CAD-CAM tam seramik materyallerin renk, translusensi ve pürüzlülükleri üzerine polisaj ve glaze ışlemlerinin etkisinin değerlendirilmesi
Evaluation of the effect of polishing and glaze techniques on the color, translucency and surface roughness of CAD-CAM all-ceramic materials
- Tez No: 624208
- Danışmanlar: DOÇ. DR. SÜLEYMAN CUMHUR ALTINTAŞ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Dental materyaller, Dental porselen, Diş renk değişikliği, Sır, Yüzey pürüzlülüğü, CAD/CAM, Dental materials, Dental porcelain, Tooth discoloration, Glaze, Surface roughness
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Hacettepe Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı; farklı yüzey bitirme işlemleri (Glaze: G ve Polisaj: P) uygulanmış LDS (Lityum disilikat), ZLS (Zirkonya ile güçlendirilmiş lityumsilikat) ve TrZ (translusens zirkonya) materyallerinin translusensi, renk ve pürüzlülüklerinin kahve termal siklusu öncesi ve sonrası in-vitro değerlendirilmesidir. Lityum disilikat (IPS e.max CAD), zirkonya ile güçlendirilmiş lityum silikat (Celtra Duo HT) ve translusens zirkonya (Cercon HT) materyallerinden 40'ar adet (1 mm kalınlığında) örnek hazırlanmıştır. Klinik aşındırmayı taklit etmek amacıyla 20 sn aşındırma işlemi uygulanmıştır. Örneklere iki farklı yüzey işlemi uygulanmış ve bir kahve çözeltisinde 10.000 termalsiklusa tabi tutulmuştur. Örneklerin pürüzlülük değerlerini (Ra: Ortalama Pürüzlülük Değeri, Rz: Ortalama Maksimum Profil Yüksekliği) ölçmek için kontakt profilometre, renk stabilitelerini ve translusensi parametrelerini (TP) ölçmek için kolorimetre cihazı kullanılmıştır. Renk farkı verileri Kruskal Wallis testi ile değerlendirilmiş, grupların farklılık gösterdiği durumda Dunnet çoklu karşılaştırma testi kullanılmıştır. Aşındırma sonrası pürüzlülük verilerinin değerlendirilmesinde tek yönlü varyans analizi (ANOVA) kullanılmıştır. Pürüzlülük ve translusensi parametresi (TP) verilerinin değerlendirilmesinde tekrarlı ölçümlerde varyans analizi ve Duncan çoklu karşılaştırma testi uygulanmıştır. p<0.05 istatistiksel olarak anlamlı kabul edilmiştir. Renk değişimi sadece polisaj uygulanmış ZLS (ZLS-P) grubunda klinik olarak algılanabilir eşiğin üstünde olup, tüm gruplarda klinik olarak kabul edilebilir eşiğin altındadır (<2.23). Aşındırma sonrası en yüksek pürüzlülük değerleri (Ra ve Rz) ZLS materyalinde görülmüş, bunu LDS ve TrZ takip etmiştir. Glaze uygulanmış ZLS (ZLS-G) ve LDS (LDS-G) gruplarının ortalama pürüzlülük değerleri (Ra) polisaj uygulanan gruplara kıyasla daha düşük olmasına karşın bu fark istatistiksel olarak anlamlı bulunmamıştır. Glaze uygulanmış TrZ (TrZ-G) grubu, polisaj uygulanan (TrZ-P) gruba kıyasla istatistiksel olarak anlamlı olacak düzeyde daha yüksek bir Ra değeri göstermiştir. Rz (Ortalama Maksimum Profil Yüksekliği) parametresi açısından ise tüm materyallerde glaze uygulaması daha düşük değerler görülmesini sağlamışken, bu fark TrZ grubunda istatistiksel farka sebep olmamıştır. Termal siklus öncesi ve sonrası en yüksek translusensi değeri LDS materyalinde görülmüş, bunu ZLS ve TrZ takip etmiştir. Kahve termal siklusu materyallerin pürüzlülük değerlerinde (Ra, Rz) artışa, translusensilerinde ise azalmaya sebep olmuştur.
