Farklı hibrit CAD/CAM bloklarından çeşitli kalınlıklarda üretilen kronların rezin simanlarla maskeleme etkinliğinin değerlendirilmesi

The evaluation of the masking effectiveness of the crowns produced by different hybrid CAD/CAM blocks in the various thicknesses with rezin cement

  1. Tez No: 557505
  2. Yazar: FARHAD WAHID RASOOL RASOOL
  3. Danışmanlar: DR. ÖĞR. ÜYESİ BEYZA ÜNALAN DEĞİRMENCİ
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Van Yüzüncü Yıl Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 120

Özet

Farklı Hibrit CAD/CAM Bloklarından Farklı Kalınlıklarda Üretilen Kronların Rezin Simanlarla Maskeleme Etkinliğinin Değerlendirilmesi. Van Yüzüncü Yıl Üniversitesi, Sağlık Bilimleri Enstitüsü, Protetik Diş Tedavisi Anabilim Dalı, Doktora Tezi, Van, 2019. Üstün estetik özellikleri ve elastik özelliklerinin diş dokusuna yakın olması ile hibrit seramikler sıklıkla kullanılmaktadır.Hibrit seramikler diş hekimliğinde restorasyon yapımında alt yapının renginin yansımasıdır. Bu alt yapının maskelenmesi için farklı yöntemler mevcuttur. Bu tez çalışmasının amacı, farklı kalınlıklardaki farklı hibrit seramiklerin alt yapı renginin maskeleme etkinliğini araştırmaktır. Çalışmada 4 değişik içeriğe sahip CAD/CAM bloklardan (Cerec blok, GC Cerasmart, Vita Enamic, 3M Lava Ultimate) 1 mm 1,5 mm ve 2 mm kalınlıkta olmak üzere her bir gruba ait 10'ar örnek olacak şekilde toplam 120 test örneği hazırlanmıştır. Çalışmada, test örnekleri isomet bıçağı ile, 100N basınçla, distile su altında kesilerek hazırlanmıştır. Alt yapı olarak A3 renginde Kuraray kompozit kullanılmıştır. Örneklerin simantasyonu için A2 renginde G-CEM Link Force rezin siman kullanılmıştır. Örnekler asitleme ve bonding işleminden sonra alt yapılara 10N sabit basınç altında rezin siman ile simante edilmiştir. Simantasyon işleminden sonra tüm örnekler, etüv cihazında 37 derecede 24 saat boyunca bekletilmiştir. Her bir gruba ait örnekler spektrofotometre cihazı (Spekctroshade Verona, İtalya) ile 5 tekrar ile ölçülmüştür. Örneklere ait L,a,b değerleri excell programına kaydedilmiş ve değerlerin ortalamaları alınmıştır. Renkteki değişiklikler ΔE formülüyle hesaplanmıştır. Örneklere ait değerler ΔE cinsinden SPSS programına kaydedilmiş ve istatistik analiz yapılmıştır. İstatistiksel analiz için Kruskal Wallis test ve ikili karşılaştırmalarında Dunn's testi kullanılmıştır. Anlamlılık en az p

Özet (Çeviri)

The Evaluation of The Masking Effectiveness of The Crowns Produced By Different Hybrid CAD/CAM Blocks In The Various Thicknesses With Rezin Cement. University of Van Yuzuncu Yıl, Institute of Health Sciences, Prosthodontic Department, Phd Thesis, Van, 2019. Hybrid ceramics are frequently used because of their superior aesthetic properties and elastic properties close to the tooth texture. Hybrid ceramics it is a reflection of the color of the infrastructure in restoration in dentistry. There are several methods for masking this infrastructure. The aim of this thesis is to investigate the masking efficiency of the substructure, color of different hybrid ceramics in various thicknesses. In this trial, total of 120 test specimens were prepared for each group consisting of CAD/CAM blocks with 4 different contents (Cerec block, GC Cerasmart, Vita Enamic, 3M Lava Ultimate), 1 mm 1.5 mm and 2 mm. The samples were prepared by isomet knife with 100N pressure under distilled water. In the structure, A3 color Kuraray composite is used for substructure. G-CEM Link Force rezin cement was used for the cementation of the samples. After etching and bonding, the samples were cemented with rezin cement at 10N constant pressure. All samples were incubated at 37 °C for 24 hours in incubator after cementation. Samples from each group were measured by spectrophotometer (Spekctroshade Verona, Italy) 5 times. The L, a, b values of the samples were recorded in the excell program and the values were averaged. Changes in color were calculated with the formula ΔE. The values of the samples were recorded in SPSS program in ΔE and statistical analysis was performed. Kruskal Wallis test was used for statistical analysis and Dunn's test was used for group comparison. Significance was evaluated at least p

Benzer Tezler

  1. Fırça abrazyonunun farklı CAD/CAM seramiklerinin renk ve parlaklığı üzerine etkisinin değerlendirilmesi

    Evaluation of the effect of brush abrasion on color and brightness of different CAD/CAM ceramics

    TUĞBA AYCAN ERKAL

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2022

    Diş HekimliğiVan Yüzüncü Yıl Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ MEHMET UĞUR

  2. Farklı diş macunlarının hibrit CAD/CAM blokların fiziksel özellikleri üzerine etkilerinin değerlendirilmesi

    Demands for the effects of whitening toothpastes on the physical properties of hybrid CAD/CAM blocks

    BEYZA KARADAĞ NALDEMİR

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2021

    Diş HekimliğiVan Yüzüncü Yıl Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ MURAT ESKİTAŞCİOĞLU

    DR. ÖĞR. ÜYESİ BEYZA ÜNALAN DEĞİRMENCİ

  3. CAD/CAM teknolojisiyle üretilen farklı tam seramik inlay/onlay restorasyonların marjinal uyumlarının ve klinik başarılarının in vivo olarak değerlendirilmesi

    Marginal adaptation and clinical evaluation of different CAD/CAM inlayonlay restorations as a split-mouth study

    ELİF COŞKUN

    Doktora

    Türkçe

    Türkçe

    2018

    Diş HekimliğiMarmara Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. YASEMİN ÖZKAN

  4. Rezin-nano seramik ve polimer-infiltre seramiklere uygulanan farklı yüzey işlemlerinin kompozit rezinlerle bağlantısının incelenmesi

    Effect of different surface treatments on bond strength of composite resin to resin nano cerami̇c and polymer

    NUMAN TATAR

    Doktora

    Türkçe

    Türkçe

    2016

    Diş HekimliğiOndokuz Mayıs Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. ÇAĞRI URAL

  5. Farklı CAD/CAM materyalleri ile üretilen lamina veneerlerin bağlanma dayanımlarının in vitro koşullarda değerlendirilmesi

    Farkli CAD/CAM materyalleri ile üretilen lamina veneerlerin bağlanma dayanimlarinin in vitro koşullarda değerlendirilmesi

    ASENA KAPTANOĞLU

    Doktora

    Türkçe

    Türkçe

    2024

    Diş Hekimliğiİstanbul Medipol Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. HALUK BARIŞ KARA