The Effect of annealing temperature and time on the mechanical properties of cross linked polyethylene film

Tavlama sıcaklığının ve süresinin çaprazbağlı polietlen filmin mekanik özelliklerine etkisi

  1. Tez No: 68462
  2. Yazar: RAİD M.I BANAT
  3. Danışmanlar: PROF. DR. TEOMAN TİNÇER
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Çaprazbağlı polietilen, tavlama süresi ve sıcaklığı, mekanik özellikler, Crosslinked polyethylene, annealing time, and temperature, mechanical properties. IV
  7. Yıl: 1997
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 66

Özet

Öz TA VLAMA SICAKLIĞININ VE SÜRESİNİN ÇAPRAZBAĞLI POLİETİLEN FİLMİNİN MEKANİK ÖZELLİKLERİNE ETKİSİ Banat, Raid M. I. Yüksek Lisans Tezi, Kimya Anabilim Dalı Tez Yöneticisi: Prof. Dr. Teoman Tınçer Ocak 1997, 52 sayfa Son 20-30 yıl içerisinde poliolefîn boruların değişik sıcak-su sistemlerinde kullanılması, önemli ölçüde artmıştır. Bu çalışmanın amacı, tavlama işleminin çapraz bağlı polietilen filmlerinin mekanik özelliklerine etkisini değerlendirmektir. Çaprazbağlı polietilen film, Brabender Plastic-Corder Extruder' inde, 30 ve 45 rpm vida hızlarıyla, ekstrüzyon işlemiyle hazırlanmıştır. 30 rpm' de ekstrüzyon ve 70, 80, 90°C'lerde 4,6,8,10,12 ve 30 saat süre periyotlarında tavlanan çaprazbağlı polietilen filmlerin mekanik özellikleri, hem işlem yönünde, hem de işlem yönüne dik olarak, tavlama sıcaklık ve süresi yönündenincelenmiştir. 30 rpm'de ekstrüzyon yapılan filmlerin mekanik özellikleri 45 rpm'de yapılandan, 90°C'de tavlamada daha iyidir. 80°C'de tavlanan polimer filminin kopma kuvveti, 70°C ve 90°C'de tavlananlarla karşılaştırıldığında artmıştır, fakat aynı zamanda kopma uzaması bütün tavlama sıcaklıkları için, tavlama süresi arttıkça fazlalaşmıştır. Tavlama süresi modülü arttırmıştır ve en yüksek değer en uzun tavlama süresi olan 30 saat için bulunmuştur. Akma gerilimi, tavlama süresiyle özellikle 12 saatte yüksektir ve tavlama sıcaklığı akma gerilimini fazla değiştirmemiştir. 90°C'de tavlanan polimer filminin akma uzaması ve ona yakın olan 80°C'de tavlanan polimer filminin akma uzaması, 70°C'de tavlanandan daha yüksek bulunmuştur; fakat akma uzaması jel içeriği arttığı için tavlama süresiyle azalmıştır. 80°C'de 8 saat tavlama süresi, 70 ve 90°C'deki bütün tavlama süreleriyle karşılaştırıldığında daha iyi mekanik özellikler verdiği gözlenmiştir.

Özet (Çeviri)

ABSTRACT THE EFFECT OF ANNEALING TEMPERATURE AND TIME ON MECHANICAL PROPERTIES OF CROSSLINKED POLYETHYLENE FILM Banat Raid M. I. Master thesis, Department of Chemistry Supervisor: Prof. Dr. Teoman Tınçer Januray 1997, 52 pages During the last two decades the use of polyolefin pipe in different hot-water systems has increased considerably. Floor heating is the largest field of application. The aim of the work is to evaluate the effect of annealing process on the mechanical properties of the crosslinked polyethylene films. Crosslinked polyethylene film was prepared by extrusion process at two screw speeds 30 rpm and 45 rpm, in extruder attachment of Brabender Plastic-Corder. The mechanical properties of crosslinked 111polyethylene films extruded at 30 rpm and annealed at 70, 80 and 90°C for several periods of time 4, 6, 8, 10, 12 and 30 hours along the travel direction of processing and in the transverse direction were discussed in terms of annealing temperature and annealing time. Films extruded at 30 rpm had better mechanical properties than those extruded at 45 rpm when annealed at 90°C. Ultimate tensile strength of the polymer film annealed at 80°C increased when compared with annealing at 70°C and 90°C, while elongation at break increased as the annealing time increased in all annealing temperatures. Annealing time increased the modulus and the highest values were found at the longest annealing time, 30 hours. Yield stress increased with annealing time especially after 12 hours of annealing and annealing temperature did not alter significantly. It was found that the yield strain of the polymer film annealed at 90°C higher than those annealed at 70°C and almost the same with that annealed at 80°C, but yield strain decreased with annealing time due to increase in gel content. We found the annealing temperature of 80 °C and the annealing time of 8 hours yielded better mechanical properties compared with those annealed at 70°C and 90°C at all annealing time.

Benzer Tezler

  1. Fused filament fabrication of PETG: Investigation of the mechanical properties through the parameter optimization

    PETG'nin ergiyik yığma modellemesi: Mekanik özelliklerinin parametre optimizasyonu ile incelenmesi

    BUKET PARLAK

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    Uçak Mühendisliğiİstanbul Teknik Üniversitesi

    Uçak ve Uzay Mühendisliği Ana Bilim Dalı

    DOÇ. DR. HÜLYA CEBECİ

  2. Yüksek karbonlu bir çeliğin mikroyapı ve mekanik özelliklerine izotermal tavlamanın etkisi

    Effect of isothermal annealing on microstructure and mechanical properties of a high carbon steel

    MUSTAFA SERDAR KUZYAKA

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DOÇ. MURAT BAYDOĞAN

  3. Hydrothermal growth of ZnO nanowires enhanced characteristic properties

    ZnO nanotellerin karakteristik özellikleri iyileştirilerek hidrotermal olarak büyütülmesi

    ÜMÜŞ HALE TUĞRAL ARSLAN

    Doktora

    İngilizce

    İngilizce

    2020

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. CÜNEYT ARSLAN

    PROF. DR. NİLGÜN BAYDOĞAN

  4. Effect of cold rolling and annealing parameters on the microstructure and mechanical properties of dual phase steels

    Soğuk haddeleme ve tavlama parametrelerinin çift fazlı çeliklerin mikroyapı ve mekanik özelliklerine etkisi

    OKAN POYRAZ

    Yüksek Lisans

    İngilizce

    İngilizce

    2020

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. BİLGEHAN ÖGEL

  5. 3XXX alüminyum alaşımlarında magnezyum ve alternatif proseslerin etkisinin incelenmesi

    Investigation of the effect of magnesium and alternative processes on 3XXX series aluminum alloys

    ÇİSEM DOĞAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. SEBAHATTİN GÜRMEN