Pomzadan alümina üretiminin hidrometalurjik yöntemlerle araştırılması

Investigation of alumina production from pumice by hydrometalurgical methods

PDF İndir

  1. Tez No: 675797
  2. Yazar: MUHAMMED KÜRŞAT AYDEMİR
  3. Danışmanlar: PROF. DR. MURAT ERDEMOĞLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Maden Mühendisliği ve Madencilik, Mining Engineering and Mining
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2021
  8. Dil: Türkçe
  9. Üniversite: İnönü Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Maden Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Maden Mühendisliği Bilim Dalı
  13. Sayfa Sayısı: 117

Özet

Bu tez çalışmasında, Kayseri bölgesinden temin edilen asidik pomzanın hidrometalurjik yöntemlerle değerlendirilerek pomzadan alümina üretimi olanakları araştırılmıştır. Başlıca %64,64 SiO2 ve %14,85 Al2O3 içeriğine sahip olan pomzadan liç yöntemiyle alümina üretilmesi amaçlanmıştır. Bu amaçla pomza su, HCl, H2SO4 ve HNO3 çözeltilerinde liç edilerek bu ortamlardaki alüminyum kazanımları ortaya çıkarılmıştır. Tüvenan pomzanın tüm ortamlardaki liçi sonucunda çözeltiye anlamlı miktarda alüminyum alınamamış olması nedeniyle pomza mekanik olarak aktifleştirmek amacıyla gezegensel hareketli bilyalı değirmen kullanılarak 2-60 dk aralığında çeşitli sürelerde öğütülmüştür. Öğütülmüş ürünler, sabit koşullarda liç edilmiş ve en yüksek alüminyum kazanımı (%66,40) 60 dk. aşırı öğütülmüş pomzanın HCl çözeltisiyle liçi sonucunda elde edilmiştir. Alüminyum kazanımını artırmak üzere sıcaklık, süre ve asit derişimi parametrelerinin etkisinin araştırıldığı çalışmalar sonucunda 4 M HCl çözeltisinde, çözelti kaynama sıcaklığında ve 24 saatte yapılan liç işlemiyle alüminyum kazanımı %91,37'ye yükselmiştir. Elde edilen bu liç çözeltisinden evaporasyon yoluyla çöktürülen AlCl3 tuzu 1200°C'de 3 saat kavrularak ilk kez pomza alüminası üretilmiştir. Alüminanın %62,87 Al2O3 içeriğine sahip olduğu, sodyum ve potasyum içeriğinin çok düşük ancak demir ve kalsiyum içeriğinin ise yüksek olduğu görülmüştür. Sonuç olarak, pomzadan alümina üretimi için mekanik aktivasyon, asit liçi, çözelti saflaştırma, çöktürme ve kavurma aşamalarından oluşan temel bir akım şeması önerilmiştir.

Özet (Çeviri)

In this thesis study, the possibilities of alumina production from pumice were investigated by evaluating the acidic pumice obtained from Kayseri region by hydrometallurgical methods. It was aimed to produce alumina by leaching from the pumice with 64.64% SiO2 and 14.85% Al2O3 content. For this purpose, pumice was leached in water, HCl, H2SO4 and HNO3 solutions and the aluminium recoveries in these media were revealed. As a result of the leaching of the run-of-mine pumice in all media, a significant amount of aluminium could not be taken into the solution, so it was milled at various times between 2-60 minutes using a planetary ball mill in order to mechanically activate the pumice. The milled products were leached under constant conditions and the highest aluminium recovery (66.40%) was obtained as a result of leaching the intensively 60 min. milled pumice with HCl solution. As a result of studies investigating the effect of temperature, time and acid concentration parameters to increase aluminium recovery, it was increased to 91.37% by leaching in 4 M HCl solution at the boiling temperature for 24 hours. AlCl3 salt precipitated from this leach solution through evaporation was roasted at 1200 °C for 3 hours and pumice alumina was produced for the first time. It was observed that alumina has 62.87% Al2O3 content, while sodium and potassium contents were very low, iron and calcium contents were high. As a result, a basic flow sheet including mechanical activation, acid leaching, solution purification, precipitation and roasting stages was proposed for alumina production from pumice.

Benzer Tezler

  1. Tez No

    177717

    Borun pomzadan seramik yapımında eritici olarak kullanılması

    Use of boron as a fluxing agent in production of ceramics from pumice

    AHMET KOLKIRAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    KimyaErciyes Üniversitesi

    Kimya Ana Bilim Dalı

    YRD. DOÇ. DR. ÖMER EDİP KUZUGÜDENLİ

  2. Tez No

    516502

    Perlit ve pomzadan üretilen filtrelerin is partikülleri üzerine etkisinin deneysel araştırılması

    Experimental study on the effects of perlit and pomzane produced filters on is-particulars

    ERKAN YÜKSEL

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Makine MühendisliğiBitlis Eren Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. HÜSEYİN TURHAN

  3. Tez No

    199950

    Asidik ve bazik pomzadan üretilen yapı malzemelerinin mühendislik özelliklerinin belirlenmesi

    Investigation of engineering properties of building materials made with acidic and alcaline pumice

    YASİN ERDOĞAN

    Doktora

    Türkçe

    Türkçe

    2007

    Maden Mühendisliği ve MadencilikÇukurova Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    DOÇ.DR. ERGÜL YAŞAR

  4. Tez No

    58457

    Hafif betonun karot numuneleri ile standart silindir numunelerinin mukavemet değerleri arasındaki ilişkinin araştırılması

    Başlık çevirisi yok

    BURHAN ALP

    Yüksek Lisans

    Türkçe

    Türkçe

    1997

    İnşaat MühendisliğiAtatürk Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. RÜSTEM GÜL

  5. Tez No

    299437

    Deli Halil (Osmaniye) bazaltik pomzalarının cam seramik yapımında kullanım olanakları ve karakterizasyonu

    Usability of Deli Halil (Osmaniye) basaltic pumice in glass ceramic production and characterization

    SUNA ÇETİN

    Doktora

    Türkçe

    Türkçe

    2012

    Jeoloji MühendisliğiÇukurova Üniversitesi

    Maden Yatakları ve Jeokimya Ana Bilim Dalı

    YRD. DOÇ. MUSTAFA AKYILDIZ

Geri Dön