Bulk fill kompozit rezinlerin farklı tabaka kalınlıklarında ve farklı ışık güçlerinde polimerize edilmesinin kompozitin dönüşüm derecesi, mikro sertliği ve sitotoksisitesine etkisi
Effect of polymerization of bulk fill composite resins in different layer thicknesses and light irradiance on the degree of conversion, micro hardness and cytotoxicity of the composite
- Tez No: 629468
- Danışmanlar: DR. ÖĞR. ÜYESİ AYŞE DÜNDAR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental restorasyon, Kompozit malzemeler, Kompozit reçineler, Mikrosertlik, Sitotoksisite, Dental restoration, Composite materials, Composite resins, Microhardness, Cytotoxicity
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Akdeniz Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı bulk fill kompozit rezinlerin farklı kalınlıklarda ve farklı ışık gücü modlarında polimerize edilmesinin kompozitlerin dönüşüm derecesi, mikro sertlik ve sitotoksisiteleri üzerindeki etkilerini değerlendirmektedir. Gereç ve Yöntem: Bu çalışma deneysel bir araştırma olup, bu çalışmada Sonic Fill 2 (SF), Filtek Bulk Fill (FBF) isimli iki farklı bulk fill kompozit rezin kullanıldı. Her iki kompozitten 5 mm çapında 2, 4 ve 6 mm kalınlıkta hazırlanan örnekler 2 farklı güç modunda (1000mW/cm2-20 sn ve 3200 mW/cm2- 3sn) polimerize edilerek her grupta 5 numune olacak şekilde dönüşüm derecesi, mikro sertlik ve sitotoksisite analizleri için toplamda 180 adet örnek elde edildi. Dönüşüm derecesi, Fourier Transform Infrared Spektrometre ile, mikro sertlik ölçümü Vickers sertlik ölçüm cihazıyla örneklerin alt ve üst yüzeylerinden yapılmıştır. Sitotoksisite, WST-1 testiyle fibroblast hücreleri (L929) kullanılarak 1,7 ve 21. günlerde analiz edilmiştir. SPSS 22 paket programı ile elde edilen verilerin istatistiksel analizi yapılmıştır. Bulgular: Bulk fill kompozit rezinlerin tabaka kalınlığı arttıkça kompozitlerin alt yüzeylerinde dönüşüm dereceleri anlamlı derecede azalmıştır (p<0,05). Sadece FBF 4 mm ve 6 mm kalınlığındaki örnekler arasında istatistiksel olarak anlamlı fark bulunmamaktadır. Bulk fill kompozit rezinlerin alt üst yüzey mikro sertlik oranları incelendiğinde her iki kompozitin her iki polimerizasyon yöntemiyle polimerize edilen 2 mm kalınlığında hazırlanan örnekleri ve standart güç modunda polimerize edilen 4 mm kalınlığındaki örnekleri 0,80 kabul edilebilir eşik değeri geçmiştir. WST-1 testinin sonuçlarına göre; en yüksek hücre canlılığı 7. günde Sonic Fill 2 kompozit rezinin standart güç modunda polimerize edilen 2 mm kalınlıktaki örneğinde görülmüştür. WST-1 deneyinin sonuçlarına göre; bulk fill kompozitlerin tabaka kalınlığı arttıkça hücre canlılığı azalmıştır. Sonuç: Bulk fill kompozit rezinler uygulama kolaylığı ve zaman tasarrufu sağlasa da artan tabaka kalınlığına bağlı yetersiz fiziksel ve mekanik özelliklere sahip olabilir ve sitotoksik etkiler gösterebilir.
Özet (Çeviri)
Purpose: The aim of this study is to evaluate the effects of polymerization of bulk fill composite resins in different layer thicknesses and different light power modes on the degree of conversion, micro hardness and cytotoxicity of composites. Materials and Methods: This study is an experimental study and two different bulk fill composite resins named Sonic Fill (SF) and Filtek Bulk Fill (FBF) were used in this study. A total of 180 composite samples with 5 mm diameter, 2, 4 and 6 mm thicknesses and polimerized with 2 different power modes (1000mW/cm2-20 sn and 3200 mW/cm2- 3sn) were prepared for the degree of conversion, micro hardness and cytotoxicity analaysis. The degree of conversion was measured with Fourier Transform Infrared Spectrometry, micro hardness measurement with the Vickers hardness tester from the lower and upper surfaces of the samples. Cytotoxicity was measured on days 1,7 and 21 using fibroblast cells (L929) with the WST-1 test. Statistical analysis of the data obtained was made with SPSS 22 program. Results: As the layer thickness of bulk fill composite resins increased, the degree of transformation in the lower surfaces of the composites were decreased significantly(p<0,05). There were no statistically significant difference except FBF 4 mm and 6 mm thickness samples. When the upper and lower surface micro hardness ratios of Bulk fill composite resins were examined, samples of both composites prepared in 2 mm thickness polymerized by both polymerization methods and 4 mm thickness samples polymerized in standard power mode have exceeded the acceptable threshold value of 0.80. According to the results of the WST-1 test; on the 7th day, the highest cell viability was seen in the 2 mm thick sample of Sonic Fill 2 composite resin polymerized in standard power mode. According to the results of WST-1 experiment; as the layer thickness of bulk fill composites increased, cell viability decreased. Conclusions: Although bulk fill composite resins provide ease of application and time savings, they may have insufficient physical and mechanical properties due to increased layer thickness and may show cytotoxic effects.
Benzer Tezler
- Halojen ve led ile polimerize edilmiş bulk fill kompozit rezinlerin dönüşüm derecesi ve mikrosertlik değerlerinin karşılaştırmalı olarak incelenmesi
Comparative analysis of conversion degrees and microhardness values of bulk fill composite resins polymerized with different light devices
MERVE KÜTÜK
Diş Hekimliği Uzmanlık
Türkçe
2018
Ondokuz Mayıs ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
Yükleniyor...
- Farklı yöntemlerle hazırlanan üç farklı kompozit rezinin dentine bağlanma dayanımlarının in vitro değerlendirilmesi
Evaluation of the shear bond strength of three different composite resins to dentin which using different methods:in vitro
ALPEREN MURAT YALNIZ
Diş Hekimliği Uzmanlık
Türkçe
2020
Ankara ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
Yükleniyor...
- Süt dişlerinde farklı viskozitelere sahip bulk fill kompozit rezinlerin marjinal adaptasyonunun mikro bilgisayarlı tomografi ile değerlendirilmesi
Evaluation of the marginal adaptation of bulk-fill composite resins with different viscosities i̇n primary teeth using microcomputed tomography
ECEM KARAKAŞ
- Süt molar dişlerin mod kavitelerinde farklı tip kompozit rezinlerin stres dağılımlarının incelenmesi
Investigation of stress distribution of different types of composite resinsin mod cavities of primary molar teeth
SELİN ACAR
- Shear bond strenght of three bulk-fill composites and conventional composites restorative material to dentine : In-vitro
Bulk fill kompozit rezinler ve geleneksel kompozit rezinlerin dentine bağlanma dayanimlarinin in vitro değerlendirilmesi
AHMED NOUHA
Yüksek Lisans
İngilizce
2014
Yeditepe ÜniversitesiRestoratif Diş Tedavisi ve Endodonti Ana Bilim Dalı
Yükleniyor...