Farklı yapı ve kalınlıklardaki CAD-CAM blokların yüzey ve optik özelliklerinin incelenmesi

Investigation of surface and optical properties of CAD-CAM blocks in different structures and thicknesses

  1. Tez No: 671231
  2. Yazar: LENA ALMASIFAR
  3. Danışmanlar: DOÇ. DR. NİHAN GÖNÜLOL
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2021
  8. Dil: Türkçe
  9. Üniversite: Ondokuz Mayıs Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 87

Özet

Amaç: Bu çalışmada farklı yapılardaki CAD/CAM blokların Ultraviole yaşlandırma sonrası renk stabilitesi ve optik özellikleri incelenmiştir. Materyal ve Metot: Çalışmamızda 5 farklı (4 hibrit ve 1 feldspatik) CAD-CAM materyal kullanılmıştır. Her materyalden 40 adet numune elde edilmiştir. Numuneler su soğutması altında elmas disk ile kesme makinasında iki farklı kalınlıkta (20 adet 0,7 mm ve 20 adet 1,2 mm) kesildip ve toplam (200) numune hazırlanmıştır. Yüzey standardizasyonu için numunelerin bir yüzleri P600, P1200, P2000' lik silikon karbit kağıtlar ile zımparalandı. Tüm numuneler yüzey polisajına tabi tutuldu. Her gruptaki numuneler, iki farklı simantasyon yöntemi için ikiye ayrılıp (10 numune dual cure ve 10 numune light cure) ve numuneler ultrasonik temizleme cihazı ile 10 dk temizlenip 3 dakika distile suda bekletildi. Hibrit blokların arka yüzeyleri simantasyon öncesi, 50-µm' lik AL₂O₃, tozu kullanılarak 0,15 MPa basınç ile kumlanıp ve cam seramik bloklar, %9 HF asit (60 sn) ile pürüzlendirildi. Seramik primer 60 sn tüm numunelere uygulandı. Light cure (LC) ve dual cure (DC) rezin Siman kalınlığı yaklaşık 0.15 mm olacak şekilde numunelere sürülüp daha önceden hazırlanmış levhalara bastırıldı. Numuneler polimerizasyon için kullanılan LED cihazı 1200mW/cm₂ ile klinik şartlarını taklit etmek için 1 dk numunelerin dış yüzey tarafından polimerize edildi. Numunelerin son kalınlıkları dijital kumpas ile kontrol edildi. Daha sonra numunelerin ilk renk ve translüsensi ölçümü spektrofotometre cihazı ile yapıldı. Daha sonra sonra numuneler UV yaşlandırma cihazında 300 saat, toplam 150 KJ/m² enerjiye maruz bırakıldı. Ikinci renk ve translüsensi ölçümü U.V. yaşlandırma sonrası CIEDE2000 sistemine göre hesaplandı. Veriler IBM SPSS V23 ile analiz edilmiştir. Bulgular: Materyallerin yapısı renk ve translüsensi üzerinde belirgin etki göstermiştir. Gruplar arasındaki en az renk değişimini feldspat seramik yapıda olan CEREC gösterirken en yüksek renk değişimini rezin nano seramik yapıda olan Lava Ultimate göstermiştir (p

Özet (Çeviri)

Aim: The purpose of this invitro study is to evaluate color stability and optical properties of CAD / CAM blocks with different structures after U.V. aging. Materyal and Methods: A total 200 specimens were prepared from, 5 different (4 hybrid and 1 feldspathic) CAD-CAM materials. 40 samples were obtained from each material. The samples were sectioned into two different thicknesses (20 pieces of 0,7 mm and 20 pieces of 1,2 mm) with a diamond disc cutting machine under cooling water. Surface of samples were standardized by silicon carbide papers (P600, P1200, P2000 Grit) under water cooling. All samples were subjected to surface polishing. After test samples were ultrasonically cleaned for 10 minutes and kept in distilled water for 3 minutes. Samples were divided into groups for dual cure and light cure cementation techniques. The hybrid blocks were sandblasted with 50-µm AL₂O₃, particles with 0.15 MPa pressure, and the glass ceramic blocks were etched with 9% HF acid, Ceramic primer applied to all samples for 60 sec and dried. Light cure (LC) and dual cure (DC) resin cement was applied to specimens (approximately 0,15 mm thickness) then polymerized with a LED unit for 1 min with 1200mW / cm². Digital caliper was used for final thickness measurements. First color and translucency were measured by spectrophotometer device, then the samples were exposed to a total 150 KJ / m² of energy for 300 hours in a UV aging unit. Second color and translucency was measured and Calculated after UV aging, according to the CIEDE2000 system. Data were analyzed by using the IBM SPSS V23. Result: CAD/CAM materials type and structure have significant effect on color and translucency. CEREC, with feldspar ceramic structure, showed the least color change among the groups, While LU with a resin nano-ceramic structure showed the highest color change (p

Benzer Tezler

  1. Farklı hibrit CAD/CAM bloklarından çeşitli kalınlıklarda üretilen kronların rezin simanlarla maskeleme etkinliğinin değerlendirilmesi

    The evaluation of the masking effectiveness of the crowns produced by different hybrid CAD/CAM blocks in the various thicknesses with rezin cement

    FARHAD WAHID RASOOL RASOOL

    Doktora

    Türkçe

    Türkçe

    2019

    Diş HekimliğiVan Yüzüncü Yıl Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ BEYZA ÜNALAN DEĞİRMENCİ

  2. Molar dişlere farklı materyallerle uygulanan onlay restorasyonların oklüzal yükleme sonrası kırılma dayanımlarının karşılaştırılması

    Comparison of fracture strengths of onlay restorations applied with different materials on molar TEETH after occlusal loading

    ALEYNA ÖYKÜ AKBAŞAK SUNGUR

    Doktora

    Türkçe

    Türkçe

    2023

    Diş HekimliğiBaşkent Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. SELİM ERKUT

  3. Prepless ve laminate veneer restorasyonlarında kullanılan farklı kalınlıklardaki seramiklerin simantasyon sonrası renk stabilitelerinin incelenmesi

    Prepless ve laminate veneer restorasyonlarinda kullanilan farkli kalinliklardaki seramiklerin simantasyon sonrasi renk stabilitelerinin incelenmesi

    HÜLYA ÇETİN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2020

    Diş HekimliğiBolu Abant İzzet Baysal Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ KÜBRA DEĞİRMENCİ

  4. Anodizasyon ile renklendirilmiş titanyum dayanakların ve farklı alt yapı kalınlıklarının zirkonya alt yapı rengi üzerine etkisinin değerlendirilmesi

    Evaluation of the effect of anodized titanium abutments and substructure thickness on the color of zirconia substructure

    BÜRKAN BERKAY BAŞ

    Doktora

    Türkçe

    Türkçe

    2023

    Diş Hekimliğiİstanbul Medipol Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. UMUT ÇAKAN

  5. Alüviyal ortamda farklı zemin kesitlerinde zemin iyileştirilmesi seçeneklerinin değerlendirilmesi

    The evaluation of soil improvement options in different soil sections containing alluvial soft soils

    BERNA ÇAĞLAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    İnşaat MühendisliğiSakarya Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. SEDAT SERT