Özet (Çeviri)
The purpose of this study is to evaluate the influence of different surface treatments (Glaze: G and Polishing: P) on the translucency, color stability and surface roughness of LDS (Lithium disilicate), ZLS (Zirconia reinforced lithium silicate) and TrZ (translucent zirconia) materials. 40 specimens (1 mm thickness) discs were prepared from lithium disilicate (IPS e.max CAD), zirconia reinforced lithium silicate (Celtra Duo HT) and translucent zirconia (Cercon HT) materials. Specimens were grinded in order to mimic the chairside-adjustment process for 20 seconds. Two different types of surface treatments were applied to the specimens and the specimens were subjected to 10.000 thermocycles in a coffee solution. Contact profilometer was used to measure the roughness values (Ra: Average Roughness Value, Rz: Maximum Height of Profile), and colorimeter was used to measure color stability and translucency parameters (TP). Color difference data were evaluated with Kruskal Wallis test and Dunnet multiple comparison test. One-way variance analysis (ANOVA) was used to evaluate the roughness data after grinding. Repeated measures ANOVA and Duncan multiple comparison test was used to evaluate the roughness (Ra, Rz) and translucency parameter (TP) data. p<0.05 was considered significant. Only the ZLS-P (Zirconia reinforced Lithiumsilicate-polishing) group's color differences was perceptible but the color differences values of all groups were smaller than the clinically acceptability threshold (<2.23). The highest roughness values (Ra and Rz) were observed in the ZLS material after grinding, followed by LDS and TrZ. ZLS-G (Zirconia reinforced Lithiumsilicate-glaze) and LDS-G (Lithium disilicate-glaze) groups showed the lower mean value Ra than polished groups, which showed no statistically significant difference among them. TrZ-G (Translucent Zirconia-glaze) group showed a significantly higher Ra value compared to TrZ-P (Translucent Zirconia-polishing) group. For all materials, glazing provided lower Rz (Maximum Height of Profile) value, but for TRZ no significant differences were found between the Rz values of glazed and polished surfaces. Before and after coffee thermocycling, LDS presented the highest TP values, followed by ZLS and TrZ. The coffee thermocycling increased the roughness values (Ra and Rz) and decreased the translucency of materials
Benzer Tezler
- Yeni nesil farklı ışık geçirgenliğine sahip tam kristalize CAD/CAM seramik materyallerin farklı yüzey bitirme işlemi ve yaşlandırma sonrası yüzey pürüzlülüğü, ışık geçirgenliği ve renk değişiminin in vitro değerlendirilmesi
In vitro evaluation of surface roughness, light transmission and color change after different surface finishing and aging of new generation fully crystallized CAD/CAM ceramic materials with di̇fferent light transmi̇ttance
BAŞAK TIMARCIOĞLU
Doktora
Türkçe
2024
Diş HekimliğiSağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CUMHUR KORKMAZ
- Farklı ağız gargaralarının güncel CAD/CAM materyallerinin optik özellikleri üzerine etkilerinin incelenmesi
Investigation of the effects of different mouthwashes on the optical properties of current CAD/CAM materials
GÖZDE YAVUZKILIÇ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GÖZLEM CEYLAN
- Yapay yaşlandırmanın farklı sinterizasyon derecelerindeki monolitik zirkonya materyallerinin translusensisi üzerine etkisi
The effect of artificial aging on translusency of monolithic zirconia materials in different sinterization degrees
BURCU KANPALTA
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ÖZLEM KARA
- Farklı CAD-CAM seramik materyallerin kalınlıklarının ölçüm yapılan arka zemin tipine göre maskeleme yeteneğine etkisi ve yarı saydamlığın değerlendirilmesi
Effect of thickness of different CAD-CAM ceramic materials on masking ability according of the measured background TYPE and evaluation of translucency
TANSU BURSALI
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. İSA YÖNDEM
- Farklı CAD/CAM seramik materyallerinin yaşlandırma işlemi sonrası renk özelliklerinin/stabilitelerinin incelenmesi
Investigation of color properties/stability of different CAD/CAM ceramic materials after aging process
SEÇKİN GÜL
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiDicle ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SABİHA ZELAL ÜLKÜ