Alüminyum siyah drossundan hidrometalurjik ve pirometalurjik yöntemler ile Al2O3 esaslı seramiklerin üretiminin araştırılması
Investigation of Al2O3-based ceramic production from aluminium black dross through hydrometallurgical and pyrometallurgical operations
- Tez No: 635567
- Danışmanlar: DR. ÖĞR. ÜYESİ AHMET TURAN
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Metalurji Mühendisliği, Seramik Mühendisliği, Chemical Engineering, Metallurgical Engineering, Ceramic Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Yalova Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya ve Süreç Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Kimya ve Süreç Mühendisliği Bilim Dalı
- Sayfa Sayısı: 95
Özet
Alüminyum drossu (curuf), ergitme, ergimiş metalin transferi ve rafinasyonu süreçlerinde alüminyumun oksijene olan yüksek ilgisinden dolayı oluşmaktadır. Dross, metalik ya da metalik olmayan bileşenler içermektedir ve siyah/beyaz olarak sınıflandırılmaktadır. Beyaz dross, yüksek metalik alüminyum içeriğine sahipken siyah dross düşük metalik alüminyum içeriğine sahiptir. Bu çalışmada, pirometalurjik ve hidrometalurjik işlemlerle siyah drossun değerlendirilmesi için optimum koşulların belirlenmesi amaçlanmıştır. Deneysel çalışmaların ilk aşamasında, halojenür esaslı safsızlıkları buharlaştırma yoluyla gidermek ve metalik alüminyum içeriğini Al2O3'e dönüştürmek için siyah dross beş farklı sıcaklıkta kalsine edilmiştir. Çalışmaların ikinci aşamasında, orijinal ve kalsine dross, mümkün olduğunca saf alümina esaslı seramik elde edebilmek için farklı reaktiflerle liç edilmiştir. Liç deneylerindeki amaç, empüritelerin çözeltiye alınarak liç deneylerinde kullanılan asitlerin içerisinde çözünürlüğü bulunmayan alüminanın filtre kekinde kalıp saflaştırılmasıdır. 1100 °C'de 60 dk. boyunca kalsine edilmiş drossun 10 mL H2SO4 ve 40 mL distile sudan oluşan çözelti içerisinde liç edilmesi ile gerçekleştirilmiş çalışmadan elde edilen alümina esaslı seramik tozları, 600 MPa tek eksenli basınç altında preslenmiş ve refrakter malzeme olarak kullanılabilirliğin görmek için argon atmosferi altında 1550 °C'ye kadar artan sıcaklıklarda 60 dk. süre ile sinterlenmiştir. Hammaddeleri, üretilen seramik tozlarını ve sinterlenmiş seramikleri karakterize etmek için XRD, XRF, kimyasal analiz, TGA, Vickers sertlik ölçümü ve Archimedes yoğunluk ölçümü teknikleri kullanılmıştır.
Özet (Çeviri)
Aluminium dross arises due to the high interest of aluminium to oxygen during melting, molten metal transfer and refining processes. The dross consists of metallic or non-metallic components depending on the charge. It can be classified as black and white. White dross has high metallic aluminium content whilst the black dross has low metallic aluminium content. In this study, it was aimed to determine the optimum conditions for the evaluation of black dross with pyrometallurgical and hydrometallurgical processes such as calcination and leaching. In the first stage of the experimental studies, the black dross was calcined at five different temperatures to remove halide-based impurities by evaporation and to convert the metallic aluminium content to Al2O3. In the second stage, original and calcined black dross samples were leached with different reagents to obtain an alumina-based ceramic as pure as possible. The purpose of leaching experiments is to extract the impurities out and to purify the alumina-based ceramics in calcination products as filter cake because the alumina does not have solubility in the acids which are used in leaching experiments. Calcined black dross, which was calcined at 1100 °C for 60 minutes, was leached in a solution of 10 mL H2SO4 and 40 mL distilled water. Obtained alumina-based ceramic powders were pressed under 600 MPa uniaxial pressure and were sintered under argon atmosphere for 60 minutes at increasing temperatures up to 1550 °C to see the use of the produced powder as refractory material. XRD, XRF, chemical analysis, TGA, Vickers hardness measurement and Archimedes density techniques were used to characterize raw materials, ceramic powders and sintered ceramics.
Benzer Tezler
- Alüminyum siyah curuflarındaki alüminyumun ve bileşiklerinin hidro ve pirometalurjik yöntemler ile geri kazanılması
Recovery of aluminium and its compounds with hydro and pyrometalurgical methods from aluminium black dross
OSMAN HALİL ÇELİK
Yüksek Lisans
Türkçe
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ONURALP YÜCEL
- Siyah çayın alüminyum içeriği
Aluminium content of black tea
ZARİFE ÖZDEMİR YAĞCI
Yüksek Lisans
Türkçe
2017
Gıda MühendisliğiOndokuz Mayıs ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
DOÇ. DR. İLKAY KOCA
- Alüminyum beyaz droslarının pirometalurjik değerlendirilmesi
Pyrometallurgical evaluation of aluminum white dross
HASAN GÜNEY
Yüksek Lisans
Türkçe
2024
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ONURALP YÜCEL
- Kurutmada konik yoğunlaştırıcılı bir güneş enerjisi sisteminin kullanılması
The Use of a solar energy system with conical concentrator in drying
İNCİ TOĞRUL
Doktora
Türkçe
2001
Kimya MühendisliğiFırat ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. DURSUN PEHLİVAN
YRD. DOÇ. DR. CEVDET AKOSMAN
- Siyah çayın işlenmesi aşamalarında bakır, demir, çinko, mangan ve alüminyum bulaşması
Contamination of copper, Iron, Zinc, Manganese and Aluminium during the process of the black tea
A.CİHAT KÜTÜK