller, Cam seramikler, Eğilme dayanımı, Mikrosertlik, Protetik diş tedavisi, Flexural strength, cad/cam, elastic modulus, lithium disilicate, microhardness, Biomedical and dental materials, Glass ceramics, Bending strength, Prosthetic dental treatment
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmanın amacı, farklı matriks yapısına sahip 7 farklı cam matriks seramik (Amber Mill, Hassbio, Kore; LiSi, GC, Japonya; Celtro Duo, Dentsply Sirona, Almanya; Tessera, Dentpsly Sirona, Almanya; IPS e.max CAD, Ivoclar, Liechtenstein) ve rezin matriks (Cerasmart, GC, Japonya; Grandio Blocs, VOCO, Almanya) CAD/CAM materyallerinin bükülme dayanımı, elastik modül, mikrosertlik değerlerini kıyaslamak, 50.000 termosiklus ile yaşlandırma sonrası farklılıkları değerlendirmektir. Gereç ve Yöntem: Tüm CAD/CAM bloklardan üç nokta bükülme testi için bar şeklinde çubuk (1.2 x 4 x 14 mm) ve yüzey mikrosertlik ölçümleri için ise dikdörtgen (2 mm kalınlığında) şeklinde su altında hassas kesim cihazı (Isomet1000, Buehler, ABD) ile toplam 210 örnek elde edildi. Örneklerin yarısı 50.000 döngü ile 5-55C arasında termal döngü cihazı (SD Mechatronik, Almanya) kullanılarak yaşlandırıldı, diğer yarısı ise 24 saat boyunca 37C distile suda bekletildi. 3 nokta bükülme üniversal test cihazı (AG-X 5kN, Shimadzu, Japonya) kullanılarak gerçekleştirildi, bükülme dayanımı (FS) ve elastik modülüs (EM) hesaplandı. Mikrosertlik ölçümleri (n=5) tamamlandı (Microhardness Tester HMV-2, Shimadzu, Japan) ve Vicker's mikrosertlik (VHN) değerleri hesaplandı. İstatistiksel analiz için Kruskal-Wallis and Mann-Whitney U testleri kullanıldı, önem düzeyi p<0,05 alındı. Bulgular: Tessera, 24 saat sonra incelenen malzemeler arasında FS (570 MPa), EM (66,2 GPa) ve VHN (717,7) için en yüksek medyan değerlerine sahipken, Cerasmart (FS:260; EM:12,8 ve VHN:99,9) sırasıyla en düşük değerleri sergilemiştir. Hem 24 saat sonra hem de termal yaşlandırma sonrasında FS, EM ve VHN için malzemeler arasında anlamlı bir fark bulunmuştur (p<0.001). Aynı zamanda, termal yaşlandırmanın ardından tüm malzemeler için FS değerlerinde istatistiksel olarak anlamlı bir düşüş olmuştur (p<0.05). Sonuç: Tedavi prosedürü için en uygun CAD/CAM malzemesini seçerken mekanik özellikleri, malzemeler arasındaki farkları ve yaşlanma sürecinden kaynaklanan potansiyel değişiklikleri göz önünde bulundurmak önemlidir.
Özet (Çeviri)
Objective: The aim of this in vitro study was to examine matrix glass matrix ceramics (Amber Mill, Hassbio, Korea; LiSi, GC, Japan; Celtro Duo, Dentsply Sirona, Germany; Tessera, Dentsly Sirona, Germany; IPS e.max CAD, Ivoclar, Liechtenstein) and resin matrix (Cerasmart, GC, Japan; Grandio Blocs, VOCO, Germany) 7 different blocks to compare the flexural strength, elastic modulus, resilience, surface Vicker's microhardness values and evaluate of the differences after aging with 24 hours and 50.000 thermocycles. Materials and Methods: Bar-shape samples (1.2 x 4 x 14 mm) for the three-point bending test and rectangular (2 mm thickness) samples for the Vicker's microhardness test, were prepared with a precision cutting device Isomet1000, Buehler, ABD) under water. Half of the samples were aged for 50.000 cycles between 5-55°C using a thermal cycle device (SD Mechatronik, Germany), and the other half were kept in distilled water at 37°C for 24 hours. Three-point bending test (n=10) was performed using a universal testing machine (AG-X 5kN, Shimadzu, Japan) according to ISO 6872:2015. Flexural strength (FS), elastic modulus (EM), resilience (R) values were calculated. Surface microhardness measurements (n=5) were completed (Microhardness Tester HMV-2, Shimadzu, Japan) by 5 repeats from each sample, and Vicker's microhardness (VHN) values were calculated. Kruskal-Wallis and Mann-Whitney U tests were used for statistical analysis, significance level was set at p<0.05. Results: Tessera had the highest median values for FS (570 MPa), EM (66.2 GPa), and VHN (717.7) among the materials under consideration after 24 hours, while Cerasmart (FS:260; EM:12.8, and VHN:99.9) exhibited the lowest values, respectively. A significant difference was found between the materials for FS, EM, and VHN both after 24 hours and after thermal aging (p<0.001). Concurrently, there was a statistically significant decrease in FS values for all materials following thermal aging (p<0.05). Conclusion: It is crucial to take into account the mechanical properties, the distinctions between materials, and the potential modifications resulting from the aging process when selecting the most appropriate CAD/CAM material for the treatment procedure.
Benzer Tezler
- Farklı yüzey işlemleri uygulanan seramiklerin termal yaşlandırma sonrası bağlanma dayanımının değerlendirilmesi
Effects of surface treatments on the SHEAR bond strength of ceramics after thermal aging
GÖZDE YALÇIN ÇETİN
- Rezin siman ile rezin matriks CAD/CAM restoratif materyaller arasındaki uzun dönem bağlanma dayanımının yapay yaşlandırma işlemleri ile değerlendirilmesi
Long-term durability of the bond strength of resin-matrix CAD/CAM ceramics to resin cement in conjunction with artificial aging
ZÜHRE AŞICIOĞLU ÇAĞLAYAN
- Farklı CAD/CAM blokların rezin kompozitlerle tamiri
Repair of different CAD/CAM blocks with resin composites
ÖZGE ÇAY
- Çeşitli yüzey işlemleri uygulanan Rezin Matriks seramiklerin rezin siman kullanılarak dişe bağlantılarının in-vitro olarak incelenmesi
In-vitro evaluation of shear bond strength of Resin Matrixceramics with different surface treatment methods
ELİF MELİKE AKARCA
Diş Hekimliği Uzmanlık
Türkçe
2019
Hacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
Yükleniyor...
- CAD/CAM sistemlerinde kullanılan 4 farklı seramik materyalin kompozit rezin ve kendinden adeziv rezin siman ile yapıştırılması takiben termal yaşlandırma işlemi öncesi ve sonrası bağlanma dayanımları karşılaştırılması
Comparison of binding strengths before and after the thermal ageing process following the bonding of 4 different ceramic materials used in CAD/CAM systems with composite resin and self-adhesive resin cement
MURAT ŞENOL
Diş Hekimliği Uzmanlık
Türkçe
2022
Ankara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
Yükleniyor...