Assesment of microstructural effects on stress corrosion cracking behaviour of 4140 and 4340 steels in a caustic solution
4140 ve 4340 çeliklerinin kostik ortamlardaki gerilimli korozyon davranışı üzerin mikroyapısal etkilerin incelenmesi
- Tez No: 68414
- Danışmanlar: YRD. DOÇ. DR. FİLİZ SARIOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Gerilimli korozyon çatlaması, düşük alaşımlı çelik, kostik çözelti, mikroyapı. iv, Korozyon, Çelik-metal, Stress corrosion cracking, low alloy steel, caustic solution, microstructure m, Corrosion, Steel-metal
- Yıl: 1997
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
öz 4140 VE 4340 ÇELİKLERİNİN KOSTİK ORTAMLARDAKİ GERİLİMLİ KOROZYON DAVRANIŞI ÜZERİNE MİKROYAPIS AL ETKİLERİN İNCELENMESİ Pehlivanoğlu, M. Kaan Yüksek Lisans, Metalürji ve Malzeme Mühendisliği Bölümü Tez Yöneticisi: Doc. Dr. Filiz Sanoğlu Ocak 1997, 89 Sayfa Mikroyapısal değişikliklerin düşük alaşımlı 4140 ve 4340 çeliklerinin gerilimli korozyon çatlaması davranışlarına (GKÇ) etkisi kompozisyonları farklı iki kostik çözelti kullanılarak oda sıcaklığında ve/veya 80 °C'de incelenmiştir. Bu amaçla elektrokimyasal anodik polarizasyon testleri ve çekme numuneleri için düşük germim hızlı, kompakt çekme numuneleri içinse sabit uzama hızlı mekanik deney yöntemleri uygulanmıştır. Sonuçlar 4140 alaşımının 4340 alaşımına kıyasla kostik ortamlarda gerilimli korozyon kırılımına daha dayanıldı olduğunu göstermiştir. Her iki alaşımda da su verme ve menevişleme işlemlerinin bu dayanıklılığı arttırdığı görülmüştür. Sadece 4140 alaşımına uygulanan küreselleştirme işlemi de benzer bir etki göstermiştir. SEM çalışmalarında, kırılma modlarının uygulanan ısıl işlemlerden etkilendiği bulunmuştur.
Özet (Çeviri)
ABSTRACT ASSESSMENT OF MICROSTRUCTURAL EFFECTS ON STRESS CORROSION CRACKING BEHAVIOUR OF 4140 AND 4340 STEELS IN A CAUSTIC SOLUTION Pehlivanoglu, M.Kaan M.S., Department of Metallurgical And Materials Engineering Supervisor: Assoc. Prof. Dr. Filiz Sarioglu January 1997, 89 Pages The effects of variations in microstructure on the stress corrosion cracking (SCC) susceptibility of the low alloy steels, 4140 and 4340,have been studied in caustic solutions of two different compositions at room temperature and/or 80 °C, under freely corroding conditions. For this purpose, electrochemical anodic polarization tests and mechanical tests, namely slow strain rate tests on smooth tensile specimens and constant displacement rate tests on compact tension specimens were performed. The results have shown that 4140 alloy was more resistant to caustic stress corrosion cracking compared to 4340. Heat treatments involving quenching and tempering were found to increase resistance to SCC of both alloys. A similar trend was observed after the spheroidization treatment applied only to 4140 alloy. Cracking modes observed in SEM studies were affected by the heat treatments applied.
Benzer Tezler
- B segmenti bir binek araçta amortisör yayının kırılma analizi
Failure analysis of the damper spring in a B-segment passenger car
EREN ARSLAN
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiSakarya ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. KENAN GENEL
- The investigation of mechanical properties of annealed 5005Al alloys at different parameters
Tavlanmış 5005 Al alaşımlarının mekanik özelliklerinin farklı parametrelerde incelenmesi
RAGHAD MAJEED ABDULKAREEM AL-MUSAWI
Yüksek Lisans
İngilizce
2023
Metalurji MühendisliğiKarabük ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. İSMAİL HAKKI KARA
- Nikel sülfamat içeren banyolarda gerçekleştirilen nikel kaplama özellikleri üzerine, banyo bileşimine ilave edilen borik asit ilavesinin etkisinin araştırılması
Investigation of the effect of boric acid addition to bath composition on the properties of nickel coatings deposited from nickel sulfamate baths
ÖMERCAN SİVRİ
Yüksek Lisans
Türkçe
2025
Mühendislik BilimleriSakarya Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
PROF. DR. UĞUR ŞEN
- Biber çeşitlerinde farklı tuz dozlarının tohum çimlenmesine etkileri
The effects of different salt concentrations on seed germination in pepper cultivars
NİHAN GURUR EROL
Yüksek Lisans
Türkçe
2025
ZiraatVan Yüzüncü Yıl ÜniversitesiBahçe Bitkileri Ana Bilim Dalı
DOÇ. DR. TURGAY KABAY
- Dwell fatigue life assessment of dual-phase titanium alloy using polycrystalline plasticity
Çift fazlı titanyum alaşımının bekleme-yorulma ömrünün polikristal plastisitesi kullanılarak değerlendirilmesi
SADIK SEFA AÇAR
Yüksek Lisans
İngilizce
2025
Havacılık ve Uzay MühendisliğiOrta Doğu Teknik ÜniversitesiHavacılık ve Uzay Mühendisliği Ana Bilim Dalı
DOÇ. DR. TUNCAY YALÇINKAYA